钢铁低温发兰,磷化液的研究

发兰，磷化是钢铁表面处理应用最为广泛的工艺。该研究得出了最新工艺配方，使发兰，磷化工艺具有低温性，低渣量，快速性，低成本的特点。     

玻璃纤维增强酚醛基复合材料平均线胀系数测试影响因素

研究了保温时间、升温速率、预处理温度等对玻璃纤维增强酚醛基复合材料线胀系数测试的影响。结果表明,玻璃纤维增强酚醛基复合材料在加热条件下进一步固化,造成样品收缩与样品受热膨胀相抵消,升温曲线出现平台。因此,测试前应对样品进行预处理,处理温度高于试样最终的测试温度,低于样品固化温度,以免材料内部结构发生变化;设置合适的升温速率,升温速率低,增加了时间成本,升温速率太高,测温热电偶引入的误差增加,且不均匀的加热使试样产生热应力,影响试验结果。     

45CrNiMo1V超高强度钢研制及应用

介绍了４５ＣｒＮｉＭｏ１Ｖ超高强度钢的相变温度、冷却转变曲线、热处理工艺参数，物理性能、冷成形和焊接工艺性能及应用状况。为应用该钢提供了有用的试验数据。     

频率标准用超导铌腔内表面处理工艺研究

频率标准用超导铌腔内表面的处理是影响超导腔Q值的最大因素。本文首先通过理论分析确定了超导腔Q与表面剩余电阻的关系,其次通过一系列的表面处理工艺来保证超导腔内表面的剩余电阻尽量小,最后通过实验得到了超导腔的Q值为1.9E9,与理论计算结果相近,证明了表面处理的有效性。     

直升机机内PWM照明调光系统产生音频干扰问题的研究

在直升机机内照明调光领域，国外军机已广泛采用脉冲宽度调制（PWM）调光方式。PWM调光方式相比传统线性调光方式具有以下明显优点：效率高，调光范围宽，功耗小，带载能力强，附加损耗小等。但PWM调光系统的不足是电磁辐射，尤其会对机内通话系统产生音频干扰，在机通耳机中会出现明显干扰声，影响机内通话质量。本方案能有效抑制PWM...     

Tolerance of wheat and lettuce plants grown on human mineralized waste to high temperature stress

The main objective of a life support system for space missions is to supply a crew with food, water and oxygen, and to eliminate their wastes. The ultimate goal is to achieve the highest degree of closure of the system using controlled processes offering a high level of reliability and flexibility. Enhancement of closure of a biological life support system (BLSS) that includes plants relies on increased regeneration of plant waste, and utilization of solid and liquid human wastes. Clearly, the robustness of a BLSS subjected to stress will be substantially determined by the robustness of the plant components of the phototrophic unit. The aim of the present work was to estimate the heat resistance of two plants (wheat and lettuce) grown on human wastes. Human exometabolites mineralized by hydrogen peroxide in an electromagnetic field were used to make a nutrient solution for the plants. We looked for a possible increase in the heat tolerance of the wheat plants using changes in photosynthetically active radiation (PAR) intensity during heat stress. At age 15 days, plants were subjected to a rise in air temperature (from 23 ± 1 °C to 44 ± 1 °С) under different PAR intensities for 4 h. The status of the photosynthetic apparatus of the plants was assessed by external СО₂ gas exchange and fluorescence measurements. The increased irradiance of the plants during the high temperature period demonstrated its protective action for both the photosynthetic apparatus of the leaves and subsequent plant growth and development. The productivity of the plants subjected to temperature changes at 250 W m⁻² of PAR did not differ from that of controls, whereas the productivity of the plants subjected to the same heat stress but in darkness was halved.     

Ni18%和0Cr15Ni5Cu2Ti异种钢材电子束焊接工艺试验研究

对Ni18%和0Cr15Ni5Cu2Ti超高强度马氏体沉淀硬化不锈钢异种钢材之间进行了电子束焊接工艺试验,就其工艺可焊性及接头性能、金相组织、焊缝质量、力学性能等开展研究,采用X-探伤、静载强度、金相观察、电镜扫描和能谱分析等检测手段对试件进行了分析并得出了相应结论。     

氨合成-水热改性法制备氢氧化镁阻燃剂

为了解决氢氧化镁和聚合物之间的不相容问题, 对氨合成法-水热改性处理2步法制备高分散氢氧化镁阻燃剂进行了研究,分析了常温合成温度、水热改性温度和水热改性时间对制备大晶型、低比表面积氢氧化镁阻燃剂的影响.结果表明,经过水热改性处理改变了氢氧化镁晶体的生长习性,生成了形貌规则、粒径分布均匀、分散性良好的氢氧化镁六方片状颗粒.另外通过提高氯化镁浓度和氨水过量1倍,探讨了常温合成反应的转化率,认为应该在反应原料等当量下寻求提高转化率的可行方法.     

电镀Ni-Sn合金热处理前后的组织和性能

分析了电镀Ni-Sn合金各种镀层的镀态组织和加热时组织的转变机理,并对镀层的耐磨性、耐蚀性进行了对比实验.结果表明,镀态组织主要由亚稳相αNi(M)和NiSn(M)组成,高Sn时出现平衡相Ni3Sn4和βSn;加热时随着温度升高,亚稳相逐渐向平衡相转变,在一定的温度下由于平衡相弥散析出,使镀层硬度升高;单相NiSn(M)组织耐强氧化性介质能力比不锈钢稍差,当加热到400℃时耐磨性优于中碳钢淬火.     

GH4049合金的大晶粒问题探讨

通过一系列试验，发现ＧＨ４０４９合金出现大晶粒问题与零件的加热速率有密切关系。通过对试验结果进行详细的讨论，得出结论：零件的固溶热处理制定应为Ａ类，即１２００℃固溶，到温装炉，保温２ｈ后空冷。