6156-T4铝合金焊接加筋薄壁结构剩余强度评估的CTOD方法

为保证飞机设计满足损伤容限性能要求,有必要对其进行剩余强度评估。针对6156-T4铝合金焊接连接薄壁结构进行了R曲线和剩余强度试验,判断了裂纹扩展经过筋条时的裂纹扩展路径,测量了母板和筋条两个方向的裂纹扩展速率,并采用不同的断裂准则和分析方法对单及双跨度多个初始裂纹长度焊接加筋薄板的剩余强度进行了预测。结果表明:裂纹扩展在经过筋条时,同时沿着母板和筋条继续扩展,筋条上的裂纹扩展方向垂直于母板且两个方向的裂纹扩展速率基本相同;采用净截面屈服准则进行剩余强度预测时会低估这种韧性较好的焊接连接薄壁结构的剩余强度;基于SINTAP-FITNET评价体系,以裂纹尖端张开位移(CTOD-δ5)作为裂纹尖端弹塑性表征参量进行剩余强度预测时,预测结果比采用K曲线预测方法精度高。     

表面处理对17-4PH不锈钢抗固体粒子冲蚀性能的影响

为对比研究表面处理对17-4PH不锈钢抗固体粒子冲蚀性能的影响,在17-4PH不锈钢表面进行了多弧离子镀陶瓷/金属多层膜制备、激光表面合金化(LSA)处理和超音速火焰喷涂(HVOF)硬质合金层处理,利用划痕仪、自组装的不锈钢抗固体粒子冲蚀(SPE)装置、多冲疲劳试验机对上述三种表面处理试样的小攻角和大攻角SPE失效行为和机理进行了研究。结果表明,微切削是17-4PH不锈钢及其表面改性试样小攻角下固体粒子冲蚀破坏的主要失效机制,多冲型疲劳破坏是17-4PH不锈钢及其表面改性试样大攻角下固体粒子冲蚀的主要失效机制。HVOF WC-17Co涂层可显著提高17-4PH不锈钢30°小攻角和90°大攻角下SPE抗力。激光表面合金化层能够改善17-4PH不锈钢抗30°小攻角和90°大攻角下SPE性能,但SPE性能改善效果弱于HVOF喷涂涂层。TiAl N/Ti多层膜不能显著提高17-4PH不锈钢抗30°小攻角和90°大攻角的SPE性能。     

7150铝合金热变形行为及微观组织

采用Gleeble热模拟机进行热压缩实验,研究7150铝合金在变形温度为300~450℃、应变速率为0.01~10s-1条件下的变形行为,采用Zener-Hollomon参数法构建合金高温塑性变形本构方程,并对变形后的微观组织进行分析。研究表明:7150铝合金的流变应力随应变速率增大而增大,随变形温度增大而降低。该合金热压缩变形的流变应力行为可用双曲正弦形式的本构方程描述,其参数A为4.161×1014s-1,α为0.01956 MPa-1,n为5.14336,热变形激活能Q为229.7531k J/mol。随着温度升高和应变速率降低,动态再结晶逐渐取代动态回复成为合金的主要软化机制。     

焊后时效处理对2219铝合金VPTIG接头微区组织和显微硬度的影响

研究了不同温度焊后时效处理对2219铝合金变极性钨极氩弧焊(VPTIG)接头各微区显微组织的影响,采用显微硬度测试和透射电镜观察分析焊接接头各微区析出相的形貌和分布。结果表明,焊后时效处理温度不同,焊接接头各微区显微组织和硬度发生的变化不同。热影响区中的完全回复区对焊后时效最为敏感,低温处理时显微硬度就有明显增长,并在160℃处理时达到最大涨幅;焊缝区变化相对较小,其显微硬度的最高涨幅出现在210℃,且小于前者;热影响区中的过时效区最为稳定,显微硬度的最大增长同样出现在160℃,但涨幅很小。透射电镜观察表明,焊接接头各微区的显微硬度变化主要与时效强化相的析出行为有关。     

6061铝合金激光穿透焊的焊缝成形

分别采用光纤激光和YAG激光对2.5mm厚的6061铝合金开展了激光穿透焊接试验,研究了主要焊接参数对焊缝成形的影响规律。结果表明,与YAG激光相比,高能量密度的光纤激光更易于实现穿透焊接,且光纤激光获得良好焊缝成形的工艺区间更大。在穿透焊接条件下,焊缝截面形貌分为钉头形和近X形两种。当激光功率较高时,光纤激光焊缝更趋向于生成近X形截面,YAG激光焊缝更易于生成钉头形截面。焊缝成形受激光功率密度和焊接热输入双重因素的影响。随激光功率密度和焊接热输入的增大,光纤激光焊缝截面形貌逐渐由钉头形向近X形转变。     

