阳极氧化铝模板法制备CoPt纳米管

采用电化学直流沉积,首次在氧化铝模板中成功制备出直径为50 nm的CoPt纳米管高度有序阵列。利用透射电子显微镜(TEM)、扫描电子显微镜(SEM)、X射线衍射仪(XRD)以及振动样品磁强计(VSM)对样品的结构和磁学特性进行测试。分析表明,CoPt纳米管是以面心立方(fcc)结构存在。当外加磁场与纳米线平行时,CoPt合金纳米管的矫顽力达450 Oe,这种大面积制备的CoPt纳米管希望在超高密度信息磁存储上得到应用。     

颗粒增强锌基复合材料断裂与断口分析

为探讨颗粒增强低熔点金属基复合材料的性能和断裂特性，扩大锌合金的应用范围，本项工作采用流变铸造法制备了ＳｉＣｐ／Ｚｎ，Ａｌ２Ｏ３ｐ／Ｚｎ基复合材料，对该材料进行了冲击韧性、弯曲强度、压缩强度等性能测试，观察了其断口形貌，分析了其断裂特性，提出了此类复合材料的断裂模式。文中还讨论了增强颗粒的表面处理、粒子含量、粒径大小、粒于种类、基体合金种类对复合材料性能的影响。     

Effects of Hybrid Voltages on Oxide Formation on 6061 Al-alloys During Plasma Electrolytic Oxidation

Plasma electrolytic oxidation (PEO) is carried out on 6061 Al-alloys in a weak alkaline electrolyte containing NaOH, Na₂SiO₃ and NaCl. Centered on the correlation of composition and structure, analyses by means of X-ray diffration (XRD), scanning electron microscope (SEM) and energy dispersive spectrometry (EDS) are conducted on the specimens, which have been PEO-treated under hybrid voltages of different direct current (DC) values (140-280 V) with constant alternate current (AC) amplitude (200 V). Attention is paid to the composition, properties and growth mechanism of oxide layers formed with hybrid voltages. Moreover, the main effects of DC value are discussed. Ceramic layers with a double-layer structure which combines hard outer and soft inner layers are found to be consist of α-Al₂O₃, γ-Al₂O₃ and mullite. With the DC values increasing, the growth of the ceramic layers tends to have increasingly obvious three-stage feature.     

过渡金属/稀土金属氧化物纳米粒子催化AP热分解研究

1引言纳米材料由于特殊的表面特性而作为催化剂被广泛地研究。按一定的比例将不同的催化剂进行掺杂混合,有可能获得优于单一催化剂的催化性能。如Cu-Zn纳米催化剂就可替代昂贵的铂或钯催化剂实现对某些有机化合物氢化反应的催化[1]。随着纳米技术的发展,纳米过渡金属氧化物[2](     

机器人磨抛氧化锆涂层工艺研究

使用搭建的机器人自动磨抛平台系统,针对氧化锆热障涂层磨抛工艺开展了研究,旨在通过机器人磨抛加工对涂层厚度及表面粗糙度进行合理控制,提高涂层表面质量。基于Preston理论建立了氧化锆涂层材料的去除模型;通过单因素试验研究了主要磨抛参数对材料去除深度的影响规律,基于正交试验确立了氧化锆涂层材料磨抛最优工艺参数组合和工艺步骤,对航空发动机喉道密封片氧化锆涂层进行了磨抛加工。试验结果表明,在一定范围内,材料去除深度随着磨抛压力及磨抛盘转速的增大而增大,随着进给速度的增大而减小;磨抛压力对材料去除深度的影响较大,磨抛倾角对去除深度的影响较小。机器人磨抛系统采用力控方式实现了定量均匀去除,涂层厚度和表面质量一致性良好,加工效率显著提高,同时也验证了本机器人自动磨抛系统的实用性和优越性。     

N2O微推力器性能及喷管热结构分析

针对采用氧化亚氮推进剂的单组元微推力器开展了比冲性能影响因素的分析,分析结果显示微推力器比冲与氧化亚氮分解效率及喷管扩张比有着密切关系。利用有限元分析法对高空及地面试验两种工况下氧化亚氮单组元微推力器喷管的结构温度场开展了数值仿真计算,并在结构温度场仿真计算的基础上进一步对地面试验用喷管的结构应力场进行了分析。初步试验表明,所设计的微喷管在地面工况下工作良好。     

Preparation and Photoluminescence of ZnO Nanostructures

Porous anodic alumina (PAA) hosts with ZnO nanoparticles loaded in were prepared by immersing PAA films in an aqueous solu-tion of zinc acetate and then annealing at high temperatures. Highly ordered ZnO nanodot arrays were produced using the method in combination of PAA template with RF magnetron sputtering deposition. The photoluminescence of the ZnO/PAA composite and the highly ordered ZnO nanodot arrays were investigated by means of a fluorescent spectrometer. The ZnO/PAA composite exhibits intense and broad photoluminescence spectra with the peak position at around 485 nm. The ZnO nanodot arrays have a strong UV light emissive peak at about 380 nm and a wide light emissive peak at 460 nm-610 nm at the room temperature.     

过渡金属氧化物表面修饰氢气传感器

以SnO2系为敏感材料制备气敏元件,在元件的表面涂敷一层Fe2O3,MnO2或CuO掺杂的活性氧化铝修饰膜,有效地隔离并消除乙醇、烟雾、有机蒸气等杂散气体对元件的干扰.     

挤压成型对LC4CS铝合金棒材阳极氧化膜结构的影响

研究了挤压成型对LC4CS铝合金棒材表面阳极氧化膜微观结构的影响。采用金相显微（OM）技术、扫描电镜（SEM）和能谱分析（EDS）等方法分析了铝合金基体中合金相的种类和分布、组织结构的变化规律以及阳极氧化膜的表面及断面形貌。研究发现,试样表面阳极氧化膜的结构特征与基体组织特征具有一致性。基体中的阳极相和阴极相颗粒分别导致了氧化膜中孔洞和夹杂缺陷的产生,在挤压变形中形成的析出相带以及不完全再结晶组织是造成氧化膜中凹坑结构和复杂网纹结构的主要原因。     

N2O单组元推力器预热过程有限元分析

以正交试验设计理论为指导,应用有限元分析软件针对采用N₂O推进剂的单组元微推力器的在真空环境下的预热过程开展了分析,计算结果表明加热功率及推力器外表面辐射率的大小对预热效果影响明显.所开展的微推力器壳体地面预热试验的试验结果与仿真计算结果吻合良好,验证了采用仿真方法来评估预热过程的可行性.为进一步的结构及试验设计提供了借鉴.