为提高硅橡胶胶黏剂胶接石英陶瓷和碳纤维增强复合材料的强度和耐温性能,研究了胶接面湿热状态、打磨程度、胶层厚度、操作等待时间等工艺参数对胶接强度的影响。在试片正常烘干、打磨的情况下,当胶层厚度为0.4 mm、操作等待时间小于0.5 h时,胶接效果最优,其压缩剪切强度达到了3.06 MPa。探索了底涂剂处理对胶接强度和耐温性能的影响。在温度不高于100℃时,底涂剂A的效果较好。经底涂剂A处理后,胶接试片常温下的强度提高了13.7%,达到3.48 MPa;100℃时的强度提升率达到37.7%。在更高温度下,底涂剂B的效果更为显著。经底涂剂B处理后,胶接试片常温下的强度提升了10.1%,达到3.37 MPa;300℃时的强度提升了44.0%,达到1.57 MPa;200℃时的强度提升率最高,为49.0%。测试结果为高温条件下石英陶瓷胶接结构的胶接工艺优化及其应用提供了参考。     

除冰液对道面混凝土的影响及保护剂防护效果

通过冻融和化学侵蚀试验，研究了NW-056A机场道面除冰液对道面水混混凝土耐久性的影响以及在道面除冰液环境下两种新型混凝土保护剂的防护效果。结果表明：①混凝土在道面除冰液中冻融后表面无明显剥落现象，相对动弹模损失率比在水中小很多，道面除冰液延缓了混凝土的冻融破坏：②混凝土在道面除冰液常温浸泡下表面无剥蚀现象，但强度比在水中降低很多，因此存在化学腐蚀．且主要表现为对混凝土内部结构的缓慢损伤；（④两种新型混凝土保护剂均对预防混凝土的冻融破坏以及除冰液环境下的腐蚀破坏起到一定作用，涂刷混凝土保护剂是提高混凝土道面耐久性的有效方法。     

Sulfur “concrete” for lunar applications – Sublimation concerns

Melting sulfur and mixing it with an aggregate to form “concrete” is commercially well established and constitutes a material that is particularly well-suited for use in corrosive environments. Discovery of the mineral troilite (FeS) on the moon poses the question of extracting the sulfur for use as a lunar construction material. This would be an attractive alternative to conventional concrete as it does not require water. However, the viability of sulfur concrete in a lunar environment, which is characterized by lack of an atmosphere and extreme temperatures, is not well understood. Here it is assumed that the lunar ore can be mined, refined, and the raw sulfur melded with appropriate lunar regolith to form, for example, bricks. This study evaluates pure sulfur and two sets of small sulfur concrete samples that have been prepared using JSC-1 lunar stimulant and SiO₂ powder as aggregate additions. Each set was subjected to extended periods in a vacuum environment to evaluate sublimation issues. Results from these experiments are presented and discussed within the context of the lunar environment.     

Progress in the Study of Galaxies: Structures,Collective Phenomena and Methods

The review contains the important achievements in dynamics of the galactic disks. Among them there are I. New structures discovered recently: • giant vortices (including giant anticyclone in the Solar vicinity); • slow bar; • inner oscillating structure within spiral arms similar that of enveloped soliton; • chaotic streamlines in the velocity field of the gaseous disk of a real galaxy. II. New collective phenomina discovered recently: • new overreflection instability initiating ‘mini-spiral’ in the innermost central parsec of Galaxy; • large-scale convection caused by nonlinear interaction of density wave with disk gas; • non-kolmogorovian spectrum of weak turbulence corresponding to the observed one in the • Solar vicinity. III. New methods worked out recently: • reconstruction of full three-dimensional vector field of gas velocity from the observed line-of- • sight velocity field; • observational test for verification of the wave-nature of the spiral arms; • observational test to distinguish two types of vertical motions: warp and z-motions in the • density wave; • derivation of correct system of two-dimensional dynamical equations from the initial three- • dimensional one. This revised version was published online in June 2006 with corrections to the Cover Date.     

