Hot Tearing Behavior of Mg-Gd-Y-X Alloys

Mg-Gd-Y-Zr alloy castings are widely used in the aerospace field owing to their high strength and excellent creep resistance. The castability of these alloys is also an important consideration for engineering application. Thus， the hot tearing susceptibilities (HTSs) of Mg-10Gd-1Y-1Zn-0.5Zr (VW91) alloy and Mg-10Gd-2Y-1Zn-0.5Zr (VW92) alloy are investigated with a constrained rod casting (CRC) mold. The microstructures and fracture surface are characterized by optical microscope and scanning electron microscope. The results unveil that the HTS of VW92 alloy is lower than that of VW91 alloy. The microstructures indicate that obvious tears can be observed in VW91 alloy， while the tears in VW92 alloy are tiny. The tear feeding and healing by eutectic are also observed in VW91 and VW92 alloys. Therefore， the lower hot tearing susceptibility of VW92 alloy is mainly attributed to the high amount of eutectic which feeds and heals tears. Besides， the effects of the coefficient of thermal expansion (CTE) and the fluidity of VW91 and VW92 alloys on their HTSs are discussed.     

Microstructure and Hot Deformation Behavior of Mg-9Al-3Si-0.375Sr-0.78Y Alloy

Using Gleeble-3500 thermal simulator， the high temperature plastic deformation behavior and microstructure evolution of Mg-9Al-3Si-0.375Sr-0.78Y alloy are investigated at the temperature of 523 K?673 K and the strain rate of 10-3 s-1?10 s-1. True strain-true stress curves show the characteristics of the typical dynamically recrystallization process. The Arrhenius constitutive equation of the hyperbolic model is established. The average activation energy and the strain rate sensitivity index are， respectively， 221.578 kJ.mol-1 and 0.137. The result shows that the α-Mg phase exhibits dynamic recrystallization (DRX) characteristics obviously. But no DRX occurs in theβ-Mg17Al12 phase. Hot deformation does not affect the primary Mg2Si phase. Under the conditions of low temperature (523 K?673 K) and high strain rate (1 s-1?10 s-1)， the flow instability and macro-defects such as crack appear in the specimens. However， there are finer recrystallization grains. Under the conditions of high temperature (≥673 K) or low strain rate， the microstructure of the alloy shows good homogeneity. The size of the primary Mg2Si phase is uniform， the size of the β-Mg17Al12 phase is small， and the distribution of the β-Mg17Al12 phase is uniform.