6082铝合金双轴肩搅拌摩擦焊试板温度场研究

采用热电偶测温技术系统测定了6mm6082铝合金双轴肩搅拌摩擦焊试板各特征点的温度变化曲线,分析了双轴肩搅拌摩擦焊过程中焊接试板不同区域的温度场分布特征。双轴肩搅拌摩擦焊搅拌头上、下轴肩同时产热,比传统搅拌摩擦焊产热量大,且热输入方式及试板接触散热条件也有很大不同,因此,其稳定焊接速度较大,从而导致双轴肩搅拌摩擦焊试板温度场分布特征与传统搅拌摩擦焊明显不同。双轴肩搅拌摩擦焊过程分为加速焊接和稳定焊接两个阶段,起始阶段,随着焊接速度的增加,靠近起始端测温点的温度逐渐升高,而远离起始端各测温点的温度升温则非常缓慢,当焊接速度达到较高的稳定焊接速度,搅拌头接近后续各测温点时,其温度值瞬间急剧升高,然后随着搅拌头的远离,温度值逐渐下降。不同区域测温点温度测试结果显示,靠近下轴肩试板测温点的温度高于靠近上轴肩试板、后退侧的温度明显高于前进侧;与单轴肩搅拌摩擦焊接试板相同,距离焊缝越近的位置温度上升和下降的越剧烈,峰值温度越高;焊接速度提高,各测温点的峰值温度依次降低,随着测温点远离焊缝中心,焊接速度对其温度分布的影响作用逐渐减弱。     

基于库伦摩擦效应的箔片轴承极限承载力理论与试验

基于有限单元法建立了考虑库伦摩擦的波箔型径向气体箔片轴承的箔片结构模型,采用有限差分法和有限单元法耦合求解Reynolds方程和气膜厚度方程,通过求解轴颈达到极限偏心率时的轴承极限承载力,研究了箔片结构库伦摩擦效应对轴承极限承载力的影响规律,并搭建了轴承极限承载力测试试验台,利用温度法测量了两个具有不同轴承壳内表面粗糙度的波箔型径向气体箔片轴承的轴承极限承载力.通过对比分析仿真结果与试验结果表明:轴承壳圆柱孔内表面粗糙度为0.4μm的轴承在10000r/min和20000r/min下,轴承极限承载力分别为15.5N和42.3N;而表面粗糙度为1.6μm的轴承极限承载力为10.9N和29.6N,这是由于波纹箔片和轴承壳体之间的库伦摩擦力增大了波纹箔片的刚度,因此增大箔片结构摩擦因数使得轴承极限承载力降低,并且仿真结果变化趋势和试验结果变化趋势吻合.      

同心筒式发射装置附加弹射力影响因素分析

采用同心筒式发射装置发射导弹时,弹底会受到附加弹射力的作用,其值主要取决于排气狭缝宽度、增力装置、导流锥等因素.利用动量方程积分形式推导出附加弹射力的理论公式,分析各种因素对附加弹射力的影响,并利用数值模拟技术进行验证.结果表明:筒底所承受冲击力与弹底所受的附加弹射力呈正相关;减小内外筒间缝隙可提高弹底所受的附加弹射力;加导流锥能降低筒底所受的冲击力.导流锥母线越光滑,筒底所受到的冲击力就越小;增加导流锥后,燃气流动达到稳定状态的时间与无导流锥时所需的时间近似于相等.      

TC4-DT钛合金磨削表面特性及其摩擦磨损性能

钛合金是一种典型难磨削加工材料,磨削表面易出现烧伤、裂纹等热损伤。本文开展了TC4-DT钛合金磨削实验,通过扫描电镜（SEM）、能谱（EDS）、X射线衍射（XRD）、显微硬度仪、金相显微镜及球-盘摩擦磨损实验仪研究了其表面特性及摩擦磨损性能。结果表明：低速磨削表面质量好,摩擦磨损性能较基体略提高;当砂轮线速度为80 m/s时,磨削表面质量良好,摩擦系数为0.38,较基体降低40%;而砂轮线速度为100 m/s时,磨削表面出现严重烧伤、网状裂纹。因此选择合理的高速磨削工艺可避免烧伤、裂纹等热损伤缺陷,并可有效改善表面摩擦磨损性能;磨削表面干摩擦磨损机制为磨粒磨损、粘着磨损和剥层磨损。     

