本文综述了作者近十年来在多向编织碳／碳复合材料力学性能研究方面的成果，包括力学模型与强度准则、热应力分析、断裂行为、性能预报与优化设计、超高温试验技术及组织性能与高温退化等内容，并分析了其存在的新问题和解决途径。     

碳/环氧复合材料模压成型工艺特性及其影响性能主要因素

文章介绍了碳/环氧复合材料模压成型工艺特性,并讨论了影响模压成型制品性能的主要因素等内容。     

碳纤维增强陶瓷基复合材料抗氧化涂层研究进展

对碳纤维增强陶瓷材料抗氧化涂层的要求、组成与制备工艺以及最近抗氧化涂层体系的发展做了综述。并且对今后抗氧化涂层的发展作了一些展望。     

高能CO2激光腔镜高反介质薄膜的传输特性

为了获得适用于高能CO2激光器的高抗破坏阈值高反薄膜,以10.6μm高反膜ZnSe/YbF3,PbTe/BaF2膜系为例,数值模拟了激光在高反介质膜中的传输的场特性;给出了激光在多层介质膜中的场强分布、温度场分布及热应力分布。结果表明硅镜基体上的PbTe/BaF2膜系所需膜层厚度小、膜层数少,反射率可高达99.98%。     

电沉积CeO2/Zn纳米复合涂层

将纳米氧化铈颗粒加入镀锌液中进行复电沉积制得纳米复合涂层。通过失重法，ICP，SEM和XRD方法探讨了纳米氧化铈颗粒对电沉积锌涂层的影响。结果表明，在同样的电沉积条件下，纳米复合涂层的耐蚀性明显提高，而微米复合涂层的耐蚀性只稍有改善；纳米复合涂层中氧化铈的含量高于微米复合涂层中的氧化铈含量。纳米氧化铈颗粒改变了锌涂层的表面组织形貌和晶体结构，从而提高了涂层的耐蚀性。     

Grinding temperature and energy ratio coefficient in MQL grinding of high-temperature nickel-base alloy by using different vegetable oils as base oil

Vegetable oil can be used as a base oil in minimal quantity of lubrication(MQL). This study compared the performances of MQL grinding by using castor oil, soybean oil, rapeseed oil, corn oil, sunflower oil, peanut oil, and palm oil as base oils. A K-P36 numerical-control precision surface grinder was used to perform plain grinding on a workpiece material with a high-temperature nickel base alloy. A YDM–III 99 three-dimensional dynamometer was used to measure grinding force,and a clip-type thermocouple was used to determine grinding temperature. The grinding force, grinding temperature, and energy ratio coefficient of MQL grinding were compared among the seven vegetable oil types. Results revealed that(1) castor oil-based MQL grinding yields the lowest grinding force but exhibits the highest grinding temperature and energy ratio coefficient;(2) palm oil-based MQL grinding generates the second lowest grinding force but shows the lowest grinding temperature and energy ratio coefficient;(3) MQL grinding based on the five other vegetable oils produces similar grinding forces, grinding temperatures, and energy ratio coefficients, with values ranging between those of castor oil and palm oil;(4) viscosity significantly influences grinding force and grinding temperature to a greater extent than fatty acid varieties and contents in vegetable oils;(5) although more viscous vegetable oil exhibits greater lubrication and significantly lower grinding force than less viscous vegetable oil, high viscosity reduces the heat exchange capability of vegetable oil and thus yields a high grinding temperature;(6) saturated fatty acid is a more efficient lubricant than unsaturated fatty acid; and(7) a short carbon chain transfers heat more effectively than a long carbon chain. Palm oil is the optimum base oil of MQL grinding, and this base oil yields 26.98 N tangential grinding force,87.10 N normal grinding force, 119.6 °C grinding temperature, and 42.7% energy ratio coefficient.     

真空电子辐照对碳纤维/ 氰酸酯复合材料的影响

利用空间带电粒子模拟设备模拟真空电子辐照环境,研究真空电子辐照条件下碳纤维/氰酸酯复合材料层间剪切强度和质量损失率变化规律,并利用XPS和SEM对辐照前后复合材料表面性质和断口形貌进行分析和表征。结果表明:150 keV真空电子辐照作用对碳纤维/氰酸酯复合材料表面影响较大,随着真空电子辐照注量增加复合材料质量损失率先快速增加后趋于平缓,而层间剪切强度先增加后略有降低。     

三种纳米碳材料吸波涂层设计及性能

对纳米炭黑(UC)、特导纳米炭黑(L6)、碳纳米管(CNT)三种材料在8～18 GHz波段吸波涂层进行了优化设计及吸波性能分析.结果表明,三种材料的复介电常数随着纳米碳材料质量分数的增加,其实部和虚部均以不同的速度增大.利用理论计算的Cole-Cole图,结合实验测得的复介电常数,求解出这三种材料理想的介电常数,材料的质量分数和吸波涂层的匹配厚度.结果表明,CNT的吸波效果最好,当CNT质量分数为20％涂层、厚度为1.6mm时,反射衰减率在11.2～ 15 GHz均优于-10 dB吸收峰最大值,达到29.6 dB.     

碳纤维表面微观结构的定量化表征方法

通过使用Matlab编程处理日本东丽T300、国产GCF-1和GCF-2等3种碳纤维样品断面的扫描电镜照片,采用二值标签算法获得了碳纤维的直径及圆度等碳纤维物理特征定量数据。建立了采用直线方程切线法寻找并计算碳纤维表面沟槽的数量及尺度的方法,发现3种碳纤维样品的边缘沟槽的深度及宽度的分布均符合Weibull分布的特征。3种碳纤维的表面物理特征随温度变化的规律相同,说明其在结构上存在着一致性。经过不同温度热处理后3种碳纤维样品的圆度值变化不大,平均直径随着热处理温度的升高逐渐减小,并且表面沟槽的数量及分布的变化规律相同,说明其结构存在一致性。3种碳纤维的圆度等表面物理特征存在一定差异,T300的圆度小于国产GCF-1及GCF-2碳纤维。     

无纬碳布增强针刺毡C/C复合材料性能的研究

比较了几种不同工艺制备的针刺毡C/C复合材料。对针刺碳毡织物首先进行预增密处理,得到初始密度和碳纤维含量较高的坯料,然后用树脂浸渍法进一步致密化。研究表明,用该方法制备的C/C复合材料比未经预处理的试样,拉伸强度提高39%,压缩强度提高14%,层间剪切强度提高36%。通过SEM观察和常温力学性能的测试,分析表明工艺的改进是强度提高的主要原因。