为了提高AZ91D镁合金的耐腐蚀性能和表面硬度,对其进行了表面热处理扩散渗锌处理,并对其得到的膜层表面和断面形貌、结构组成、耐腐蚀性能、显微硬度等性能进行了探讨,测量了该合金热扩散渗锌前后试样的阳极极化曲线和交流阻抗图,这些试验结果都表明在AZ91D镁合金材料表面进行热扩散渗锌获得的表面膜层均匀细致,膜层由Mg₇Zn₃、Mg和Zn构成,而且该膜层与基体相比耐腐蚀性和对镁合金基体的防护性能有了显著提高,并具有较高的表面显微硬度.     

热控涂层紫外辐照试验方法的研究

几种有机热控涂层在真空下进行模拟太阳紫外辐照的试验。在真空条件和大气条件下测试涂层性能的变化,以比较热控涂层在进行紫外辐照时,原位测试和非原位测试的差异。     

Investigation on a Sol-gel Coating Containing Inhibitors on 2024-T3 Aluminum Alloy

For a long time, chromate incorporated conversion coatings have been drawn special attention in corrosion protection of air-craft-used aluminum alloys. However,ever-increasing environmental pressures requires that non-chromate conversion coatings be developed because of the detrimental carcinogenic effects of the chromate compounds. In recent years, the sol-gel coatings doped with inhibitors were developed to replace chromate conversion coatings, and showed real promise. A sol-gel coating was prepared and its anti-corrosion behavior was investigated using the potentiodynamic scanning (PDS) and the electrochemical impedance spectroscopy (EIS). It is found that the sol-gel coating obtained by the hydrolysis and condensation of 3-glycidoxypropyltrimethoxysilane (GPTMS) and tetramethoxysilane (TMOS) is prone to form defects if cured at the room temperature, whereas if cured at a higher temperature (100 ℃), these flaws can be avoided. Furthermore, it can be seen that addition of anti-foam agents and surfactants will reduce the faults if cured at the room temperature. Effects of the corrosion inhibitors, CeCl3 and mercaptobenzothiazole (MBT), in the sol-gel coatings on 2024-T3 aluminum alloy were also investigated. Results show that the corrosion resistance of the sol-gel coatings containing CeCl3 proves to be better than that of the pure and MBT added sol-gel coatings by the electrochemical methods.     

Electrolytic Passivation of Nitinol Shape Memory Alloy in Different Electrolytes

The corrosion behavior of the nitinol alloy was studied in various corrosion media of different Cl^- ion concentrations. The results demonstrate that the Cl^- ion concentration has significant influences on the corrosion behavior of the nitinol alloy. In order to enhance the corrosion resistance, protective films were generated on the surface of the nitinol alloy by means of the electrochemical passivation method, for which five different electrolytic solutions were investigated. The surface analysis indicates full growth of all samples passivated in the different electrolytic solutions with layers, however, showing different morphological features. Without any defects like micro-cracks and pores, the surface of the samples passivated in the molybdate solution turns out smoother and denser than those passivated in other solutions. It is shown that the electro-chemical passivation will reduce Ni content but increase Ti content in the surface, reaching the Mole ratio of Ti：Ni = 9.01：1 on the outermost surface. Potentiodynamic polarization test demonstrates that the samples electrochemically passivated in the molybdate solution present a significant increase in breakdown potential due to titanium enrichment on the outermost surface.     

