转速对20 mm厚2219铝合金搅拌摩擦焊接件的组织及性能的影响

对20 mm厚的2219 C10S铝合金板材进行搅拌摩擦焊对接试验,在进给速度为100 mm/min的条件下,对比研究转速为400～550 r/min时的对接接头的内部缺陷、宏观形貌及微观组织、显微硬度和拉伸力学性能的差异。结果表明,当转速为400～500 r/min时,焊接接头无缺陷,能获得内部质量较高的焊接接头。随着转速的增加,焊核区“洋葱环”的间距和轴肩影响区的范围增大,焊核区和热力影响区的硬度的降低越明显。接头的拉伸性能随转速的增大而降低,拉伸强度最高可达到334 MPa,接头断裂模式主要为韧性断裂,断裂位置发生在后退侧的热力影响区与热影响区的交界处,与显微硬度最小位置相吻合。当转速增大至525 r/min时,焊缝出现表面点状缺陷;当转速达到550 r/min时,焊缝出现连续的犁沟缺陷。     

软土地区水平定向钻施工对周围环境的影响

通过水平定向钻在市政工程中的广泛应用,水平定向钻施工越来越显示出它的优势,其施工对周围环境的影响需要评估。为此,对水平定向钻小直径管道施工过程引起的力学效应进行了讨论,重点探讨了拉力、扭矩和泥浆的影响,同时通过分析沉降位移监测值,就具体施工过程所带来的影响进行了讨论,得出了有益的结论。     

铝合金与不锈钢的连接技术

阐述了钎焊、摩擦焊技术在铝合金与不锈钢连接中的应用情况.此外,介绍了液相扩散连接、爆炸焊、超声波焊、表面活化连接等新型连接技术.     

焊透深度和前进侧位置对FSW 贮箱锁底接头性能的影响

开展了2219MCS 叉形环和2219C10S 短壳组成的锁底接头的搅拌摩擦焊工艺试验,详细分析了

搅拌针长度和前进侧位置对锁底接头Hook 型缺陷、力学性能、断裂方式的影响规律。结果表明:搅拌摩擦焊

锁底接头在短壳一侧存在Hook 型缺陷,短壳位于前进侧时的搭接界面上翘曲率和迁移量均大于叉形环位于

前进侧,且随着搅拌针长度的增加,搭接界面的向上迁移量逐渐增大。相同的焊透深度时,叉形环位于前进侧

的力学性能优于短壳位于前进侧;相同的前进侧位置时,随着焊透深度的逐渐增加,接头力学性能逐渐降低。

锁底接头搭接界面缺陷形貌及迁移量的变化是引起力学性能变化的主要原因。优化的试验结果显示,当焊透

深度和短壳板材厚度相同,且叉形环位于焊缝前进侧的力学性能最优,常温可达到300 MPa,低温可达到370

MPa,延伸率均超过3. 5%。锁底接头的拉伸断裂方式与焊缝前进侧位置密切相关。当短壳位于前进侧时,从

短壳一侧热力影响区断裂;当叉形环为前进侧时,从焊缝焊核区断裂。

     

空间用9Cr18 钢PIII 复合离子注入表面改性工艺研究

采用等离子体浸没离子注人(PⅢ)技术对9Cr18轴承钢表面进行了双注入及共注入Ti+N工艺处理.测试了处理前后试样的显微硬度及真空摩擦因数,并表征分析了表面磨损形貌.结果表明:处理后试样的显微硬度都有大幅提高,最大增幅达68.7％；表面真空摩擦因数由0.15下降到0.08；磨斑尺寸及粗糙度分别减少了54.4％和37.4％.双注入与共注入方式在相同参数下,双注入处理后的试样表面综合性能更加优异.     

