透波氮化硅纤维的综合性能评价表征研究

系统研究了氮化硅纤维的基本物理性能、力学性能和介电性能,并且探究了各性能的测试方法。结果表明,氮化硅纤维在1 500℃的高温强度保留率达到50%以上,介电常数为6.0左右,说明氮化硅纤维可以作为透波材料在苛刻的高温环境下长时使用。     

大型飞行器表面烧蚀防热涂层低温快速补涂工艺

采用补涂工艺对烧蚀防热涂层进行低温快速补涂,并针对飞行器临飞行前状态,制定了涂层结合力提升、快速固化、多余物控制等的方案。电弧风洞试验表明:补涂涂层烧蚀量小,最高表面温度580℃,最高背面温度64℃,具有良好的防热性能。采用本工艺补涂涂层进行了多次飞行试验并取得了成功,表明本补涂工艺具有良好的工艺稳定性。     

黏胶丝基碳布增强C/C复合材料研究

采用黏胶丝基碳布进行了二维层板C/C复合材料研究。和PAN基碳布进行对比,分别从碳纤维微观结构、表面形貌、碳布物理性能、树脂基复合材料炭化过程残余热应力模拟、C/C复合材料力学和热物理性能表征等方面进行了对比分析和研究。结果表明,2 200℃处理的黏胶丝基碳纤维是非石墨化结构;纤维横断面呈腰子形,碳布纬向纱弯曲。黏胶丝基碳纤维的密度仅1．39 g/cm~3;拉伸模量很低,约50 GPa。炭化过程研究表明,黏胶丝基碳纤维轴向具有持续的正的线膨胀行为,在炭化初期与酚醛树脂的膨胀行为相一致;黏胶丝基碳布增强树脂基材料在800℃的面内自由热应变是PAN基材料的1/8;模拟的炭化过程热应力是PAN基材料的1/60。黏胶丝基C/C层板材料的层剪强度高于PAN基C/C复合材料,达到16．2 MPa;其拉伸强度为46．6 MPa,弯曲强度高达95．5 MPa,拉伸模量与弯曲模量基本一致,约10 GPa。黏胶丝基C/C复合材料在800℃的热导率是6．48 W/(m·K),与PAN基C/C复合材料非常接近;在800℃的线膨胀系数是2．18×10~(-6)/ K,远高于PAN基C/C复合材料的-0．387×10~(-6)/K。总之,黏胶丝基碳纤维由于其表粗糙度大、碳布纬向纱弯曲、极低的拉伸模量、正的轴向线膨胀系数,因而C/C复合材料层剪强度高,成型工艺中热应力低,较PAN基碳纤维更适合于研制不分层的二维C/C复合材料。     

含冲击损伤复合材料加筋层板压缩剩余强度

将复合材料加筋层板受低速冲击后的损伤区域描述为一个椭圆形弹性核,材料在核区的弹性模量下降由冲击表面的凹坑深度确定。利用含任意椭圆核各向异性板杂交应力有限元来模拟含损伤区域,杆单元来模拟筋条,钉单元模拟铆钉（胶层）和常规8节点等参单元模拟其余无损区域,建立起含低速冲击损伤复合材料加筋层板的力学响应分析方法。利用基于特征曲线概念的点应力判据、最大正应力判据和最大剪应力判据分别预测蒙皮的破坏、筋条的破坏和铆钉（胶层）的破坏,从而预测加筋层板在压缩载荷下的剩余强度,获得了与试验相吻合的结果。最后讨论了损伤尺寸、损伤形态、铺层比例等参数对加筋层板剩余强度的影响。     

基于蜻蜓膜翅结构的飞机加强框的仿生设计

由于机动性和能耗的要求,飞机设计过程当中轻量化设计是十分重要的。经过亿万年的进化,在承受自身重量及生长环境的载荷过程中,生物体获得了适应环境的最优结构。通过分析蜻蜓膜翅和飞机机身加强框的结构相似性,提取决定蜻蜓膜翅结构优良力学性能的结构特征,将其应用到飞机机身加强框的设计当中,并用有限元工具验证了结构的优化效果。在同样的承载条件下,仿生型结构的比刚度比原型结构提高了2%~6%,比强度提高了1%~8%。同时,仿生型结构的最大应力减小,而最小应力明显增大,因此其应力分布更加均匀,从而体现了仿生结构件材料的优化分布和最大效能。     

