SCR技术制备A2017半固态材料及其触变性能的研究

单辊搅拌技术 (SCRShearing/CoolingRollProcess)技术制备的A2 0 17半固态材料比常规铸造坯组织优良 ;SCR技术制备的A2 0 17半固态材料在 5 30～ 5 70℃范围内 ,可以进行触变成形 ;半固态成形平均屈服强度比热加工时的屈服强度低 10MPa ;A2 0 17半固态材料触变过程分为四个阶段 ,稳定触变阶段A2 0 17半固态材料的触变性能稳定 ,半固态加工时容许的最大加工变形范围为 6 4 %～ 72 %。     

LC9高强度铝合金过时效工艺试验

通过对ＬＣ９高强度铝合金过时效工艺试验，并与ＬＣ９ＣＳ状态作性能对比，证实该材料具有良好的耐应力腐蚀及抗裂纹扩展性能，从而确认ＬＣ９ＣＧＳ３铝合金在飞机上推广使用的可行性。     

基于FW-H方程的旋翼气动声学计算研究

由流体力学N S方程导出的非齐次波动方程———FfowcsWilliams Hawkings方程(简称FW H方程),可以精确地描述在静止流体中运动的物体与流体相互作用的发声问题。以FW H方程为理论模型,将旋翼桨叶运动发声问题等效为包含桨叶的任意运动控制面(声源面)的声辐射问题,并在旋翼绕流Euler方程数值模拟的基础上,在时域内计算了悬停旋翼和前飞旋翼的声场。应用于UH 1H和AH 1/OLS两种旋翼模型的气动声学计算表明:计算结果与噪声实验值符合良好;所研制的程序不仅能够较准确地计算单极子噪声和偶极子噪声,而且具有较强的跨音速四极子噪声预测能力。     

Deep Impact: Working Properties for the Target Nucleus – Comet 9P/Tempel 1

In 1998, Comet 9P/Tempel 1 was chosen as the target of the Deep Impact mission (A’Hearn, M. F., Belton, M. J. S., and Delamere, A., Space Sci. Rev., 2005) even though very little was known about its physical properties. Efforts were immediately begun to improve this situation by the Deep Impact Science Team leading to the founding of a worldwide observing campaign (Meech et al., Space Sci. Rev., 2005a). This campaign has already produced a great deal of information on the global properties of the comet’s nucleus (summarized in Table I) that is vital to the planning and the assessment of the chances of success at the impact and encounter. Since the mission was begun the successful encounters of the Deep Space 1 spacecraft at Comet 19P/Borrelly and the Stardust spacecraft at Comet 81P/Wild 2 have occurred yielding new information on the state of the nuclei of these two comets. This information, together with earlier results on the nucleus of comet 1P/Halley from the European Space Agency’s Giotto, the Soviet Vega mission, and various ground-based observational and theoretical studies, is used as a basis for conjectures on the morphological, geological, mechanical, and compositional properties of the surface and subsurface that Deep Impact may find at 9P/Tempel 1. We adopt the following working values (circa December 2004) for the nucleus parameters of prime importance to Deep Impact as follows: mean effective radius = 3.25± 0.2 km, shape – irregular triaxial ellipsoid with a/b = 3.2± 0.4 and overall dimensions of ∼14.4 × 4.4 × 4.4 km, principal axis rotation with period = 41.85± 0.1 hr, pole directions (RA, Dec, J2000) = 46± 10, 73± 10 deg (Pole 1) or 287± 14, 16.5± 10 deg (Pole 2) (the two poles are photometrically, but not geometrically, equivalent), Kron-Cousins (V-R) color = 0.56± 0.02, V-band geometric albedo = 0.04± 0.01, R-band geometric albedo = 0.05± 0.01, R-band H(1,1,0) = 14.441± 0.067, and mass ∼7×10¹³ kg assuming a bulk density of 500 kg m⁻³. As these are working values, {i.e.}, based on preliminary analyses, it is expected that adjustments to their values may be made before encounter as improved estimates become available through further analysis of the large database being made available by the Deep Impact observing campaign. Given the parameters listed above the impact will occur in an environment where the local gravity is estimated at 0.027–0.04 cm s⁻² and the escape velocity between 1.4 and 2 m s⁻¹. For both of the rotation poles found here, the Deep Impact spacecraft on approach to encounter will find the rotation axis close to the plane of the sky (aspect angles 82.2 and 69.7 deg. for pole 1 and 2, respectively). However, until the rotation period estimate is substantially improved, it will remain uncertain whether the impactor will collide with the broadside or the ends of the nucleus.     