离轨帆弹性桅杆力学性能分析

采用有限元分析软件ABAQUS分析弹性桅杆几何参数对其力学性能的影响,为离轨帆弹性桅杆设计提供一定的理论依据。结果表明:增加壳体厚度、保持弧长不变,减小曲率半径以及增大壳体截面圆心角都能有效提高离轨帆自动展开能力及弹性桅杆支撑刚度;弹性桅杆的弯曲内部应力只与材料属性、曲率半径、缠绕半径以及壳体厚度有关;曲率半径减小、壳体厚度增加都会增大弹性桅杆的弯曲内部应力,有可能会导致弹性桅杆在缠绕时发生塑性变形。因此,在对弹性桅杆设计时,需综合考虑弹性桅杆几何参数对其展开能力以及缠绕性能的影响。     

Improving tensile-shear properties of friction stir lap welded dissimilar Al/Mg joints by eliminating hook defect and controlling interfacial reaction

To improve tensile-shear properties of fiction stir lap welded(FSLW) dissimilar Al/Mg joints, pin-tip profiles were innovatively designed and welding speed was optimized, and effects of them on formation, interface microstructure and mechanical properties of different FSLW joints were investigated. With increasing the welding speed, the tensile-shear load of FSLW joints produced by three pins presents an increasing firstly and then decreasing trend. Compared with Rpin, the hook and hole defect i...     

Microstructural formation and mechanical performance of friction stir double-riveting welded Al-Cu joints

A novel friction stir double-riveting welding (FSDRW) technology was proposed in order to realize the high-quality joining of upper aluminum (Al) and lower copper (Cu) plates, and this technology employed a Cu column as a rivet and a specially designed welding tool with a large concave-angle shoulder. The formations, interfacial characteristics, mechanical properties and fracture features of Al/Cu FSDRW joints under different rotational velocities and dwell times were investigated. The results showed that the well-formed FSDRW joint was successfully obtained. The cylindrical Cu column was transformed into a double riveting heads structure with a Cu anchor at the top and an Al anchor at the bottom, thereby providing an excellent mechanical interlocking. The defect-free Cu/Cu interface was formed at the lap interface due to the sufficient metallurgical bonding between the Cu column and the Cu plate, thereby effectively inhibiting the propagation of crack from the intermetallic compound layer at the lap interface between the Al and Cu plates. The tensile shear load of joint was increased first and then decreased when the rotational velocity and dwell time of welding tool increased, and the maximum value was 5.52 kN. The FSDRW joint presented a mixed mode of ductile and brittle fractures.     

敏捷SAR卫星平台载荷一体化控制方法研究

面向具备波束指向捷变能力的小型化敏捷合成孔径雷达(SAR)卫星成像需求,提出了通过平台姿态敏捷机动和载荷波束捷变扫描一体化控制实现条带成像、多条带拼接成像、滑动聚束成像等传统成像模式的方法。针对配合成像过程提出的大角度机动和高精度高稳定度连续指向跟踪控制要求,采用5个单框架控制力矩陀螺(SGCMG)组成的"五面锥"构形控制力矩陀螺群作为执行机构,设计了基于姿态四元数和角速度反馈的改进型递阶饱和控制器,实现了平台的敏捷机动和对目标的稳定跟踪指向。数学仿真结果表明:该控制系统有效可行。     

基于机器视觉的搅拌摩擦焊缝装配质量评测方法

搅拌摩擦焊常采用无坡口焊缝,焊缝装配质量对搅拌摩擦焊装配质量影响较大,通过焊缝的特征,可以对搅拌摩擦焊缝的装配质量进行评判。线结构光是提取焊缝特征的常用手段,基于结构光传感器扫描获得的焊缝轮廓信息多通过离散的点进行表示,如何高效地从轮廓点中提取焊缝轮廓信息,是焊缝特征识别的新挑战。本文提出一种基于机器视觉的焊缝装配质量评测方法,将离散的轮廓点转换为位图,通过抗锯齿算法提高轮廓直线特征的识别可靠性,并计算对应焊缝的装配质量信息,进而实现对整条焊缝的装配质量的量化评价。与传统的离散点拟合方法相比,本方法具有较为明显的效率优势。