不同热处理工艺下激光增材制造TC4钛合金组织与性能研究进展

由于激光增材制造(Laser Additive Manufacturing,LAM)TC4钛合金加工成形过程的特殊性,导致该合金在力学性能上存在明显的各向异性,同时韧性、疲劳性能不能很好地满足使用要求。从材料组织与力学性能之间的关系出发,介绍了不同热处理工艺对激光增材制造TC4钛合金组织与力学性能的影响,指出了当前激光增材制造TC4钛合金热处理研究中存在的问题,并为后续激光增材制造TC4钛合金的热处理研究提供思路与方向。     

Synthesis and characterization of geopolymer from lunar regolith simulant based on natural volcanic scoria

In this study, a new GVS（Ground Volcanic Scoria） lunar regolith simulant was produced. The similarity between GVS and lunar soil was proved by comparison with Apollo lunar soil samples and other commercial lunar soil simulants. Then, GVS lunar regolith simulant was investigated as the source material for preparing geopolymer to produce building material for lunar colony construction. To study the possibility of preparing geopolymer from GVS lunar regolith simulant and the optimum activator formu...     

TC17钛合金焊接接头组织与力学性能分析

对TC17钛合金薄板采用氩弧焊和电子束焊两种焊接方法焊接,进行了拉伸试验,结合拉伸试验结果与断口形貌,对比分析了力学性能与焊接接头组织之间的联系。研究结果表明,TC17钛合金在经历TIG焊接热循环后,焊缝及靠近焊缝的热影响区晶粒粗化,电子束焊接头热影响区较窄且没有粗晶区形成;两种焊接试样抗拉强度均与母材等强;相对延伸率有所降低,主要是热影响区及焊缝的组织变化所致;氩弧焊焊缝组织较不均匀性更为显著。     

加热温度对TC4钛合金的空冷组织及热疲劳抗力的影响

对经不同温度加热随后空冷的ＴＣ４钛合金在－１９６～３５０℃范围内进行了外约束型热疲劳试验。结果表明：经单相区加热的合金，其热疲劳裂纹易于沿原β相晶界处萌生，以穿晶的方式扩展，对热疲劳裂纹萌生抗力较低。而经９５０℃加热的合金，其热疲劳裂纹易于沿初生α相与基体（条形的α＋β相）的界面处萌生，裂纹易于切过条形的α＋β相扩展，其热疲劳裂纹萌生抗力最高。经９００℃加热的合金，其热疲劳裂纹易于沿初生α相与基体的界面处萌生并沿其扩展，合金的热疲劳裂纹萌生抗力也较低     

稀土对GH4169激光微焊接接头组织性能的影响

通过添加稀土元素Ce对0.2mm厚的GH4169高温合金进行微激光对接焊接,利用光学显微镜、扫描电镜、电子精密拉伸仪测试等分析方法,对比研究稀土元素对焊缝表面成形、接头显微组织及力学性能的影响。结果表明：在添加稀土元素的条件下焊接时,对焊接工艺参数进行正交试验优化,得出焊接最优工艺参数为脉冲功率17%、脉冲频率4.0Hz、脉冲宽度3.1 ms,此时焊接接头断裂在母材。焊接过程中,液态金属流动使稀土在熔池中均匀混合,获得了组织均匀的焊缝。稀土元素能够改变焊缝温度梯度,形成“梯形”状焊缝;同时,稀土元素能够降低接头的显微硬度,增强接头的韧性和塑性。     

2219铝合金厚板TIG焊接头组织与力学性能研究

采用氦弧打底+氩弧填充、盖面的焊接工艺对2219-T87铝合金15 mm厚板进行TIG焊接试验,研究其焊缝成形和组织力学性能。结果表明,此工艺焊缝成形美观,无可见焊接缺陷,气孔抑制效果好,接头平均抗拉强度为278.22 MPa,平均断后延伸率为3.89%,接头平均强度系数达到58.94%。接头硬度整体表现为焊缝中心最低,从焊缝中心到母材呈现先增大后局部降低再增大的趋势;且焊缝中心填充层硬度高于打底层和盖面层。熔合区的微观组织为柱状树枝晶和胞状树枝晶,且垂直于熔合线生长,在靠近熔合区两侧出现了等轴细晶带。焊接接头断面有较多撕裂棱和韧窝,局部发现第二相粒子和微孔,其断裂机制为典型的韧性断裂。     

Joining of SiO2 ceramic and TC4 alloy by nanoparticles modified brazing filler metal

Nano-Al₂O₃ particles modified AgCuNi filler was adopted to braze the SiO₂ ceramic and TC4. The effects of filler size as well as the brazing temperature on the interfacial microstructure and mechanical property of the joints were investigated. Nanoscale filler reduced the phases dimension and promoted the homogeneous distribution of microstructure, obtaining a higher joint strength when compared to microscale filler. The increase of brazing temperature made the accelerating dissolution and diffusion of Ti, which promoted the increase of thickness of Ti₄O₇ + TiSi₂ layer adjacent to SiO₂ ceramic and diffusion layer zone nearby TC4 alloy. The hypoeutectic structure was produced in the brazing seam due to the high Ti content. The maximum shear strength of ∼40 MPa was obtained at 950 °C for 10 min.     

TiAl 与TC4 扩散焊接接头的组织与性能

主要对TiAl基金属间化合物与TC4的扩散连接技术进行了研究。通过对钛铝基合金进行热处理,获得了高温性能良好的全片层组织;通过对扩散连接后的接头进行组织结构、力学性能和断口的分析发现,在915℃/80 MPa/1 h的扩散连接条件下,TiAl基合金与TC4实现了冶金结合,在室温、400和500℃下,接头的抗拉强度分别达到了TiAl母材的91.77%、95.27%和99.21%。     

国产Hi-Nicalon型SiC纤维热处理后微观结构及性能演化

为考察国产Hi-Nicalon型SiC纤维在高温下的结构-性能演化规律,对国产Hi-Nicalon型SiC纤维分别在空气和氩气环境下进行了不同温度热处理,并对纤维的微观结构及纤维束丝力学性能演化进行了表征与测试。结果表明,在空气环境下,当超过1 100℃时,国产Hi-Nicalon型SiC纤维束丝强度开始下降,伴随着纤维表面生成SiO_2氧化膜,当温度超过1 200℃时,纤维表面会形成SiO_2氧化膜鼓泡。在氩气环境下1 100～1 500℃时,纤维束丝强度开始发生缓慢劣化。当热处理温度超过1 500℃时纤维束丝强度开始加速劣化,伴随着纤维开始发生β-SiC到α-SiC相变以及SiC晶粒尺寸增大。     

工艺制度对粉末TA15钛合金组织性能的影响

文摘研究不同保温时间和制粉方法对热等静压TA15钛合金的微观组织、拉伸性能和拉伸断口形貌的影响。结果表明:粉末TA15钛合金组织由等轴α-Ti、层状α-Ti和少量β-Ti组成。热等静压保温时间为20min时粉末TA15钛合金已达到致密,随着保温时间延长到120 min组织逐渐均匀长大。采用等离子旋转电极法的粉末TA15钛合金的拉伸性能优于惰性气体雾化粉末TA15钛合金。拉伸断裂模式为韧性断裂,断口微观形貌为韧窝。