刀具织构轮廓对碳纤维增强复合材料面下损伤影响的切削仿真研究

为减小碳纤维增强复合材料（CFRP）加工时的面下损伤深度,创建了基于二维Hashin准则的宏观连续动态切削CFRP有限元模型,分析了切削力和面下损伤深度与纤维方向角之间的变化趋势,通过引入织构刀具来降低切削力及面下损伤深度,比较了沟槽形织构刀具、圆形织构刀具、三角形织构刀具切削CFRP的切削力和面下损伤。结果表明,不同织构刀具的切削力和面下损伤深度随纤维方向角变化趋势一致,均在0°时最小,90°达到最大值;织构刀具相对传统无织构刀具切削CFRP时均降低了切削力和面下损伤深度,其中圆形织构刀具降低程度最大;仿真模型经实验验证准确有效。     

航空复合材料纸蜂窝夹芯结构热成型开裂研究

飞机复合材料芳纶纸蜂窝夹芯部件在热压罐成型时处于热-力耦合工况。本文关注热成型过程中可能出现的蜂窝开裂现象,通过试验获得了蜂窝芯的拉、压、剪性能参数和芳纶纸的热性能参数,同时结合有限元分析手段和反演方法,对整体蜂窝夹芯部件的热-力顺序耦合和局部芯子抽真空导致的蜂窝胞元间压强差进行数值模拟。结果表明：成型过程中的热应力不会导致蜂窝胞元间胶层开裂,局部憋气的压差可能导致蜂窝开裂;胶层部分破坏与胶层完全破坏所需的胞元间压强差的差值与胶层初始法向断裂应力正相关;胶层完全破坏所需的胞元间压强差随着受载胞元数量的增多而减小。     

Out of phase thermal mechanical fatigue investigation of a directionally solidified superalloy DZ125

Out of phase(OP) thermal mechanical fatigue(TMF) behavior of a directionally solidified(DS) superalloy DZ125 was experimentally and numerically studied. Two different temperature conditions, which are 500–1000 °C and 400–900 °C, were considered in the present research.Stress and strain responses as well as fatigue life results were presented and discussed. Scanning electron microscope(SEM) and metallographic analysis were used to study the damage mechanism. An oxidation assisted crack initiation and propagation phenomenon were found to explain the shorted life under TMF cycles. In order to characterize the stress and strain deformations under TMF loadings, a modified Chaboche's constitutive model was applied. Additionally, the TMF life of the material was modeled and predicted by Neu–Sehitoglu damage law with high accuracy.     

应用少量短电阻应变丝布置的损伤评估智能材料结构

智能材料结构是一门新学科，它越来越引起不同学科研究者们的兴趣，本文研究采用电阻应变丝为传感元件，人工神经网络为处理辨识器的损伤评估智能材料结构，提出并实施了一种少量短电阻应变丝的传感元件布置方法，用以对结构中损伤或大应变的区域和级别进行在线评估。     

Experimental method for and theoretical research on defect tolerance of fixed plate based on damage mechanics

An experimental method and a theoretical analysis based on continuum damage mechan-ics are applied for the defects tolerance of fixed plate. The defects type studied in this article is scratch, which i...     

Comparison of model and experimental ionospheric parameters at high latitudes

Modern use and study of the auroral region needs to attract a wider class of models for describing conditions of radio wave propagation in the ionosphere. In this paper the possibilities of the International Reference Ionosphere model, well-proven and widespread in the mid-latitudes, are investigated in the high latitude zone. Model and measured values of the critical frequency foF2 for two mid-latitude stations (Juliusruh and Goosebay) and four high-latitude ones (Loparskaya, Sodankyla, Sondrestrom, Thule) are compared. Deviations of medians, variations from day to day and solar activity trends seemed to be similar for both areas. This similarity is irrespective of the RZ12 index. Special attention is paid to the TEC parameter and its determination using 6 versions of models, a new version of the model IRI2010 (IRI-Plas) among them. It is shown that the IRI-Plas model significantly improves the definition of TEC in contrast to the versions of IRI2007 and the new model NeQuick. The use of the median of the experimental equivalent slab thickness, together with the current values of the TEC, increases by a factor of two the agreement between calculated and measured foF2 values as compared with the variations from day to day. This allows foF2 to be defined in near-real time.     

Experimental method for and defect tolerance of fixed plate theoretical research on based on damage mechanics

An experimental method and a theoretical analysis based on continuum damage mechan- ics are applied for the defects tolerance of fixed plate. The defects type studied in this article is scratch, which is considered a typical defect on fixed plate according to the engineering practice. The general approach to the defects tolerance analysis of scratched fixed plate is presented. The method of fatigue life prediction for standard notched specimens has been established on the basis of continuum damage mechanics. For the purpose of obtaining the influence law of fatigue life in consequence of scratches, fatigue experiments of standard notched specimens and scratched specimens have been done. Evalu- ation of the fatigue life of scratched fixed plate has been carried out. And the value of scratch defects permissible to the condition of safety service life has been worked out. According to the results of the- oretical calculations, the fatigue experiment of scratched fixed plate has been performed. The outcome shows that the theoretical prediction tallies with the experimental results.     

新乡市工业化与城镇化互动关系研究

采用定量指标IU比和NU比分析了新乡市1978-2010年的城镇化与工业化对比关系，总体而言新乡市城镇化水平低于工业化水平。对新乡而言，应该借助中原经济区建设的契机，依托现有的城镇和工业基础，推进产业结构的优化，大力发展第三产业和服务业，加快体制创新，促进农村劳动力向城镇转移，增加就业。     

对我国企业广告误区的分析

随着我国社会主义商品经济发展到以销定产的买方市场阶段，企业广告活动的数量、范围都在大幅度地增长。但在快速增长的同时，也存在着一系列的问题，作者对这些问题加以分析。     

首都机场双跑道独立运行的设想与研究

目前首都机场的双跑道隔离运行方式无法适应航空运输业的飞速发展,抑制了首都机场的枢纽化进程.通过对首都机场运行状况的分析及其与国外机场的比较,认为双跑道独立运行方式是一种先进的管制方法,而且投资少,见效快,可以使机场跑道的容量成倍增长.独立运行的核心问题是如何保障进近过程中航空器的安全,它对空域、跑道监视设备和监控方法都提出了更高的要求.给出首都机场双跑道独立运行的设想和初步研究,为首都机场的发展提供了必要的理论支持与技术保障.