C／SiC复合材料与CVDSiC涂层的结合性能研究

采用先驱体转化法(PIP方法)制备C/SiC陶瓷基复合材料,通过调整多孔预制件的体积密度制备出不同组分比的C/SiC复合材料。结果显示,C/SiC复合材料的热膨胀系数随着复合材料中SiC含量的增加而增加,其与CVDSiC涂层之间的热匹配也相应增加,通过CVI方法制备梯度过渡层,在C/SiC复合材料表面制备出致密度较高的CVDSiC涂层。     

Ni基合金与γ-TiAl基合金的固态连接规律研究

通过对Ni基合金进行激光熔覆γ-TiAl基合金涂层处理,对γ-TiAl基合金进行激光表面熔凝处理,提出了一种采用激光表面改性技术和超塑扩散连接相结合的Ni基合金/γ-TiAl基合金连接新技术。研究了合金激光改性层的显微组织特征,探讨了Ni基合金/γ-TiAl基合金固态扩散连接的规律。结果表明:激光表面改性技术提高了Ni基合金/γ-TiAl基合金的连接质量,合金通过激光表面改性处理后,采用连接温度850℃、连接压力60MPa、连接时间1h的连接条件及900℃保温0.5h连接后续热处理,实现了Ni基合金/γ-TiAl基合金的连接。     

SiC纤维CVD涂层工艺研究

对SiC纤维的CVD涂层工艺进行研究.实验发现采用BCl3,H2及CH4作为反应气体,采用与SiC纤维生产工艺相匹配的走丝速度并控制一定的工艺参数,在1350℃左右可得到厚度2～3mm且表面致密的B4C涂层,纤维涂层后性能基本保持不变.仅采用BCl3及CH4作为CVD涂层工艺反应气体,在1180～1250℃即可沉积出表面光滑致密,厚度2～3mm的富碳B4C涂层,涂层后纤维性能可提高10%左右,且涂层与纤维结合强度很高,优于B4C涂层与SiC纤维的结合强度.实验还发现SiC纤维涂覆B4C及富碳B4C涂层后,能有效阻隔界面反应,可大幅提高SiC/Ti基复合材料的性能.     

喷丸处理对IC6合金NiCoCrAlY涂层表面粗糙度的影响

研究喷丸处理对IC6合金NiCoCrAlY涂层表面粗糙度的影响.结果表明,在涂层真空扩散处理后进行喷丸处理,喷丸压力0.4MPa和时间4min可显著改善NiCoCrAlY涂层表面粗糙度,使Ra降至1.6μm以下,并可提高涂层致密度.涂层喷丸处理所引入的残余压应力没有引起基体IC6合金再结晶.因此采取喷丸处理改善IC6合金NiCoCrAlY涂层表面粗糙度是完全可行的.     

TC4钛合金与多层TiN/Ti涂层的砂尘冲蚀损伤试验

建了砂尘冲蚀试验系统,采用粒子成像测速方法获得了气体压力和砂尘速度之间的关系,并在砂尘质量浓度为28.91g/m3,速度为80m/s,冲蚀角度为30°的条件下,对TC4钛合金和多层TiN/Ti涂层进行了冲蚀试验.结果表明:TC4钛合金抗冲蚀损伤能力较差,平均质量损失率达0.7mg/min.多层TiN/Ti涂层可承受砂尘冲蚀200min以上,且TiN/Ti调制比为1:3涂层的抗冲蚀能力优于调制比为1:1的涂层.砂尘粒子垂直冲击速度分量引起的微区剥落是涂层冲蚀损伤的主要原因,增加多层涂层韧性是提高其抗冲蚀性能的关键.      

新型封严涂层高温高速磨耗试验机的研制

为模拟航空涡轮发动机气路封严配副在工作状态下的磨损磨耗现象,研究封严涂层的可磨耗性能,研制了1套新型的可磨耗性能评价试验器。该试验器采用叶片-涂层刮削式磨耗副,使用模拟轮盘带动叶片高速旋转实现叶尖的切线速度;采用封严涂层试样径向进给以模拟叶片刮削切入;使用压电石英晶体3向测力仪定量测量瞬态刮削力;采用高速高温火焰加热试样。考核结果表明:试验器能够完成叶尖切线速度为0~300 m/s、进给速率为1.5~2025μm/s、加热温度为20~800℃条件下的磨耗试验,试验效果良好,数据稳定可靠。