纤维表面涂层对碳纤维/聚芳基乙炔性能的影响

为提高碳纤维/聚芳基乙炔(CF/PAA)复合材料的性能,采用不同种类的涂层(环氧,硅氧烷和倍半硅氧烷)对碳纤维(CF)进行表面改性。通过复合材料的短梁弯曲和热氧老化试验表征不同涂层的改性效果。层间剪切强度(ILSS)结果表明,倍半硅氧烷涂层具有最好的处理效果。热氧老化测试结果表明,倍半硅氧烷涂层适用于耐热树脂体系。这种涂层可以通过改变官能团适应不同树脂体系复合材料的界面改性。     

碳纤维增强塑料的强度与碳纤维性能的关系

本文探讨了碳纤维增强塑料的强度与碳纤维性能的关系,结果表明二者关系密切,并指出根据材料在结构中的不同工作条件确定对碳纤维的要求时,应综合考虑对其工作性能起决定性作用的各种因素。     

新生代的气候效应与碳循环

对发生于新生代的６次巨大天体撞击作用（６５Ｍａ，３４Ｍａ，１５Ｍａ，２４Ｍａ，１．１Ｍａ，０．７Ｍａ）的气候效应进行的模拟表明，这６次巨大天体撞击作用产生的尘埃进入平流层后，可使全球平均温度下降至零度以下，降温效应持续时间最长可达３０年之久，首次在模拟中考虑全球性森林大火产生的ＣＯ２和死亡生物分解生成的ＣＯ２的温室效应，研究表明这两种作用使大气中ＣＯ２增量最大仅达６７％，其增温效应远远低于尘埃层产     

Fabrication of Diamond-like Carbon Films by Ion Assisted Middle Frequency Unbalanced Magnetron Sputtering

Diamond-like carbon (DLC) films are deposited by the Hall ion source assisted by the mid-frequency unbalanced magnetron sput-tering technique. The effects of the substrate voltage bias, the substrate temperature, the Hall discharging current and the argon/nitrogen ratio on the DLC film’s performance were studied. The experimental results show that the film’s surface roughness, the hardness and the Young’s modulus increase firstly and then decrease with the bias voltage incrementally increases. Also when the substrate temperature rises, the surface roughness of the film varies slightly, but its hardness and Young’s modulus firstly increase followed by a sharp decrease when the temperature surpassing 120 ℃. With the Hall discharging current incrementally rising, the hardness and Young’s modulus of the film decrease and the surface roughness of the film on 316L stainless steel firstly decreased and then remains constant.     

Study on Microwave Dielectric Property of Carbon Black and Short Carbon Fibers

Carbon black and carbon fibers of different lengths were introduced in different matrices at different ratios to explore their microwave dielectric properties under 8.2 GHz-12.4 GHz. It is found that the actual dielectric constants of the samples containing carbon black are in a two-order function of the contents of carbon black （ε＇, ε＂=Av2＋Bv＋C） and the complex dielectric constants show an obvious frequency response. Of the added fibers of different lengths, the 4 mm-long one could well disperse in the matrices having not only good frequency response, but also larger real parts, imaginary parts and loss values. The imaginary parts and the loss values （tanδ）of the samples with 4 mm-long carbon fibers added increase linearly with the contents of fiber increasing. So it is practicable to adjust the dielectric parameters of the material in a wide range by changing the added amount of carbon black, and the carbon fiber or altering the lengths of the carbon fiber added.     

短碳纤维增强PPEK复合材料的性能研究

采用熔融共混的方式制备了不同短碳纤维含量增强含二氮杂萘酮聚芳醚酮(PPEK)基复合材料，对复合材料的加工性能、力学性能、摩擦性能、耐热性进行了研究。结果表明：短碳纤维增强复合材料均可以注塑成型；短碳纤维对PPEK的增强作用明显，拉伸强度和弯曲强度均有大幅提高；复合材料中短碳纤维起到了明显的自润滑作用，复合材料的摩擦系数和磨损率均随碳纤维含量的增加而明显降低；短碳纤维的加入进一步提高了复合材料的耐热性。     

C/C复合材料致密化制备技术发展现状与前景

综述了C／C复合材料致密化制备技术，分析比较了化学气相渗透工艺、液相浸渍工艺及化学液－气相沉积工艺的优缺点。认为化学气相沉积工艺在过去一些年中发展很快，但它的工艺周期长；液相浸渍工艺繁杂，其浸渍炭化和石墨化工序需反复多次（通常4－6次），因此其效率也比较低；而液－气相沉积工艺周期短、效率高，很有发展潜力，当前急需开展该沉积技术原理的研究及改进其实验设施。     

短切炭纤维/酚醛树脂胶粘剂的配方研究

为确定最佳组分含量,采用正交实验法对“酚醛树脂(PF) 纳米S iO2粉 石墨粉 ZrO2粉 短切炭纤维”胶粘剂体系进行了配方研究,并探讨了组分含量对胶粘剂性能的影响。得到的最佳配方为“PF 2%纳米S iO2粉 1%石墨粉 1%ZrO2粉 4%短切炭纤维”,其对石墨材料的粘接强度达11.6 MPa,胶粘剂本体线烧蚀率为0.058 mm/s,质量烧蚀率为0.0732 g/s。胶粘剂可进一步用于粘接修复C/C复合材料喉衬构件的工艺缺陷。     

低成本炭/炭复合材料的研究进展——化学液相沉积工艺

简述了制备炭/炭复合材料的新工艺——化学液相沉积(CLD)的沉积原理。利用工业燃油作为裂解炭前驱体,炭纤维毡作为增强体,通过工艺参数控制得到低成本炭/炭复合材料。CLD工艺所得材料沉积密度1.6 g/cm3,轴向压缩强度92 MPa,等离子烧蚀率0.06 mm/s,与CVD工艺所得材料相近。与常规CVD工艺相比,CLD工艺制备的C/C复合材料在制备时间上缩短了4/5,致密速率快5倍多。所得基体裂解炭为粗糙层与光滑层结构(大部分为粗糙层结构)。基体炭与炭纤维接合界面适中,且呈洋葱状分布,从而材料具有一定韧性。     

细编穿刺三向碳／碳材料应力集中问题的研究

通过数值模拟和试验的方法，对弹头端头帽所采用的细编穿刺三向碳／碳材料的应力集中问题进行了研究，对试验结果进行了分析。对深入了解该材料的力学性能有较大帮助，并已应用于设计。