消失模铸造阻燃镁合金的组织与力学性能

对消失模铸造阻燃镁合金的组织和力学性能的试验研究表明，RE的加入在组织中出现了枝条状共晶Al11RE3相，并未形成粗大A12RE相，同时晶界上离异共晶β相的数量大大减小，且呈不连续网状或孤立块状分布。降低模样厚度和浇注温度，合金的组织明显细化，共晶Al11RE3相和β相的尺寸减小，分布更为均匀。消失模铸造阻燃镁合金的力学性能与消失模铸造AZ91镁合金的基本相当，断裂方式是以解理为主的脆性断裂。     

激光选区烧结金属粉末的研究

A series of experiments are carried out with selective laser sintering(SLS) for copper,copper-nickel powder matetials.The phenomena of the sintering process is ana-lyzed,the influence of techmological parameters is dis-cussed in detail,By means of SEM with energy spectrum system and X-ray diffraction spectrum,the morphology of the microstructure and the compositions of the different zones are analyzed,the mechanism of the laser sintering metallic powders is preliminarily explored,All those above lay the foundations for the forming metal parts by laser sintering metallic powders.     

航空发动机用钛合金BT20组织分析及相变点的测定

为了实现航空发动机上外调节片等重要零件的再制造，对其所用材料BT20钛合金进行组织分析，采用计算法和连续升温金相法研究了BT20钛合金的相变点，为航空发动机零部件的再制造修理提供参考。     

Al-Ti-B晶粒细化剂的组织与细化效果

以较为常见的8011铝合金为研究对象,分析了Al-Ti-B中间合金对其组织及性能的作用机理,结果表明:Al-Ti-B对合金组织具有细化作用,同时对其性能也有一定的影响,最后对试验结果进行了分析与总结。     

T250与30CrMnSiA异种材料焊接工艺技术

从冶金方面分析了T250与30CrMnSiA材料焊接工艺性。通过手工钨极氩弧焊焊接工艺研究试验,选择焊丝材料,确定材料焊接状态,制定了合理有效的焊接工艺规范和措施。采用光学金相显微镜、维氏硬度测试和力学性能检测等手段,对T250与30CrMnSiA异种材料焊接接头金相组织、力学性能和显微硬度等方面进行详细分析。结果表明,T250和30GrMnSiA异种材料具有良好的焊接性,填充HT250焊丝,采用热输入量较小的焊接电流进行焊接,接头强度与30GrMnSiA材料强度相当。     

AA2024铝合金搅拌摩擦焊接头特性研究

对6 mm厚AA2024-T4铝合金搅拌摩擦焊接头特性进行了研究。通过拉伸试验,得到了应力-应变曲线。用光学显微镜、显微硬度仪以及扫描电镜对焊接接头进行了金相分析、硬度测试以及断口分析。结果表明：试件断裂属于韧性断裂;断裂发生在前进侧热机影响区/热影响区的过渡区;当搅拌头转速为800 r/min,焊接速度为100 mm...     

Research on influence of typical microstructure characteristics of Ni base single crystal on creep rupture and deformation analysis of turbo blade

Considering the influence of typical microstructure characteristics on creep performance,a series of UM-F single crystal alloys which had similar element components but different microstructures were used to analyze the relationship between creep life and microstructure characteristics of Ni base single crystal.Three main factors were proposed:misfit,volume fraction of precipitate and maximum matrix channel width.The Microstate parameter Ymicro was established to estimate the deformation state of the materials.The linear relationship between the initial value of microstate parameter Y0 and creep life under a certain temperature/load was affirmed.By analyzing the high temperature region of turbo blade using the material parameters of DD 3,the creep deformation and the life prediction of the critical points of blade were obtained and the result closed to the test.     

Cr对Nb-16Si-22Ti-2Al-2Hf合金显微组织与高低温力学性能的影响

 以Nb-16Si-22Ti-2Al-2Hf成分为基础,分别添加了2%和17%(原子分数,后同)的Cr元素替代Nb(分别称2Cr和17Cr合金),研究了Cr含量对Nb-16Si-22Ti-2Al-2Hf合金相组成、显微组织形貌、室温断裂韧性和高温强度的影响,分析了高低温失效机制。结果表明,铸态和1 375 ℃×100 h热处理后2Cr合金由Nbss和Nb₅Si₃两相组成;当Cr含量为17%时,出现了具有C15结构的Laves Cr₂Nb相,合金由Nbss、Nb₅Si₃和Cr₂Nb三相组成,热处理后在Nb₅Si₃中还析出了球状Cr₂Nb相。随着Cr含量由2%提高到17%,热处理合金的室温断裂韧性K_Q由14.32 MPa·m^1/2下降到10.30 MPa·m^1/2。合金强度与Cr含量的关系受温度影响,随Cr含量提高,室温和1 150 ℃时合金的硬度或强度增高,而1 250 ℃和1 350 ℃时合金强度降低。如1 150 ℃时2Cr和17Cr合金的屈服强度σ_0.2分别为349 MPa和387 MPa;1 350 ℃时分别为306 MPa和74 MPa。     

激光增材制造过程数值仿真技术综述

数值仿真是研究激光增材制造过程中各类物理现象、揭示零件缺陷形成机理、优化增材制造工艺参数的重要手段,该领域学者针对增材制造过程中的热分析、金属粉末颗粒性质分析、微观结构分析、质量缺陷成因分析等方面,开展了大量研究,提出了相应的数学模型和方法。激光增材制造过程的数值仿真是一个在空间和时间上均跨越多个尺度的复杂问题,微观、介观、宏观尺度下数值仿真所关注的对象和所使用的方法各不相同;多数研究聚焦于某一尺度下的过程仿真,另一部分研究则基于不同模型的数据关系建立模型间的耦合关系,实现热-相、热-力的综合分析。对现阶段激光增材制造数值仿真领域的主要技术进行了综述,在梳理数值仿真基本流程的基础上,对其中涉及的热源模型,粉末模型,力学模型以及微观结构模型进行了介绍,讨论了其特点和适用性;结合相关技术领域的发展,探讨了激光增材制造数值仿真技术的发展方向,旨在为本领域的技术研究与发展提供参考。