Friction moment analysis of space gyroscope bearing with ribbon cage under ultra-low oscillatory motion

This paper presents the model of calculating the total friction moment of space gyroscope ball bearings which usually work under ultra-low oscillatory motion and are very sensitive to the friction moment. The aim is to know the proportion of the friction moment caused by each frictional source in the bearing＇s total friction moment, which is helpful to optimize the bearing design to deduce the friction moment. In the model, the cage dynamic equations considering six degree-of-freedom and the balls dynamic equations considering two degree-of-freedom were solved.The good trends with different loads between the measured friction moments and computational results prove that the model under constant rate was validated. The computational results show that when the speed was set at 5 r/min, the bearing＇s maximum total friction moment when oscillation occurred was obviously larger than that occurred at a constant rate. At the onset of each oscillatory motion, the proportion of the friction moment caused by cage in the bearing＇s total friction moment was very high, and it increased with the increasing speed. The analyses of different cage thicknesses and different clearances between cage pocket and ball show that smaller thickness and clearance were preferred.     

中介机匣典型故障排除及深度修理

航空发动机中介机匣组件因各种故障而需修理或导致报废的现象时有发生。针对发动机中介机匣分流环裂纹掉块、上部衬套磨损松动、弹性环磨损、同心度检测不合格等故障进行分析研究,提出解决措施,制定满足发动机使用要求的合理技术标准和修理方法。在修理技术方法中,采用挖补补焊方法解决分流环裂纹掉块故障;采用极坐标定位与专用模板衬套相结合的方法提高新品衬套加工精度以解决上部衬套更换新品后装配准确性难题;采用装配过盈销钉和扩口工艺以保证零件的堵孔质量等。结果表明:这些修理措施提高了中介机匣零部件的利用率,延长了其使用寿命,降低了发动机修理成本。     

转动微动磨损条件下7075铝合金的局部疲劳行为研究

在新型转动微动磨损试验机上,进行了7075铝合金与GCr15钢球配副在不同角位移幅值下的转动微动磨损实验。在磨痕表面形貌及剖面微观分析的基础上,研究了转动微动磨损的局部疲劳裂纹萌生和扩展行为。结果表明:转动微动磨损条件下疲劳裂纹主要分布于混合区,大量的裂纹向基体内部扩展,混合区材料的失效形式主要表现为裂纹的萌生和扩展,并伴随因疲劳磨损所致的片状剥落;在部分滑移区,疲劳裂纹萌生后平行于表面方向扩展,微动损伤主要表现为材料的轻微剥落;在滑移区,在局部接触疲劳和磨损的竞争过程中,疲劳效应减弱且材料磨损占支配地位。此外,疲劳裂纹的形成与转动微动的中心隆起有密切关系。     

双金属铆钉特点及安装工艺技术

双金属铆钉是一种铆接过程中钉杆不变形的新型铆钉,适用于复合材料等结构的连接。铆钉既具有较高的抗剪性能,又具有良好的铆接性能,还具有重量轻、成本低、装配简单等特点,已经在航空航天等部门获得了应用。结合国内外双金属铆钉的发展状况,简单阐述其性能与结构特点,并简要介绍其安装工艺技术。     

离子注入抑制摩擦温升的研究

 离子注入抑制摩擦表面的温升,是减少粘着磨损、提高摩擦副耐磨性的新途径。本文采用离子注入技术抑制航空柱塞泵配流副试件摩擦表面的温升,获得显著的效果。当逐级改变负载时,离子注入试件摩擦表面的温度平均下降３５℃；当逐级改变润滑油流率时,试件表面温度平均下降４６℃。并初步探讨了离子注入抑制摩擦温升的机理。     

形状记忆合金切削加工性试验研究

通过切削试验认为，ＮｉＴｉ基记忆合金切削加工性差主要是因为切削温度高、刀具易磨损，故宜选用Ｋ类硬质合金作刀具材料，且存在最佳切削速度。