The microstructure of rain has been studied with observations using a vertical looking Micro Rain Radar (MRR) at Ahmedabad (23.06°N, 72.62°E), a tropical location in the Indian region. The rain height, derived from the bright band signature of melting layer of radar reflectivity profile, is found to be variable between the heights 4600 m and 5200 m. The change in the nature of rain, classified on the basis of radar reflectivity, is also observed through the MRR. It has been found that there are three types of rain, namely, convective, mixed and stratiform rain, prevailing with different vertical rain microstructures, such as, Drop Size Distribution (DSD), mean drop size, rain rate, liquid water content and average fall speed of the drops at different heights. It is observed that the vertical DSD profile is more inhomogeneous for mixed and stratiform type rain than for convective type rain. It is also found that the large number of drops of size <0.5 mm is present in convective rain whereas in stratiform rain, drops concentration is appreciable up to 1 mm. A comparison of measurements taken by ground based Disdrometer and that from the 200 m level obtained from MRR shows good agreement for rain rate and DSD at smaller rain rate values. The results may be useful for understanding rain structures over this region.     

纳米TiC粉末改性钎料钎焊CBN磨粒的结合界面和磨损特性

采用了Ag-Cu-Ti 合金和纳米 TiC 粉末组成的新型复合钎料钎焊立方氮化硼(CBN)磨粒和工具基体,运用了三维体式显微镜和扫描电镜,研究了CBN磨粒与改性钎料之间的结合体系,包括界面微结构和反应产物,并进行了钎焊磨粒耐磨性试验.试验结果表明:加入的纳米TiC粉末均匀分布在钎料层内,细化了Ag-Cu-Ti合金钎料层的显微组织,有效控制了CBN磨粒与钎料的剧烈反应;磨粒表面化合物均匀致密,确保了CBN磨粒、纳米改性钎料和基体之间的结合强度;钎焊CBN磨粒的磨损形式以磨耗磨损为主,后期出现微小破碎,无磨粒脱落.     

Ti-6Al-4V钛合金激光弯曲成形微观组织研究

以1mm厚Ti-6Al-4V合金薄板为对象,运用光学金相显微镜、电子探针、扫描电子显微镜、氮氢氧联合分析仪、显微维氏硬度计,研究了特定累积线能量下90°弯曲角弯折区显微组织。结果表明,弯折区组织与累积线能量输入有关,当累积线能量在适当范围时,材料堆积增厚,极表层出现轻微复熔铸态组织,上层为板条马氏体α′,中层为针状马氏体α′,底层为长大粗化的(α+β)组织;距表层约0.2mm范围吸收间隙元素强烈致使硬度急剧提高并呈明显梯度;累积线能量输入过大,弯折区出现大面积复熔铸态组织并伴有裂纹产生。     

新型Co基合金Co-9Al-(9-x) W-xMo-2Ta-0.02B的显微组织与高低温力学性能

以新型Co基合金Co-9Al-9W-2Ta-0.02B成分为基础,分别添加了原子分数为2％、4％、6％、9％的Mo元素替代W（分别称2Mo、4Mo、6Mo、9Mo合金,W+Mo的原子分数为9％,无Mo添加的称为0Mo合金）,研究了Mo元素对合金相组成、显微组织形貌、维氏硬度和高低温压缩强度的影响.结果表明铸态合金由Co...     

Ag和稀土Y复合添加对金属间化合物NiAl显微组织的影响

研究了Ag和Y的复合添加对金属间化合物NiAI显微组织的影响。利用非自耗电弧炉制备了三种不同Y和Ag含量（1．0,5．0,10．0质量分数％）的NiAJ合金,其中一组试样进行了高温固溶和时效处理。实验结果表明,随着Y和Ag含量的增加,铸态下的NiAI合金晶粒呈逐渐细化的趋势,并且柱状晶生长方式逐渐演变为典型的糊状凝固方式。EDS和XRD分析表明,晶界处有富Ag、Y相形成;固溶时效后的NiAl合金组织则演变为粗大的等轴晶粒,Y和Ag元素仍然在晶界处偏聚。     