Dynamic analysis of C/C composite finger seal

A seal device as an important component of aeroengines has decisive influence on per- formance, reliability, and working life of aeroengines. With the development of aeroengines, demands on the performance characteristics of seal devices are made strictly. Finger seal as a novel kind of sealing device, recently attracts more and more attentions in academic circles and engineer- ing fields at home and abroad. Research on finger seals has been extensively developed, especially on leakage and wear performances under dynamic conditions. However, it is a pity that the work on finger seals has been limited with a single approach that is improving the performance by structural optimization; in addition, the technology of dynamic analysis on finger seals is weak. Aiming at the problems mentioned above, a distributed mass equivalent dynamic model of finger seals considering the coupling effect of overlaid laminates is established in the present paper, the dynamic perfor- mance of 2.5 dimension C/C composite finger seal is analyzed with the model, and then the effects of fiber bundle density and fiber bundle preparation direction on finger seal＇s dynamic performance are discussed, as well as compared with those of Co-based alloy finger seal. The current work is about dynamic analysis of finger seals and application of C/C composite in this paper may have much academic significance and many engineering values for improving research level of finger seal dynamics and exploring feasibility of C/C composite being used for finger seals.     

基于轮廓法测试铝合金拉弯成形残余应力研究

以2026-T3511铝合金T形结构件的拉弯成形件为研究对象,首先采用线切割将T形结构件分割成两块具有T形截面的试样,然后基于轮廓法测试应力原理应用激光位移传感器分别测试两个分割截面的轮廓变化,进而将两个截面的测量值拟合平均后与有限元模型结合以计算该试样的初始残余应力,从而获得该T形结构件的横截面法向应力并分析其分布特征。研究结果表明,基于轮廓法测得的应力分布与有限元仿真结果分布规律相近:峰值压应力为60MPa,峰值拉应力为40MPa;轮廓法在航空结构件应力测试中能够准确地获得其他测试方法无法获得的横截面完整的应力分布。     

7075铝合金在不同温度盐水环境中的腐蚀疲劳行为

基于飞机结构材料7075铝合金在沿海地区服役时海水飞溅及曝晒导致的高温腐蚀疲劳损伤问题,研究了7075铝合金在35,55,75℃下3.5%NaCl溶液环境中的腐蚀疲劳寿命,并使用扫描电子显微镜(SEM)观察断口形貌,探讨了温度对腐蚀疲劳裂纹萌生扩展的影响机理。结果表明:同一应力水平下,温度越高,腐蚀疲劳寿命越短,300MPa时35,55,75℃下的中值寿命分别为33 001,30 931,15 346次循环。腐蚀损伤和疲劳损伤存在竞争关系,应力水平较高时,腐蚀较轻,试样寿命主要受应力水平影响,疲劳源多从铝合金基体与包铝层结合处萌生;应力水平较低时,腐蚀较严重,疲劳寿命随温度升高明显下降,疲劳源多从腐蚀坑处萌生。断口形貌显示高温环境主要通过加速腐蚀坑的形成来影响疲劳源的萌生,深坑状腐蚀坑应力集中严重,对疲劳性能伤害大。     

浅论铝合金真空钎焊机箱的应用和加工

本文阐述了真空钎焊技术的优点及铝合金真空钎焊机箱的应用和加工的重要性,突出了机载装备中真空钎焊的必要性。其次,本文以某型号机箱为例,围绕着铝合金真空钎焊机箱加工的四个方面详细地加以介绍、描述和总结了加工工艺及要点。最后,本文指出了铝合金真空钎焊机箱能够提升航空电子系统的整体效能,只有通过提高工艺水平,规范生产流程,才能确保机载电子设备机箱的生产和质量稳定,提高生产效益。     

TC4-DT钛合金磨削表面特性及其摩擦磨损性能

钛合金是一种典型难磨削加工材料,磨削表面易出现烧伤、裂纹等热损伤。本文开展了TC4-DT钛合金磨削实验,通过扫描电镜（SEM）、能谱（EDS）、X射线衍射（XRD）、显微硬度仪、金相显微镜及球-盘摩擦磨损实验仪研究了其表面特性及摩擦磨损性能。结果表明：低速磨削表面质量好,摩擦磨损性能较基体略提高;当砂轮线速度为80 m/s时,磨削表面质量良好,摩擦系数为0.38,较基体降低40%;而砂轮线速度为100 m/s时,磨削表面出现严重烧伤、网状裂纹。因此选择合理的高速磨削工艺可避免烧伤、裂纹等热损伤缺陷,并可有效改善表面摩擦磨损性能;磨削表面干摩擦磨损机制为磨粒磨损、粘着磨损和剥层磨损。