玻璃钢圆筒壳体内压下的变形及破坏强度

本文以线弹性薄膜理论为基础对固休火箭发动机玻璃钢筒体内压下变形,同时应用最小余能原理对其破坏强度问题分别进行了理论分析与计算.通过对全尺寸壳体的变形测试和爆破压力试验,以及对标准容器进行的批量爆破试验,证实理论分析基本符合试验结果.     

翼盒结构的可靠性分析及基于系统可靠性的优化设计

 本文研究了翼盒结构的可靠性分析及基于系统可靠性的结构优化设计方法。采用发展了的优化准则法枚举系统的主要失效模式,和Feng的高精度法计算系统破坏概率,提出两个迭代公式进行元件尺寸的优化设计。算例结果表明本文方法是中、大型结构系统可靠性分析及优化设计的有效方法。     

星载毫米波反射面天线结构

“神舟4号”飞船的多模态微波辐射计天线的工作频率跨到毫米波段．这在我国过去的航天器天线中尚未遇到．采用了计算机机电热一体化设计手段，从材料的选择入手，把最佳的电性及结构设计、先进有效的制造、检测与装配技术有机地融为一体之后，保证了天线最终的高精度指标．本文从高精度反射面天线的要求出发，从设计、分析、实现以及验证多方面说明星载反射面天线形面高精度的控制与实现．     

L型复合材料机械连接接头承载能力与失效行为研究

L型复合材料连接结构已应用于运载火箭结构的端框设计,但目前对于该结构的承载能力和破坏模式缺乏研究。将典型的L型连接端框简化为无弧度的平直L型接头片段,通过单向对拉试验,对6 mm和8 mm两种厚度L型机械连接接头的承载能力和破坏模式进行了研究。由承载能力试验结果表明:L型接头在拉力作用下呈现出明显的A、B、C三个阶段,其中A阶段的拉力最大值可作为该类接头结构的极限承载能力。采用有限元方法分析接头的破坏模式,仿真与试验结果的误差为2.5%,取得了较好的一致性。由数值分析表明:拉力作用下L型接头的承载能力主要取决于螺栓压紧区附近和直角拐角区域的层间强度和基体强度;在原铺层信息基础上增加0°层数和降低90°层数,对接头承载能力提升效果不明显。研究结果可为L型复合材料连接结构的设计提供参考。     

航空铆钉连接件的抗冲击性能

以分离式Hopkinson拉杆装置为基础,设计了特殊的铆接试验件,对MS20615铆钉的铆接结构开展了动态加载下不同加载角度、不同加载速率的力学性能试验。结合其准静态试验结果,获得了铆接结构在纯剪切、30°拉剪耦合、45°拉剪耦合、60°拉剪耦合和纯拉伸试验下的力学性能参数。试验结果表明,加载角度、加载速率对铆接结构的失效载荷与失效模式有显著的影响。在试验结果的基础上,使用有限元软件LS-Dyna建立了铆接结构的简化模型,对比了试验和数值模拟得到的铆接结构载荷-位移曲线,并对简化数值模型进行了网格相关性分析,验证了简化的铆钉单元模型的可行性。     

纤维增强复合材料层合板分层扩展行为研究进展

纤维增强复合材料层合板在航空航天等领域被广泛应用,分层损伤是层合板主要的损伤形式,一直是复合材料力学研究的焦点问题之一。本文从试验研究、理论分析和数值模拟3个方面对国内外在纤维增强复合材料分层问题所取得的研究成果进行了系统综述,重点介绍了单向复合材料I型、Ⅱ型和I/Ⅱ复合型层间断裂韧性测试方法和原理以及多向层合板分层扩展行为的试验研究。得到了表征和评价分层失效机理和扩展行为的纤维桥接模型、静力分层扩展准则和疲劳分层模型,并详细阐述了采用内聚力模型（CZM）、虚拟裂纹闭合技术（VCCT）和扩展有限元方法（XFEM）等先进数值方法模拟分层扩展的研究现状。最后,对复合材料层合板分层扩展研究的发展方向进行了展望。