Dynamic analysis of C/C composite finger seal

A seal device as an important component of aeroengines has decisive influence on per- formance, reliability, and working life of aeroengines. With the development of aeroengines, demands on the performance characteristics of seal devices are made strictly. Finger seal as a novel kind of sealing device, recently attracts more and more attentions in academic circles and engineer- ing fields at home and abroad. Research on finger seals has been extensively developed, especially on leakage and wear performances under dynamic conditions. However, it is a pity that the work on finger seals has been limited with a single approach that is improving the performance by structural optimization; in addition, the technology of dynamic analysis on finger seals is weak. Aiming at the problems mentioned above, a distributed mass equivalent dynamic model of finger seals considering the coupling effect of overlaid laminates is established in the present paper, the dynamic perfor- mance of 2.5 dimension C/C composite finger seal is analyzed with the model, and then the effects of fiber bundle density and fiber bundle preparation direction on finger seal＇s dynamic performance are discussed, as well as compared with those of Co-based alloy finger seal. The current work is about dynamic analysis of finger seals and application of C/C composite in this paper may have much academic significance and many engineering values for improving research level of finger seal dynamics and exploring feasibility of C/C composite being used for finger seals.     

面内弯曲载荷作用下两边简支两边固支复合材料层合板的屈曲

为扩充航空复合材料结构稳定性设计手段,基于Levy形式级数和有限差分法,提出了面内纯弯曲载荷作用下两边简支两边固支（SSCC）复合材料层合板临界屈曲载荷的数值解法。首先,应用有限差分法将挠度函数进行离散化处理;然后利用边界条件扩充方程组,最后将临界屈曲载荷的求解转化为广义特征值问题。通过数值算例分别在各向同性板和复合材料层合板上验证了本文方法,并与有限元方法（FEM）进行了比较。结果表明,本文方法具有很高的精度,为复合材料层合板的屈曲分析开辟了新的途径。     

压辊材料及形状对纤维铺放压紧效果的影响

近年来纤维铺放（AFP）技术被广泛用于大型复杂飞机复合材料构件成型。为了保证纤维铺放过程的一致性,纤维铺放压辊必须在适应芯模型面的同时具有较好的压紧力分布均匀性。鉴于此,对不同弹性模量的压辊材料进行了试验分析,薄膜压力传感器及超声显微镜测试结果表明,低弹性模量的压辊材料变形较大,较好地适应了芯模表面,压力分布相对均匀且可以减少铺层的层间孔隙数量,硅橡胶压辊比聚乙烯压辊压紧力分布均匀性提高了50%~60%,铺层孔隙率降低了92.1%。针对孔隙分布主要集中在压辊两端及压紧力在压辊两端下降幅度较大的问题,采用ANSYS Workbench对压辊端部进行斜端面优化,得到最优倾斜角度为20°;测试结果表明斜端面压辊压力分布均匀性比直断面压辊提高了42.9%,铺层孔隙率下降了51.6%。     

硫化压力对橡胶／金属热硫化粘接剥离强度的影响

研究 NR1155天然橡胶在不同硫化压力下热硫化后的物理力学性能。基于90°粘合剥离强度测试方法分别测量了不同硫化压力下制备的橡胶／金属复合结构试样的粘合剥离强度,并采用低场 NMR 橡胶交联密度测定仪分析试样中橡胶部分的交联密度,同时采用冷场发射电子扫描显微镜（SEM）研究剥离破坏表面。结果表明：NR1155天然橡胶胶料与 Chemlok205／Chemlok220热硫化胶粘体系具有很好的相容性和协同硫化作用。随着硫化压力的提高,橡胶／金属的粘合剥离强度呈现先降低后增加的规律,且最大剥离力呈现对硫化压力的函数依赖关系,而硫化胶的交联密度则呈现相反的趋势。     

基于代理模型的二元收扩喷管流道型面优化设计

在二元收扩（2D-CD）喷管设计参数对喷管气动性能影响研究的基础上,以获得尽可能高的喷管推力系数为目标,以喉道宽高比、喉道型面半径比、收敛半角和扩张半角为设计变量,对二元收扩喷管的流道型面进行了优化设计。设计过程中,利用正交试验设计方法确定初始样本点,建立喷管推力系数与设计参数间的Kriging代理模型,采用自适应模拟退火算法（ASA）对代理模型进行分析求解。结果表明,二元收扩喷管的优化型面参数为:喉道宽高比为6,喉道型面半径比为0.3,收敛半角为15°,扩张半角为5.64°,此时最大推力系数为0.97847,流量系数为0.98778.      

航空碳纤维树脂基复合材料加筋板压缩屈曲及后屈曲性能

开展了复合材料加筋板轴压稳定性实验,对加筋板的屈曲及后屈曲性能、破坏模式和后屈曲失效表征进行了研究.实验结果表明加筋板在轴压下具有良好后屈曲承载潜能,破坏载荷约为屈曲载荷的2.2倍;其屈曲模式为筋条间蒙皮首先发生屈曲失稳,筋条在整个承载过程中保持直线,起到“屈曲分隔”的作用.通过对加筋板屈曲及后屈曲性能的理论分析,得出的理论屈曲载荷和理论破坏载荷与实验结果相对误差均小于8%,并确定了在后屈曲过程中蒙皮中心挠度的变化规律和轴向载荷的面内分布特征.      

复合材料夹层结构在航空领域的应用

详细描述了复合材料夹层结构及几种常用芯材的性能特点,综合分析了复合材料夹层结构在飞机上的应用案例,对各种夹层结构芯材成型工艺的重点、难点进行了探析,得到了复合材料夹层结构的性能概况及使用工艺要求,可为复合材料夹层结构设计、制造提供参考。     

复合材料开口结构参数化建模技术研究

基于MSC.Patran软件,运用PCL语言编写了参数化建模程序,实现了多种开口形式和加强形式的复合材料开口结构二维模型快速化、自动化建立。运用刚度等效原理将复合材料任意截面形式的筋条等效成各向同性矩形实心筋条,解决了目前有限元软件中没有提供复合材料一维梁单元的问题。结合复合材料开口结构刚度计算与优化设计实例,验证了建模方法的准确性与实用性。     

客机复合材料APU舱门结构设计及分析

按照结构布局、适航要求及APU门载荷水平,对复合材料APU舱门结构进行设计研究.为满足防火要求和闪电防护要求,选择先进碳纤维复合材料和泡沫芯材,设计了一种复合材料夹层结构.利用有限元模型对夹层结构在气动载荷和风载作用下进行应力和位移分析,得到应变云图和变形云图,分析说明该夹层结构设计满足设计要求.通过对B737飞机APU舱门结构研究和重量提取,进行重量等效对比分析,结果表明该复合材料夹层结构比金属结构重量轻25.8％,减重效果明显.     

环氧树脂基形状记忆复合材料的制备与性能

以自制的形状记忆环氧树脂为基体,CCF300级碳纤维U-3160织物为增强材料,采用真空袋成型工艺制备形状记忆复合材料,分析碳纤维含量对复合材料的形状记忆性能的影响。结果表明,当碳纤维含量为0%~50%时,随着增强体碳纤维含量的增加,复合材料的形状固定率由98%降至91%,形状回复率也由98%降至91%。在有限次的循环实验中,循环次数对形状固定率和形状回复率没有明显的影响。