This work aims to investigate far-UVC light at 222 nm as a new microbial reduction tool for planetary protection purposes which could potentially be integrated into the spacecraft assembly process. The major advantage of far-UVC (222 nm) compared to traditional germicidal UVC (254 nm) is the potential for application throughout the spacecraft assembly process in the presence of humans without adverse health effects due to the limited penetration of far-UVC light into biological materials. Testing the efficacy of 222-nm light at inactivating hardy bacterial cells and spores isolated from spacecraft and associated surfaces is a necessary step to evaluate this technology. We assessed survival of Bacillus pumilus SAFR-032 and Acinetobacter radioresistens 50v1 exposed to 222-nm light on proxy spacecraft surfaces simulated by drying the bacteria on aluminum coupons. The survival fraction of both bacteria followed a single stage decay function up to 60 mJ/cm², revealing similar susceptibility of both species to 222-nm light, which was independent of the exposure rate. Irradiation with far-UVC light at 222 nm is an effective method to decontaminate the proxy spacecraft materials tested in this study.     

硼酸盐玻璃中稀土离子的发光研究

应用荧光光谱、红外振动光谱等研究了在可见光区发光的Ｐｒ（３＋），Ｓｍ（３＋），Ｅｕ（３＋），Ｔｂ（３＋），Ｄｙ（３＋），Ｅｒ（３＋）和Ｔｍ（３＋）等镧系稀土离子在硼酸盐玻璃中的发光行为，系统地分析了稀土离子在硼酸盐玻璃基质中的激发谱和发光谱特性。     

Design and performance of a vacuum-UV simulator for material testing under space conditions

This paper describes the construction and performance of a VUV-simulator that has been designed to study degradation of materials under space conditions. It is part of the Complex Irradiation Facility at DLR in Bremen, Germany, that has been built for testing of material under irradiation in the complete UV-range as well as under proton and electron irradiation. Presently available UV-sources used for material tests do not allow the irradiation with wavelengths smaller than about 115 nm where common Deuterium lamps show an intensity cut-off. The VUV-simulator generates radiation by excitation of a gas-flow with an electron beam. The intensity of the radiation can be varied by manipulating the gas-flow and/or the electron beam.     

UV镜对摄影测量精度的影响及消除方法研究

针对摄影测量中加入UV镜后对测量结果的影响问题进行了研究。通过理论推导UV镜对于像点坐标偏移的影响,得出UV镜对像点偏移的影响规律,并提出采用自检校光束法平差的方法消除UV镜对像点偏移的影响,实验证明本文得出的对UV镜产生的像点偏移规律的分析及解决方法都是正确的。     

GEO卫星热控涂层αS退化空间综合环境模拟试验

文章用综合低能辐照试验模拟15年地球同步轨道环境对热控材料S781白漆、SR107-ZK白漆、镀银FEP、OSR片的太阳吸收率退化趋势。有机白漆有严重退化,而OSR和 镀银FEP材料退化较少。通过与飞行试验结果比较,证明了本次模拟试验的有效性。通过利用退化趋势的试验数据,应用最小二乘法获得退化数学模型。二次指数退化模型与4种材料退化曲线符合较好。更长试验时间结果可以通过数学模型外推的方法获得。经试验验证,用8年试验数据外推15年数据误差不超过1%。     

The Genesis Solar Wind Concentrator Target: Mass Fractionation Characterised by Neon Isotopes

The concentrator on Genesis provided samples of increased fluences of solar wind ions for precise determination of the oxygen isotopic composition. The concentration process caused mass fractionation as a function of the radial target position. This fractionation was measured using Ne released by UV laser ablation and compared with modelled Ne data, obtained from ion-trajectory simulations. Measured data show that the concentrator performed as expected and indicate a radially symmetric concentration process. Measured concentration factors are up to ∼30 at the target centre. The total range of isotopic fractionation along the target radius is 3.8%/amu, with monotonically decreasing ²⁰Ne/²²Ne towards the centre, which differs from model predictions. We discuss potential reasons and propose future attempts to overcome these disagreements.     

TiO2基紫外探测器的制备及退火工艺对光电性能的影响

采用磁控溅射方法,通过不同工艺的退火处理,制备了光电性能优良的TiO2基紫外探测器.通过紫外光电性能测试、扫描电子显微镜( SEM)观察及X射线衍射(XRD)分析,研究了退火工艺对探测器光电性能的影响规律.结果表明:随着退火温度的增加,TiO2晶粒尺寸显著增大,晶界和缺陷数量的变化是导致TiO2基紫外探测器的光电性能随退火工艺变化的根本原因.经500℃/2h退火后,紫外探测器的光电流高出暗电流近2.5个数量级,紫外波段的光响应高出可见光波段近2个数量级,所制备紫外探测器达到了高辐射灵敏度和可见盲特性的要求.     

太阳紫外辐射对星上光学膜层的影响

光学遥感是当前卫星遥感的重要手段, 而卫星温控和能源系统也广泛采 用光学膜层, 它们在空间环境条件下的性能对卫星应用任务的完成, 乃至卫星寿命、安全将起着非常重要的作用. 本文给出了太阳紫外辐射对星上光学膜层影响的主要机制, 分析了这一影响的主要规律和原子氧剥蚀、高能粒子和静电场的作用, 综述了太阳紫外辐射对星上光学系统表面膜层影响的测量结果, 最后提出了星上光学膜层污染防护中应重点关注的几个方面.      

过氧化氢/紫外线/臭氧氧化技术处理肼类污水的应用

采用放大试验规模（处理量1 m³/h）的H₂O₂（过氧化氢）/UV（紫外线）/O₃（臭氧）氧化技术处理肼类推进剂污水,在30.0±1.6 ℃,pH=9.0±0.2的条件下,研究肼类的过氧化氢增强光解臭氧化降解。对比不同氧化技术的协同效应以及对污水降解的影响,重点考察过氧化氢、紫外线、臭氧和初始浓度等工艺参数对降解效果的影响,对氧化技术的应用进行了优化。研究结果表明：该技术可使COD去除率提高27.66%,肼类的降解速率随着过氧化氢投加量、紫外线辐射强度、O₃投加速率和水质地提高而升高,随着初始质量浓度的提高而下降。在最佳工艺下,处理5 000 mg/L质量浓度的废水,处理60 min时,COD去除率分别为98.62%（偏二甲肼）、99.17%（甲基肼）、99.94%（肼）和93.25%（单推-3）。     

ZnO透明导电薄膜制备及紫外辐照处理特性研究

ZnO作为一种典型的透明导电氧化物（Transparent conductive oxide,TCO）材料,具有同氧化铟锡(Indium tin oxide,ITO)相比拟的光电性能,其原料丰富、绿色环保、易于制备、生成成本低等优点使ZnO成为最有希望替代ITO的材料。本文以玻璃为衬底,利用量子点种子层作为缓冲层,采用传统水热方法制备了低成本ZnO透明导电薄膜,采用特殊的紫外光辐照工艺对薄膜进行后处理,探索薄膜生长参数和紫外光辐照处理工艺对其透光率和导电性的影响。结果表明,紫外辐照处理不影响薄膜的透光性能,而使材料的方块电阻降低3个数量级,数值从没处理时的1.5×105 Ω/□降低到 150 Ω/□,极大地提高了薄膜的电导率,为ZnO薄膜材料电导率的提高提供了一个简单高效的途径。