This paper presents a brief review of activities in laminar flow control being performed at the Central Aerohydrodynamic Institute named after Prof. N.E. Zhukovsky (TsAGI). These efforts are focused on the improvement of the existing laminar flow control methods and on the development of new ones. The investigations have demonstrated the effectiveness of aircraft surface laminarization applications with the aim of friction drag reduction. The opportunity of considerable delaying of laminar-turbulent transition due to special wing profile geometry and using boundary layer suction and surface cooling has been verified at sub- and supersonic speeds through various wind tunnel testing at TsAGI and during flying laboratory experiments at the Flight Research Institute (LII). The investigations on using hybrid laminar flow control systems for friction drag reduction were also carried out. New techniques of laminar flow control were proposed, in particular, the method of local heating of the wing leading edge, boundary layer laminarization by means of receptivity control, and electrohydrodynamic methods of boundary layer stability control.     

离子束辅助沉积WS_2-Ti-Ag复合薄膜的摩擦性能

采用ZDH-100型号离子束复合沉积设备沉积WS_2-Ti-Ag复合薄膜,基材为轴承钢和单晶硅(100).采用场发射扫描电子显微镜、XRD衍射仪,检测复合薄膜的表面形貌、微观结构.采用球-盘式摩擦磨损试验机,对复合薄膜在大气环境中的摩擦性能进行了研究.结果表明:采用离子束辅助沉积技术制备的WS_2-Ti-Ag复合薄膜是非晶态薄膜;并且随法向载荷的增加,复合薄膜的摩擦因数减小,摩擦状态越稳定,耐磨寿命越短.     

高摩擦性能碳／碳复合材料的微观结构

使用激光拉曼探针和电子显微术对试样的断裂面和薄膜样品观察及电子衍射技术研究了两种抗摩擦性能相差悬殊的碳／碳复合材料的微观结构，发现两种材料的微观结构在石墨晶体的结晶结构完整性和取得性以及纤维和基体间的界面行为上有显著差异。     

基于马尔可夫链的飞机刹车片检查时间确定

为结合飞机实际运行工况,科学合理地制定刹车片检查时间,提出了一种基于马尔可夫链理论的预测模型。以某一机群刹车片检查时间确定为例,分别论述了刹车片磨损状态的划分,以及转移概率矩阵的构造与估计,并对该机群刹车片磨损状态进行了预测,其预测结果与实际检查情况较吻合。根据刹车片磨损状况的预测结果,制定了该机群在实际运行工况下的刹车片检查时间。实际运行情况表明,所制定的刹车片查检时间可行、有效。     

一种铝锂合金搅拌摩擦焊接头力学性能及微观组织研究

研究了C24S-T8铝锂合金搅拌摩擦焊接头力学性能及微观组织。通过焊接工艺参数的优化,获得了无孔洞缺陷、焊缝质量优异的接头,强度系数约82%。拉伸时塑性变形及断裂集中于焊缝处。基材晶粒呈薄饼状,沿轧制方向拉长;焊核区为细小等轴的再结晶晶粒,平均晶粒尺寸约2.3μm,大部分晶界是大于15°的大角度晶界;热机影响区的晶粒在焊接过程中发生了偏转和变形。C24S-T8铝锂合金基材强化相包括T1相(Al2CuLi)、θ’相(Al2Cu)和S’相(Al2CuMg);热机影响区及焊核区内强化相完全溶解,造成硬度下降。     

Friction moment analysis of space gyroscope bearing with ribbon cage under ultra-low oscillatory motion

This paper presents the model of calculating the total friction moment of space gyroscope ball bearings which usually work under ultra-low oscillatory motion and are very sensitive to the friction moment. The aim is to know the proportion of the friction moment caused by each frictional source in the bearing＇s total friction moment, which is helpful to optimize the bearing design to deduce the friction moment. In the model, the cage dynamic equations considering six degree-of-freedom and the balls dynamic equations considering two degree-of-freedom were solved.The good trends with different loads between the measured friction moments and computational results prove that the model under constant rate was validated. The computational results show that when the speed was set at 5 r/min, the bearing＇s maximum total friction moment when oscillation occurred was obviously larger than that occurred at a constant rate. At the onset of each oscillatory motion, the proportion of the friction moment caused by cage in the bearing＇s total friction moment was very high, and it increased with the increasing speed. The analyses of different cage thicknesses and different clearances between cage pocket and ball show that smaller thickness and clearance were preferred.     

2219铝合金变截面结构搅拌摩擦焊接工艺及组织特性

针对变截面结构产品,提出了一种变截面搭接结构搅拌摩擦焊接方法,通过加装辅助板将整条焊缝焊接方向上补偿为等厚度。焊接采用一次定位焊接+二次定位焊接+正式焊接的工艺方式,一次定位焊为预定位,二次定位焊保证辅助板与试片主体结构之间形成有效连接,正式焊保证形成完整的焊缝。焊缝表面成形良好,超声相控阵检测无超标缺陷。通过对力学性能的分析,变截面搭接结构处焊缝与非搭接处焊缝和常规对接焊缝的力学性能基本相同,平均抗拉强度均达到母材的70%以上,平均延伸率均在5.8%以上。变截面搭接焊缝焊核处晶粒形态为细小的等轴晶,靠近轴肩影响区部分的晶粒尺寸大于靠近焊缝根部的晶粒尺寸,受再结晶影响,焊缝两侧热机影响区处辅助板搭接界面消失。     

2219铝合金搅拌摩擦焊缝Al2Cu相聚集行为特征分析

对2219C10S状态铝合金进行搅拌摩擦焊接试验,发现焊缝中存在聚集物的异常聚集现象,聚集相在X光检测中显示为亮白色聚集物,主要形态分为团块状、线状和指状三种,聚集相处焊缝的力学性能与无聚集相焊缝的力学性能基本相同。各形态聚集相的分布位置受搅拌头焊接影响区域的不同而不同,团块状聚集相主要存在于焊核中心或偏焊缝上表面位置处,线状和指状聚集相主要存在于焊核中心或偏焊缝根部位置处。对异常聚集相进行能谱分析知,聚集相主要组成元素为Al和Cu,原子百分比近似为2∶1,确定聚集相主要成分为Al2Cu。对聚集相的成因进行分析认为,聚集相的产生主要受搅拌摩擦焊接热输入及搅拌头机械搅拌作用的影响,在焊接过程中,塑态软化金属中的Al2Cu在填补搅拌针后方空腔的过程中出现了聚集行为,随着塑态金属的凝固,聚集行为开始变得缓慢并结束。