新型Co基合金Co-9Al-(9-x) W-xMo-2Ta-0.02B的显微组织与高低温力学性能

以新型Co基合金Co-9Al-9W-2Ta-0.02B成分为基础,分别添加了原子分数为2％、4％、6％、9％的Mo元素替代W（分别称2Mo、4Mo、6Mo、9Mo合金,W+Mo的原子分数为9％,无Mo添加的称为0Mo合金）,研究了Mo元素对合金相组成、显微组织形貌、维氏硬度和高低温压缩强度的影响.结果表明铸态合金由Co...     

淬火／回火热处理对TiAl基合金晶粒细化的影响

研究了淬火/回火热处理中淬火温度和回火时间对Ti-48Al-2Cr-0.5Mo合金晶粒细化的影响。研究表明:一定的淬火/回火热处理能将大小约为1000μm的铸态组织细化成为18～30μm的均匀双态组织;TiAl基合金的细化效果严重依赖淬火阶段的加热温度,温度升高,得到的块状组织较细,羽毛状组织体积分数减少,在两相区回火时,高温淬火组织的回火组织较细,而时间的延长,晶粒长大,但不明显。     

钛合金TB6铣削加工硬化实验

研究了使用涂层硬质合金刀具对钛合金TB6进行端铣加工时,铣削参数以及刀具后刀面磨损量对加工硬化（表面硬化率、硬化层深度以及硬化层硬度分布）的影响,以弄清TB6铣削硬化现象及机理.结果表明,在实验参数范围内,刀具无磨损的情况下,硬化率基本保持在107%~112%范围内,硬化层深度范围为18~36 μm;铣削速度增加时,加工硬化程度会有较为明显的降低现象,而进给量与切深对加工硬化的影响并不明显;刀具磨损对加工硬化的影响较为显著,后刀面磨损量低于0.2 mm时,硬化层深度随着磨损增加从30 μm增加至55 μm,而后刀面磨损量为0.35 mm时,硬化层深度达到了130 μm.刀具磨损后在加工表面下较浅位置出现软化区域,而且随着磨损量的增加,软化越来越明显.      

碳纤维增强聚四氟乙烯材料微观结构

为了研究碳纤维增强聚四氟乙烯材料的最佳加工工艺,采用扫描电镜对碳纤维增强聚四氟乙烯材料的微观结构形貌进行了观察,并对碳纤维增强聚四氟乙烯材料的结晶形态和成型后毛坯的内部微观缺陷进行了对比研究和分析。研究表明:碳纤维增强聚四氟乙烯毛坯表面存在"球状结晶",无缺陷的毛坯内部不会产生"球状结晶";碳纤维增强聚四氟乙烯毛坯内部的气孔、分层缺陷在冷压过程中形成。减少碳纤维增强聚四氟乙烯粉料的团聚,能有效减少成型后毛坯内部气孔缺陷的产生;碳纤维增强聚四氟乙烯材料冷压时适当降低压制压力,能有效减少分层缺陷的产生。     

Investigation of vertical profile of rain microstructure at Ahmedabad in Indian tropical region

The microstructure of rain has been studied with observations using a vertical looking Micro Rain Radar (MRR) at Ahmedabad (23.06°N, 72.62°E), a tropical location in the Indian region. The rain height, derived from the bright band signature of melting layer of radar reflectivity profile, is found to be variable between the heights 4600 m and 5200 m. The change in the nature of rain, classified on the basis of radar reflectivity, is also observed through the MRR. It has been found that there are three types of rain, namely, convective, mixed and stratiform rain, prevailing with different vertical rain microstructures, such as, Drop Size Distribution (DSD), mean drop size, rain rate, liquid water content and average fall speed of the drops at different heights. It is observed that the vertical DSD profile is more inhomogeneous for mixed and stratiform type rain than for convective type rain. It is also found that the large number of drops of size <0.5 mm is present in convective rain whereas in stratiform rain, drops concentration is appreciable up to 1 mm. A comparison of measurements taken by ground based Disdrometer and that from the 200 m level obtained from MRR shows good agreement for rain rate and DSD at smaller rain rate values. The results may be useful for understanding rain structures over this region.     

喷射沉积过程中显微组织的形成机制

通过对沉积还纵剖面的组织分析，发现沉积坯在进缘、上下表面及中心部位的显微组织明显不同。边缘及上下表面区试样的退火试验研究表明，细小的枝晶碎块在高温退火过程中发生凝共和粗化，并导致近球状晶粒组织的形成。试验确定其生长服从：D2-D02=6.37×1020e(-70036.1/T)·τ，晶界迁移激活能Qg=582KJ／mol。并依赖于两种机制：（1）在喷射沉积过程中无强烈变形枝晶的均匀化；（2）变形及断裂枝晶的生长和粗化。     

改进DZ—22定向凝固高温合金热处理制度的研究

研究了一种新的热处理制度对DZ－22走向凝固高温合金组织和性能的影响。结果表明，采用新热处理制度先进行预处理，可以消除低熔点相，提高合金的初熔温度，然后提高合金的固溶温度。在随后的冷却和时效过程中，析出更多的细小γ'相使合金的拉伸强度和持久性能得到明显提高。     

TC18钛合金普通退火工艺研究

研究了普通退火工艺参数对TC18（Ti-5A1-5Mo-5V-1Cr-1Fe）钛合金显微组织和力学性能的影响。结果表明,合金强度随退火温度升高先降低后上升,900％及以上温度退火后合金强度可达到1100MPa以上。a相形状、数量及尺寸等方面的变化是影响合金强度和塑性的关键因素。