铝合金锻件重复淬火保温时间对组织性能的影响

分析了铝合金锻件重复淬火保温时间的长短及其组织性能的影响情况。根据大量的试验数据,证实了重复淬火保温时间及时效保温时间的长短对锻件性能的直接影响,并以此确定了合理的工艺参数。     

钛合金熔模精铸氧化锆陶瓷型壳／金属界面反应研究

通过实际浇注和真空扩散连接分别制取了钛／型壳界面,借助ＳＥＭ、ＥＰＭＡ和显微硬度仪等分析测试手段对所得界面进行了深入研究,初步提出了以Ｚｒ、Ｏ元素向钛基体内的扩散为主导的界面反应机制。实验结果表明,界面反应并非在整个界面上均衡推进,而是在浓度、温度、能量起伏、以及陶瓷颗粒位向适宜的区域优先发生界面反应     

钛合金精密铸造技术

本文就钛合金精密铸造中所用的耐火材料及粘结剂做了简要叙述,例举了一些典型的精铸工艺,并介绍了国内外钛合金熔模精铸的最新成果。     

Fatigue crack propagation of new aluminum lithium alloy bonded with titanium alloy strap

A new type of aluminum lithium alloy (Al-Li alloy) Al-Li-S-4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti-6Al-4V alloy (Ti alloy) strap by FM 94 film adhesive after the surface was treated. Fatigue crack growth of samples was investigated under cyclic loading with stress ratio (R) of 0.1 and load amplitude constant. The results show that Al-Li alloy plate bonded with Ti alloy strap could retard fatigue crack propagation. Retardation effect is related with width and thickness of strap. Flaws have an observable effect on crack propagation direction.     

7075铝合金在超塑处理和拉伸过程中的显微组织变化

 研究了 70 75铝合金在超塑性预处理和拉伸过程。结果表明 ,合金经过固溶处理炉冷→轧制预处理后 ,形成 1～ 2 μm的胞块组织。在超塑拉伸过程中胞块发生回复和再结晶 ,形成细晶组织 ,使合金获得优异的超塑性性能     

国外航天材料的新进展

航天技术发展推着航天材料的进步，本文简略介绍了国外航天材料，重点是高性能Ａｌ－＝Ｌｉ合金和先进复合材料的新进展。     

离心铸造Al—20wt%Si合金自生表面复合材料的组织与性能

采用热模金属型离心铸造Al－20wt％Si合金，获得了外层聚集粗大初晶Si、中层为共晶组织、内层聚集细小初晶Si的自生三层表面复合材料。考察了复合材料的组织形貌，检测了复合材料的硬度和耐性，分析了复合材料的断裂模式。     

快速凝固Al88Ce2Ni7Fe3非晶铝合金初生型晶化的研究

用X光衍射和透射电镜研究证实快速凝固Al88sCe2Ni7Fe3非晶铝合金晶化过程中的初期阶段为初生型晶化。初生相α－Al的结晶体积分数和纳米晶体尺寸随退火温度的升高表现出非同步增长行为：前者逐渐增加而后者变化不明显。不同退火态样品的小角X光散射结果表明，非晶基体中不断析出的纳米晶α－Al粒子，由开始的低温稀疏分布转向高温密集分布。根据实验结果，分析和讨论初生相α－Al的体积分数、晶粒数目、粒子尺寸及粒子分布在初生型晶化过程中的变化规律，为纳米晶α－Al粒子强化非晶基体提供了清晰的物理图像。     

Stress corrosion behavior of 2195-T8 Al-Li alloy with an artificial pit exposed to a 30vol% HNO3 solution

This paper experimentally studied the stress corrosion behavior of 2195-T8 Al-Li alloys with prefabricated pits in 30vol% HNO₃. The microstructure was observed and determined by the scanning electron microscopy and the transmission electron microscopy. The typical corrosion features, i.e., regular or irregular corrosion pits and sub/intergranular corrosion, were investigated, and the role of stress were analyzed. The statistical results of the number and area of corrosion pits in various sizes were studied using an improved image processing method. Experimental results demonstrate that stress affects the intergranular corrosion or sub-intergranular corrosion of the alloy most, and promotes them to evolve into cracks under stress corrosion. Stress also plays a role in accelerating corrosion severity of certain corrosion feature. The number of corrosion pits with an area of 0–50 μm² can be seen as an index to reflect the degree of corrosion. Besides, a corrosion phenomenon, i.e., the pit bottom in the site with the maximum stress locally suffering from no severe corrosion, was observed and discussed.     

俄国Al—Mg—Li系1420合金的焊接裂纹和气孔

论述了Ａｌ－Ｍｇ－Ｌｉ系１４２０合金焊接时的主要缺陷（裂纹和气孔）的形成机理,针对这两种缺陷提出了减少和消除裂纹和气孔的有效方法。