For high-efficiency grinding of difficult-to-cut materials such as titanium and nickel alloys, a high porosity is expected and also a sufficient mechanical strength to satisfy the function.However, the porosity increase is a disadvantage to the mechanical strength. As a promising pore forming agent, alumina bubbles are firstly induced into the abrasive layer to fabricate porous cubic boron nitride（CBN） wheels. When the wheel porosity reaches 45%, the bending strength is still high up to 50 MPa with modified orderly pore distribution. A porous CBN wheel was fabricated with a total porosity around 30%. The grinding performance of the porous composite-bonded CBN wheel was evaluated in terms of specific force, specific grinding energy, and grinding temperature, which were better than those of the vitrified one under the same grinding conditions. Compared to the vitrified CBN wheel, clear straight cutting grooves and less chip adhesion are observed on the ground surface and there is also no extensive loading on the wheel surface after grinding.     

用CBN刀具高速切削灰铸铁的试验研究

研究了CBN刀具高速切削灰铸铁时的刀具前、后刀面磨损、耐用度以及富氧气氛对切削性能的影响,所用的灰铸铁具有不同的铁素体、珠光体比例,最高切削速度达1＇100 m/min.研究表明Amborite刀具的刀尖磨损略大于BZN6000刀具,在较低速度下加工以铁素体为主的灰铸铁时更容易发生月牙洼磨损;BZN6000刀具以700 m/min的切削速度加工铁素体含量较高的灰铸铁时耐用度较高,Amborite刀具的耐用度随切削速度而升高;在富氧气氛中切削可以减轻刀具磨损,这一效果对BZN6000刀具更为显著.文章中对这些现象的原因进行了讨论.     

纤维缠绕低损伤退绕跟随系统

为降低纤维缠绕过程中纱筒退绕的纤维磨损,研制了低损伤退绕跟随系统。通过分析纱筒卷绕特点及退绕运动过程,提出了角度替代的控制思想和导纱器自适应跟随控制策略;通过计算机控制伺服电机驱动导纱器运动,可实现对任意卷绕线型的自动跟随。实际应用表明:该方法可行,研制的系统跟随效果理想,有效消除了纤维的摩擦损伤,提高了缠绕复合材料制品的质量。     

Twaron纤维的新型化学活化方法

以傅瑞德-克拉夫茨(Friedel-Crafts)反应为基础,活化处理Twaron纤维的惰性表面。对经过活化处理的Twaron纤维进行了单丝拔出(SFP)、X射线衍射(XRD)、扫描电镜(SEM)、红外图谱(FTIR)、表面电子能谱(XPS),以及表面自由能等测试。测试结果显示,经过活化处理后,Twaron纤维表面因环氧基团的接枝而使表面自由能显著增加;纤维表面的结晶结构未发生显著改变,纤维的本体强度未降低;相对应的环氧树脂基复合材料的单丝拔出强度提高了约50%。     

纳米TiC粉末改性钎料钎焊CBN磨粒的结合界面和磨损特性

采用了Ag-Cu-Ti 合金和纳米 TiC 粉末组成的新型复合钎料钎焊立方氮化硼(CBN)磨粒和工具基体,运用了三维体式显微镜和扫描电镜,研究了CBN磨粒与改性钎料之间的结合体系,包括界面微结构和反应产物,并进行了钎焊磨粒耐磨性试验.试验结果表明:加入的纳米TiC粉末均匀分布在钎料层内,细化了Ag-Cu-Ti合金钎料层的显微组织,有效控制了CBN磨粒与钎料的剧烈反应;磨粒表面化合物均匀致密,确保了CBN磨粒、纳米改性钎料和基体之间的结合强度;钎焊CBN磨粒的磨损形式以磨耗磨损为主,后期出现微小破碎,无磨粒脱落.     

高纯硼粉的特性及其在富燃料推进剂中的应用研究

通过SEM、XRD、pH计、X射线荧光光谱仪和HAAKE流变仪等研究了高纯硼粉的物化特性,并重点研究了其用于富燃料推进剂的燃烧性能.结果表明,高纯硼粉中大部分颗粒不规则,但在微观上呈晶体结构.由于高纯硼粉表面B2O3、H3BO3杂质非常少,硼粉与水悬浊液的pH值接近中性,硼粉在HTPB粘合剂中的屈服值和表观粘度较小,且随混合时间增加,屈服值和表观粘度保持不变.通过290～407 ℃范围内高纯硼粉富燃料推进剂热分解过程的质量损失可定性认为,高纯硼粉参与凝聚相反应的活性高于无定形硼粉.燃烧性能研究表明,含高纯硼粉的富燃料推进剂低压下正常燃烧,燃烧特性与无定形硼粉相同,实测燃烧热和燃烧效率较高.     

无缓凝剂磷酸镁修补砂浆的力学性能实验研究

磷酸镁水泥(Magnesium phosphate cement,MPC)是一种快速修补型胶凝材料,具备快硬、早强、高强、粘结力强、耐久性好等优点。首先运用正交试验方法,通过控制胶砂比、氧化镁与磷酸二氢盐的物质的量比(M/P)和水胶比,确定了基准MPC修补砂浆的最优配合比。然后研究了粉煤灰和磨细矿渣对MPC修补砂浆抗压强度和抗折强度的影响,分析了其强度特征。结果表明,MPC修补砂浆的最佳M/P比为6∶1,胶砂比1∶1。掺加粉煤灰的MPC修补砂浆具有较高的强度尤其是抗折强度,适宜作为道路与机场道面的快速修补材料。掺加磨细矿渣的MPC修补砂浆,其力学性能不如掺加粉煤灰的MPC修补砂浆。此外,MPC修补砂浆的抗折强度和抗压强度之间具有密切的线性相关关系,且与养护龄期、原材料来源与烧结温度、是否掺加缓凝剂和矿物掺合料、M/P比和水胶比等因素无关。     

埋入式光纤应变传感器

埋入式光纤应变传感器是近年来随着智能复合材料的发展而发展起来的一项新技术，将传感器和致动器埋置于复合材料中，就形成了智能复合材料，而光纤传感器具有尺寸小重量轻的特点，当把它们直接埋置于复合材料中时，它们也能在恶劣的环境下工作，它们的这些特点晨常适合于制作埋入式传感器，并且能大大提高智能复合材料在航天等方面应用的潜力，本文仅对智能复合材料中的光纤应变传感器进行了探讨，介绍了几种常见的埋入式光纤应变传     

生物体液在线光纤光谱仪的研制

介绍了一种直接检测生物体液的光纤光谱仪，根据光纤和毛细管的特性，作者设计了一种特殊的光纤探头，该探头可以直接插入生物体内，通过毛细管采集生物体液，并直接引入光路中，即样品不需进行任何预处理就可以直接测量。为了提高测量灵敏度，探头中的光纤采取分层排列以增加体液在光路中的路程，该探头可使测量过程简化并且实现在位监测。利用计算机的并行口输出脉冲以控制步进电机而动色耗棱镜转动，用光电位增管接收其光谱信号，