Effect of Rhenium Addition on Isothermal Oxidation Behavior of Tribaloy T-800 Alloy

The effects of 4 wt% rhenium (Re) addition on isothermal oxidation behavior of Tribaloy T-800 alloy have been studied at 800 °C and 1 000 °C in air. At 800 °C, T-800 shows nonuniform oxidation between dendritic and eutectic areas. Re addition clearly promotes the nonuniform oxidation, leading to considerably higher mass gains than that of T-800 at this temperature. At 1 000 °C exposure, the thickness of scale on T-800 increases significantly, accompanied by severe scale spallation during cooling to room temperature. On the contrary, T-800Re shows a marked decrease of oxide growth rate compared to the linear one of T-800 at 1 000 °C. The scale adhesion is also improved with Re addition at this higher temperature. Therefore, the role of Re depends on the exposure temperature. Re addition gives high oxidation rate at 800 °C, however, the excellent oxidation resistance is obtained by the addition of Re at a higher temperature of 1 000 °C.     

真空与磁场热处理改善FeCo合金的软磁性能

针对发电机中转子用FeCo合金(国产牌号1J22)进行了组织结构与磁性能的研究.通过对该合金进行真空处理以及磁场热处理,研究了组织结构对软磁性能的影响规律;研究了附加磁场强度以及热处理温度对磁场处理效果的影响,并结合该合金的磁致伸缩伸缩系数的变化规律,分析了磁场热处理效果的微观机制.当合金组织为轧制态时,磁场热处理效果不明显;在合金的再结晶温度以上进行磁场热处理时,获得了显著的磁场热处理效果,矫顽力下降至72A/m(0~9Oe)以下.     

火箭发动机燃烧室用高强高导Cu-0．8Cr-0．2Zr合金的组织与性能

采用硬度、拉伸力学性能及导电率测试研究了Cu-0.8Cr-0.2Zr合金的力学性能和导电性能,采用金相显微镜(OM)和透射电子显微镜(TEM)观察了不同处理态合金的显微组织。研究结果表明:时效热处理过程中,合金发生回复和再结晶,同时过饱和固溶体分解析出新相,析出的纳米弥散强化相,能显著提高合金的强度,同时保持良好的导电性。Cu-0.8Cr-0.2Zr合金的最佳热处理工艺为:热轧后980℃/1h固溶处理,经70%冷变形,然后再经过450℃/4h时效处理后,硬度、抗拉强度和屈服强度分别为153HB5、29MPa和489Mpa,导电率达到85.1%IACS。研究的加工工艺实现了高强高导,获得了强度和导电率的最佳匹配。     

置氢对TC21合金粉末物理性能和压制性能的影响

采用扫描电镜观察、粉末镶嵌试样、XRD和模压成形等方法,研究了置氢(H,wt%)对TC21合金粉末颗粒形貌、表面状态、显微组织、相组成、显微硬度和压制性能等的影响.结果表明:置氢TC21粉末颗粒形貌为不规则状,粉末主要由亮相α相及暗相β相组成,颗粒显微组织呈片状、α/β集束状和网篮状.随置氢量的增加,置氢TC21粉末显微硬度呈降低趋势;α相逐渐减少,β相逐渐增多,并且有少量的α"相生成;粉末的压缩性能呈先变差后变好的不明显变化趋势,成形性能先变差又逐渐变好,置氢量0.10 wt%,0.39 wt%TC21粉末压制性能较好,置氢量0.22 wt%的TC21粉末的压制性能最差.     

铸造钛铝合金组织与力学性能

根据对钛铝合金铸态组织的金相观察,分析了合金元素Ｃｒ,Ｖ,Ｎｂ对铸锭组织的影响。研究发现,合金元素Ｃｒ,Ｖ有利于柱状晶生长,在这种柱状晶组织中γ／α２层片排列具有较强的择优取向,即层片界面垂直于柱状晶生长方向;而Ｎｂ抑制柱状晶生长,且含Ｎｂ的ＴｉＡｌ合金宏观等轴晶区和柱状晶区内层片组织均由等轴状的层片团构成,并以四点弯曲试验结果对不同合金化条件的钛铝合金的力学性能的方向性做了评价。     

超轻型Mg—Li合金

Ｍｇ－Ｌｉ合金具有高的比强度和比模量,在航天及航空等领域中具有广阔的发展前景。本文详细介绍了Ｍｇ－Ｌｉ合金的发展现状及性能改善的途径。     

LY12cz铝合金晶间腐蚀模拟试验研究

用金属间化合物 θ(CuAl₂)、S(Al₂CuMg)、MnAl₆与纯Al(L1)组成多电极体系,以模拟LY12cz合金的晶界区.通过电化学测试、SEM和能谱分析等方法研究了该合金晶间腐蚀机理.证实其晶间腐蚀是由沿晶界偏析的强化相与贫Cu区所组成的多电极体系引起的.在含Cl^－离子的中性溶液中,S相是导致晶间腐蚀的主要阳极相.S相首先发生阳极溶解,随后,贫铜区、MnAl₆相逐步随S相一起溶解.以这种方式沿晶界形成了阳极溶解通道,导致晶间腐蚀.     

Ti—15—3钛合金点焊工艺及性能研究

对我国新研制的β型Ｔｉ－１５－３新型钛合金进行了点焊工艺及性能研究,并与进口材料进行比较,从而对我国研制的Ｔｉ－１５－３钛合金的点焊焊接性作出评价为其在新机上的应用和该材料的国产化提供了可靠的依据。     

稀土元素及杂质在铝锂合金中的作用研究现状与发展

 综述了稀土元素和杂质对铝锂合金微观组织及力学性能的作用,概括了杂质致脆及稀土微合金化的规律与机制,根据已有研究结果,对目前铝锂合金的发展与应用中需要引起重视的问题,提出了某些观点与建议。     

钛合金切削挤压复合攻丝研究

将切削挤压复合攻丝新方法成功地用于高强度钛合金内螺纹的加工,这种方法不仅可以减小挤压扭矩而且能够强化螺纹根部。加工的挤压螺纹表面有一层纤维沿其牙形连续分布。利用云纹干涉法测得牙根处的最大残余压应力为120MPa左右。疲劳对比试验结果表明,在相同应力水平下,经挤压强化螺纹的疲劳寿命大约是未强化螺纹的３倍,这主要归因于挤压螺纹表面高的残余压应力,高的纤维密度和低的粗糙度。