Ti-6Al-4V合金多层板结构的超塑成形／扩散连接工艺研究

采用气压成形方法对多层板结构件进行了超塑成形/扩散连接(SPF/DB)技术研究。研究表明,最佳的扩散连接工艺参数为:连接温度T=930℃,连接时间t=30m in,连接压力P=10MPa。对连接试件的微观组织进行了观察,显示在界面处形成良好的连接。最佳的成形参数为:成形温度Tf=930℃,成形压力Pf=0.6MPa,成形时间tf=55m in。最后对成形后的板厚分布进行了研究。     

马赫数3～6宽速域内转进气道优化设计

基于对轴对称基准流场参数化研究选取半径适当小的可变中心体,再对其他设计参数进行灵敏度分析,得到设计参数对基准流场整体性能的影响规律,系数c的影响最为明显,同时各个设计参数之间耦合效应影响也很大。运用样本数据库,构建相应的神经网络近似模型并结合邻域培植多目标遗传算法对轴对称基准流场在马赫数为6时进行三目标优化,优化后的基准流场内收缩比降低了7.7%,总压恢复系数提高了2.3%,并且静压比提高了7.1%。基于此优化结果,进行内转进气道型面设计并对其在马赫数为3～6条件下黏性数值模拟,结果表明:优化后的内转进气道在马赫数为3工作时能够正常起动,在马赫数为4～6工作时,进气道有较高的压缩量,较好的流量捕获能力和总压恢复性能。      

钛合金TB6铣削表面粗糙度与表面缺陷研究

钛合金TB6铣削表面粗糙度对其使用性能具有重要影响,通过试验研究端面铣削参数、干铣削和刀具磨损对表面粗糙度及表面缺陷的影响。研究表明:表面粗糙度对每齿进给量变化最为敏感,其次是铣削宽度,再次为铣削深度,铣削速度最小;刀具磨损量(VB)对粗糙度产生明显影响,尤其VB大于0.2mm时,表面粗糙度将急剧增加,并导致划痕、孔洞缺陷;不同铣削条件下均存刀痕、侧流、隆起等缺陷;干铣削时加工表面出现熔敷物或熔滴,并增大毛刺;毛刺随切削速度的增大而变小,随刀具磨损量VB的增加而变大。钛合金TB6适宜在冷却润滑条件下低速铣削加工。     

表面状态及电解液对Ti6Al4V EJM加工质量的影响

钛合金广泛应用于航空发动机中,硝酸钠(Na NO3)电解液与氯化钠(Na Cl)电解液广泛应用于常规金属材料电化学加工。研究了钛合金在应用电解液喷射加工技术(EJM)时的表现。首先应用这两种电解液对两种不同表面质量的钛合金试件分别进行EJM加工试验,通过分析加工后所得样槽的深宽比、表面粗糙度、氧化物占比以及微观形貌,分析了钛合金原始表面状态以及电解液选用对最终加工精度的影响效果。在此基础上,以不同的顺序组合应用这两种电解液对优选出的钛合金试件再次进行EJM加工试验研究,确定最优的电解液组合应用顺序。两个系列的试验研究,为提高钛合金电化学喷射加工的质量与效率提供了一定的理论和试验依据。     

切削参数对Ti-6Al-4V锻件与粉末冶金工件表面粗糙度的影响对比

文摘表征了已加工Ti-6Al-4V锻件和粉末冶金工件表面形貌,利用正交回归试验得到了两种材料表面粗糙度值的数学模型,经过显著性检验两个数学模型能够准确地预测表面粗糙度值变化趋势。结果表明,Ti-6Al-4V锻件表面出现了进给划痕、切屑碎片和表面撕裂缺陷,粉末冶金材料表面出现了除了进给划痕、切屑碎片和撕裂外的微孔隙缺陷;两种工件表面粗糙度值均受到进给量的影响程度最大,同时粉末冶金材料内部残余微孔隙的存在导致切削速度对其表面粗糙度值的影响程度比较大。     

制导炸弹发射区研究

基于小型制导炸弹(炸弹+制导)气动特性、动力学方程、制导律、目标运动模型及发射区计算等飞行数值仿真模型与算法,在炸弹发射状态一定的情况下,通过不同的炸弹轨迹倾角、偏航角和目标运动的组合,仿真计算了大量的发射区.利用仿真软件C++与Matlab,能够较为直观地比较目标在运动状态不同情况下制导炸弹的发射区和6-DOF飞行轨迹.所得结论可为制导炸弹精确打击目标提供依据,提高了制导炸弹的作战性能.     

Preliminary results of space experiment: Implications for the effects of space radiation and microgravity on survival and mutation induction in human cells

In view of the concern for the health of astronauts that may one day journey to Mars or the Moon, we investigated the effect that space radiation and microgravity might have on DNA damage and repair. We sent frozen human lymphoblastoid TK6 cells to the International Space Station where they were maintained under frozen conditions during a 134-day mission (14 November 2008 to 28 March 2009) except for an incubation period of 8 days under 1G or μG conditions in a CO₂ incubator. The incubation period started after 100 days during which the cells had been exposed to 54 mSv of space radiation. The incubated cells were then refrozen, returned to Earth, and compared to ground control samples for the determination of the influence of microgravity on cell survival and mutation induction. The results for both varied from experiment to experiment, yielding a large SD, but the μG sample results differed significantly from the 1G sample results for each of 2 experiments, with the mean ratio of μG to 1G being 0.55 for the concentration of viable cells and 0.59 for the fraction of thymidine kinase deficient (TK⁻) mutants. Among the mutants, non-loss of zygosity events (point mutations) were less frequent (31%) after μG incubation than after 1G incubation, which might be explained by the influence of μG on cellular metabolic or physiological function. Additional experiments are needed to clarify the effect of μG interferes on DNA repair.     

一种基于并联关系模型的TC4合金本构方程

 以 TC4合金流动应力σ为目标函数,通过热态物理模拟试验,系统地研究了主要锻造热力参数 (变形温度、变形速度和变形程度等 )对目标函数的影响,基于数理统计学原理,科学地分析并回归出了能综合反映锻造热力参数对材料成形性能影响的本构方程,得出了 TC4合金变形工艺参数 (变形温度 T、等效应变速率ε、等效应变ε等 )对目标函数的影响规律,从而,为 TC4合金锻造过程的数值模拟和锻造热力参数的合理制订与控制提供了基础。     

某型歼击机飞行仿真建模与验模研究

介绍了某型歼击机全任务飞行模拟器的系统结构，针对该型歼击机的特点，详细讨论了在其飞行系统的建模与验模中应该考虑的各种因素、应遵循的原则及其实现方法等，并通过实例对其进行了验证。结果表明，方法是合理的。     

湍流模型在民机跨声速绕流计算的应用

针对民机构型DLR-F6翼身组合体,研究了不同湍流模型对气动特性和流场特征的影响.控制方程采用全场三维可压、雷诺平均的Navier-Stokes方程;计算格式采用Jameson中心有限体积、多步Runge-Kutta时间步长格式进行求解;湍流模型分别采用EARSMk-ω模型、Spalart-Allmaras(S-A)模型、SST模型、Standardk-ω(STDk-ω)模型、Low-Reynolds Numberk-ω(LRNk-ω)模型.通过对巡航状态的计算研究,分析了五种湍流模型在翼身结合处气流分离的特点,为工程应用提供了一定的借鉴意义.