Microstructure and Martensitic Transformation Behaviors of Explosively Welded NiTi/NiTi Laminates

The study is a first attempt to prepare bulk NiTi/NiTi shape memory alloy (SMA) laminates with a macroscopic heterogeneous composition by explosive welding and investigate their microstructures and martensitic transformation behaviors. After explosive weld- ing, a perfect interfacial bonding between the two components and a reversible martensitic transformation are realized in the tandem. Results show achievement of a fine granular structure and the maximum value of microhardness near the welding interface because of the excessive cold plastic deformation and the high impact velocity during the explosive welding. Meanwhile, the effects of aging on the transformation of the welded tandem are investigated by differential scanning calorimeter (DSC) and subject to discussion. The trans- formation temperatures of NiTi/NiTi SMAs increase with the rise of the aging temperature. The experimental results indicate the shape memory properties of NiTi/NiTi SMA fabricated by explosive welding can be improved by optimizing the aging technology.     

TC21钛合金的微观组织对力学性能的影响

研究了两相钛合金TC21关于两种不同微观组织(片状组织和网篮组织)的拉伸性能、断裂韧性和疲劳裂纹扩展性能.结果显示:片状组织相比网篮组织有相近的拉伸强度,但塑性较差;两者的韧性相差不大,但增韧机理不同;网篮组织在中低速扩展区的扩展速率和片状组织几乎相同,但在较高速扩展区显示略低的扩展速率;加载方向对两种组织的疲劳裂纹扩展速率基本无影响;和其他钛合金类似,TC21在Paris区存在转折.     

腰形柱壳的有限条元解

本文用考虑了曲率影响的两结线低阶有限板条元分析了腰形柱壳的力学性能这种条元位移参数少,能较好地体现壳体的几何特性。     

串置双五分量天平的研制

本文介绍风洞应变天平中首次研制成功的一台串置双五分量天平。串置双天平由一块钢材制成。O_1天平固定在 O_2天平的受力端。O_2天平既能测量左平尾载荷,又能传递由 O_1天平测量的右平尾载荷。正确分析两台天平的受力传力路线和弹性变形的综合位移量,用严谨的数学公式描述两台天平测量的力和传递的力。对这两种力进行数学分解,形成数学模型,写出天平静校公式的数学表达式,并据此研制天平静校设备,分析天平在各分力作用下的弹性位移,写出弹性角公式。上述各点是串置双天平的核心问题。最后经风洞引导性实验证明,串置双天平的原理、方案、受力分析、静校公式等都是正确的。在国内外,串置双天平第一次用于风洞实验,获得了初步成功。     

一般硬化材料弹塑性旋转盘的变分解法

首先在小弹塑性范围内用应变的奇次四项式相当精确地拟合一般硬化材料的拉伸曲线;再在体积不变条件下用弹性位移场的已知模态和一待定幅值构成弹塑性位移场;最后用势能原理确定该幅值而得到封闭解。     

A novel surrogate modeling strategy of the mechanical properties of 3D braided composites

In this paper, a surrogate-based modeling methodology is developed and presented to predict the elastic properties of three dimensional (3D) four-directional braided composites. Using this approach, the prediction process becomes feasible with only a limited number of training points. The surrogate models constructed using Finite Element (FE) method and Diffuse Approximation, reduce the computational time and cost for preparing experimental samples. In the FE model, multiscale method is applied to couple the computations of elastic properties at microscale and mesoscale. Subsequently, a parametric study is performed to analyze the effects of the three design parameters on the elastic properties. Satisfactory results are obtained via the surrogate-based modeling predictions, which are compared with the experimental measurements. Moreover, the predictions obtained from surrogate models concur well with the FE predictions. This study orients a new direction for predicting the mechanical properties based on surrogate models which can effectively reduce the sample preparation cost and computational efforts.     

Effects of process parameters on mechanical properties of abrasive-assisted electroformed nickel

A cathode mandrel with translational and rotational motion, which was supposed to obtain uniform friction effect on surface, was employed in abrasive-assisted electroforming for revolving parts with complex profile. The effects of current density, translational speed and rotational speed on the deposit properties were studied by orthogonal test. The tensile strength, elongation and micro hardness value were measured to find out how the factors affected the properties. The optimized results show that changes of current density affect the tensile strength of nickel layer most, while translational speed has the most remarkable influences on both elonga-tion and micro hardness. The low rotational speed affects the properties least. In this experiment, a smooth nickel layer with tensile strength 581 MPa, elongation 17%and micro hardness 248HV is obtained by the orthogonal test.     

热处理对FeCo-2V-0.5Cr软磁合金力学与磁学性能的影响

针对FeCo-2V-0.5Cr软磁合金,研究了真空热处理时间对其微观组织结构、力学与磁学性能的影响规律,发现在800℃下热处理时间为2h左右时,合金的抗拉强度和延伸率达到最佳,同时仍保持良好的软磁性能,抗拉强度、延伸率以及矫顽力分别为867.8MPa、10.4%以及2.0Oe。进一步对该合金进行附加磁场下的真空热处理,重点研究了合金的交流损耗与矫顽力随附加磁场方式包括磁场撤除温度与磁场下保温时间的变化规律,发现适当的磁场热处理对合金相关力学性能影响不大,但由于合金中产生了单轴各向异性而使合金矫顽力进一步降至1.6Oe。     

热处理对砂型铸造Mg-Gd-Y合金微观组织和力学性能的影响

通过金相观察(OM)、扫描电镜(SEM)以及拉伸测试系统地表征和研究了热处理对砂型铸造Mg-Gd-Y合金微观组织和力学性能的影响。研究表明:固溶态GW94、GW74、GW44合金主要由α-Mg过饱和固溶体、铸态残留相Mg5(Gd,Y)以及固溶过程形成的方块相组成。随着Gd含量的增加,固溶态Mg-Gd-Y合金中方块相的体积分数不断增加;在同一时效温度下,合金达到时效峰值的时效时间缩短;室温下拉伸的固溶态、时效峰值态合金以及200和250℃下拉伸的时效峰值态合金的抗拉强度和屈服强度不断提高(固溶态合金屈服强度先降低后升高),但是伸长率却是不断降低。时效峰值态GW94合金表现出优越的力学性能,室温时其抗拉强度和屈服强度分别为300、247 MPa,而伸长率仅为0.9%;200和250℃拉伸时,时效峰值态GW94合金抗拉强度、屈服强度和伸长率分别为329、234 MPa和2.6%以及312、233 MPa和2.7%。时效峰值态GW94、GW74合金出现抗拉强度随温度升高而升高的反常力学行为。     

负游隙对高速高温薄壁圆柱滚子轴承动态性能的影响分析

计算了圆柱滚子轴承径向游隙为负值时的等效径向预紧载荷,并考虑等效径向预紧载荷下的套圈弹性变形,通过求解包含套圈弹性变形接触变形等效径向预紧载荷的非线性方程组,得到负游隙圆柱滚子轴承内部的载荷分布情况,以及负径向游隙带来的套圈周向应力.以此分析了负游隙对轴承承载性能及疲劳寿命的影响.结果表明:负径向游隙能够有效降低轴承打滑率,但同时也会降低轴承疲劳寿命,因此在负游隙设计时需同时考虑打滑率和轴承寿命,选择恰当的负游隙.