IC10高温合金的微观组织

研究了IC10高温合金的微观组织。研究表明:铸态组织包括γ′和γ,′以及γ γ′共晶相和MC碳化物,其中γ′体积百分数为64%,碳化物相主要是TaC和H fC,碳化物呈骨架状和点状、块状分布,共晶相多为葵花状。热处理后有残留的γ γ′共晶相,碳化物分解并有γ′包覆,γ′相发生球化,晶界上MC分解,并有H fC析出。IC10合金经950℃,3000h长期时效后组织保持稳定,未析出有害的TCP相;长期时效的组织变化表现为γ′的长大和条状化;枝晶间二次析出细小的富H f的MC相;晶界上析出少量的M6C和M23C6。     

Phase Transformation and Microstructure of Ti50Ni48-xFe2Ndx Shape Memory Alloys

The influences of rare earth element Nd on the phase transformation and the microstructure of Ti₅₀Ni_48−xFe₂Nd_x shape memory alloys are investigated by means of electrical resistivity, optical microscopy, electron probe microanalyzer, and X-ray diffraction. The results show that TiNiFe alloys with different Nd contents exhibit two-step martensitic transformation. The start temperature of martensitic transformation increases sharply from 212 K to 267 K when 0.1 at.% Nd is added in, and then decreases gradually if Nd content further increases. The microstructure of TiNiFeNd quaternary alloys consists of TiNi matrix, Ti₂Ni second phase, and Nd₃Ni intermetallic compound. The spherical Nd₃Ni precipitate-particles evenly disperse in the matrix.     

FGH95粉末镍基合金热处理后的微观组织与蠕变性能

通过进行蠕变曲线测定和组织形貌观察,研究了FGH95粉末镍基合金的微观组织结构与蠕变行为。结果表明：合金经高温固溶、盐浴冷却处理后,组织结构是由细小的γ’相弥散分布在γ基体所组成,其细小（Nb,Ti）C碳化物在晶内及沿晶界不连续析出。在试验的温度和施加应力范围内,合金表现出明显的施加温度敏感性,并测算出合金在稳态蠕变期间的蠕变激活能和应力指数分别为Q=542．07kJ／mol和n=14．8。合金在蠕变期间的变形特征是孪晶和位错在晶内发生双取向滑移,其切入γ’相内的〈110〉超位错可分解形成（1／3）〈112〉超肖克莱不全位错＋层错的位错组态,发生孪晶变形的孪晶面为（111）晶面。晶界及沿晶界不连续析出的细小（Nb,Ti）C型碳化物可有效阻碍位错运动,是使合金具有较高抗蠕变能力的主要原因。     

AZ31B变形镁合金激光-MIG复合焊焊接组织和性能分析

采用激光-MIC复合焊对10mm厚的AZ31B变形镁合金进行焊接.利用光学显微镜、扫描电镜、X射线衍射仪等手段分析了焊接接头的外观和截面特征、显微组织、元素分布、焊缝物相和断口形貌等,并检测了接头区域硬度和接头强度.试验结果表明:采用激光-MIG复合焊能获得成形美观的焊缝,无明显的缺陷;焊缝热影响最大宽度位于激光区,约为100μm,焊缝组织为15～25μm的等轴晶粒;相比于母材,焊缝区的镁元素出现烧损,铝和锰元素的比例有一定增加;焊缝区主要为Mg,Al和少量的MgO相.焊接接头硬度值较均匀;焊缝抗拉强度达到222MPa,断口形貌为混合断裂断口.     

喷射成形高速钢沉积坯性能分析

研究了喷射成形高速钢T15沉积坯的部分力学性能及微观组织.结果表明,喷射成形制备的高速钢,晶粒细小,无宏观偏析,平均体密度为8.208g/cm3,三点抗弯强度达到1860 MPa.但通过SEM观察发现沉积坯内存在局部显微疏松,为了进一步提高材料性能,需要对高速钢沉积坯做热等静压等后续热加工.