Residual Strength of Stiffened LY12CZ Aluminum Alloy Panels with Widespread Fatigue Damage

Experimental and analytical investigations on the residual strength of the stiffened LY12CZ aluminum alloy panels with widespread fatigue damage （WFD） are conducted. Nine stiffened LY12CZ aluminum alloy panels with three different types of damage are tested for residual strength. Each specimen is pre-cracked at rivet holes by saw cuts and subjected to a monotonically increasing tensile load until failure is occurred and the failure load is recorded. The stress intensity factors at the tips of the lead crack and the adjacent WFD cracks of the stiffened aluminum alloy panels are calculated by compounding approach and finite element method （FEM） respectively. The residual strength of the stiffened panels with WFD is evaluated by the engineering method with plastic zone linkup criterion and the FEM with apparent fracture toughness criterion respectively. The predicted residual strength agrees well with the experiment results. It indicates that in engineering practice these methods can be used for residual strength evaluation with the acceptable accuracy. It can be seen from this research that WFD can significantly reduce the residual strength and the critical crack length of the stiffened panels with WFD. The effect of WFD crack length on residual strength is also studied.     

热模锻造对Ti-24Al-15Nb-1.5Mo/TC4双合金界面连接强度与组织的影响

研究热模锻造经真空电子束焊接的Ti-24Al-15Nb-1.5Mo与TC4双合金焊缝界面的显微硬度变化、合金元素扩散趋势、显微组织特征和拉伸性能。结果表明,焊后未经任何处理的的试样焊缝边界处Al和Nb含量有突变;经700℃保温12h,AC(空冷)的焊接件焊缝区显微硬度最高,HV0.98平均值达3780MPa;经热模锻造和热处理后,合金元素扩散充分,显微组织均匀,显微硬度均匀。焊接接头拉伸试验表明,经38%变形,1020℃锻造,700℃保温12h,AC处理的试样,高倍组织为双态组织,拉伸性能最好,室温延展率达16.5%,断面收缩率达44.5%。     

结合钎焊和氩弧焊方法对钛合金/Nb/不锈钢接头的连接

利用AgCu-1.8Ti和AgCu-4.4Ti两种钎料对Nb与0Cr17N i4Cu4Nb不锈钢进行润湿性研究,并钎焊Nb与0Cr17N i4Cu4Nb接头。AgCu-1.8Ti在Nb与0Cr17N i4Cu4Nb上的润湿角均小于AgCu-4.4Ti。分析接头组织发现,AgCu-4.4Ti钎料接头中在靠近不锈钢侧存在约50μm宽的富Ti层,而AgCu-1.8Ti钎料接头中未发现该富Ti层。利用氩弧焊将TC4与Nb预先焊好后再用两种钎料钎焊Nb和不锈钢,测定TC4/Nb/0Cr17N i4Cu4Nb接头的室温拉伸强度。数据显示,AgCu-1.8Ti钎料接头的室温拉伸强度平均值达到222.2MPa,而AgCu-4.4Ti钎料接头强度仅有133.8MPa,所有接头均断于Nb与0Cr17N i4Cu4Nb界面。     

丁羟固体推进剂力学性能模拟计算

提出了丁羟固体推进剂力学性能的三相结构模型(分散相-界面相-连续相),建立了丁羟固体推进剂力学性能与弹性母体的伸长率和弹性模量、推进剂组分固体含量、粒径、级配、粘合剂和键合剂等的数学关系,进行了编程计算;推进剂抗拉强度和伸长率的计算结果与实验值吻合较好,并用该软件计算研究了弹性母体的伸长率及模量?AP的粒径及级配?键合剂的含量等对推进剂力学性能的影响规律。     

淬硬不锈工具钢高速铣削工艺

结合生产,对S-136淬硬钢高速铣削工艺的刀具选择、冷却方式、进给路线进行了分析。结果表明,对具有大而平底面的模具型腔进行高速铣削时宜采用TiAlN涂层的圆角平头铣刀,使用油雾冷却,进给路线宜采用斜坡切入的圆弧进给方式。