钛合金表面镍包石墨喷涂层的耐磨性能

为了提高钛合金的表面耐磨性,利用氧乙炔热喷涂枪,在TC4合金表面上制备出镍包石墨涂层。采用MXP-2000型销盘式摩擦磨损实验机,进行钛合金及其镍包石墨涂层的干摩擦磨损实验,并利用扫描电镜对磨损表面进行观察和分析。实验结果发现,镍包石墨涂层的摩擦系数只有钛合金的一半左右,前者磨损量为后者的1/6,说明镍包石墨涂层可以大大提高钛合金的表面耐磨性能。TC4合金的磨损机制以黏着磨损为主,喷涂层的磨损机制以磨粒磨损为主,喷涂层中的石墨润滑相是其耐磨性高的主要原因。     

喷射沉积制备Al-Zn-Mg-Cu合金大型坯组织性能的研究

利用Ospray公司的喷射沉积设备制备了Al11.3Zn2.4Mg1.1Cu合金,合金挤压成棒材后,经过固溶和时效处理,用万能材料实验机对其进行了力学性能测试,合金的抗拉强度为849 MPa、屈服强度为796 MPa,延伸率为3.3%.透射电镜和扫描电镜对拉伸试样微观组织的研究结果表明,合金微观组织中包括微米级晶粒和纳米级晶粒,合金的强化方式为纳米晶强化、固溶强化以及沉淀强化,拉伸试样的断口分析表明,合金的断裂方式主要为沿晶断裂.     

芳纶纤维／环氧复合材料界面超声连续改性处理

运用超声技术在芳纶/环氧复合材料制备过程中对其界面进行改性处理,分析了超声处理过程中纤维与树脂之间浸润性的变化趋势以及超声作用对复合材料界面性能和力学性能的影响。结果表明:超声是通过改善纤维与树脂之间的浸润性,提高复合材料的界面性能及力学性能。     

基于BP人工神经网络的GPS／SINS组合导航算法

基于扩展Kalman滤波的GPS／SINS组合导航算法，需要对原始的非线性连续系统模型进行线性化和离散化处理，要求系统噪声和测量噪声为零均值的高斯白噪声，且易于出现滤波器发散。BP人工神经网络毋需对所求解的问题建模，能够很好地逼近系统非线性特性，获得较高精度的导航定位信息；还具有计算过程稳定，不涉及矩阵求逆，不需要迭代逼近，以及容易实现并行处理等优点。本文设计适用于GPS／SINS组合导航系统的BP网络模型，并在标准的BP算法基础上，采用共轭梯度法改进网络训练速度及精度。最后，通过仿真算例说明BP网络方法用于GPS／SINS组合导航计算的可行性。     

粉末冶金γ-TiAl基合金研究的最新进展

γ TiAl基合金是一种具有发展前途的新一代高温结构材料。首先综述了γ TiAl基合金的性能特点和应用前景 ,并简单介绍了该合金的最新基础研究情况。随后介绍了采用粉末冶金方法制备γ TiAl基合金的基本工艺、力学性能 ,最后结合γ TiAl基合金排气阀和板材的研制论述了粉末冶金在γ TiAl基合金制备及近净成形方面的优势和发展前景     

LY16—1铝合金铆钉线材性能研究

探讨了热处理制度对ＬＹ６－１新型铝合金线材剪切、铆接性能的影响，并对Ｌｙ１６－１与Ｌｙ１０合金线材高温剪切性能及抗蚀性能进行了比较。