基于静强度分布的复合材料疲劳寿命分布的预测模型(英文)

The reasons of the static strength dispersion and the fatigue life dispersion of composite laminates are analyzed in this article. It is concluded that the inner original defects, which derived from the manufacturing process of composite laminates, are the common and major reason of causing the random distributions of the static strength and the fatigue life. And there is a correlative relation between the two distributions. With the study of statistical relationship between the fatigue loading and the fatigue life in the uniform confidence level and the same survival rate S-N curves of material, the relationship between the static strength distribution and the fatigue life distribution through a material S-N curve model has been obtained. And then the model which is used to describe the distributions of fatigue life of composites, based on their distributions of static strength, is set up. This model reasonably reflects the effects of the inner original defects on the static strength dispersion and on the fatigue life dispersion of composite laminates. The experimental data of three kinds of composite laminates are employed to verify this model, and the results show that this model can predict the random distributions of fatigue life for composites under any fatigue loads fairly well.     

飞机日历寿命试验的介质成分确定和加速方法

 针对飞机使用环境,研究了飞机日历寿命试验中的腐蚀介质成分确定方法和加速方法。进行了5 ℃,25 ℃,50 ℃这3种温度和4种介质浓度下的30CrMnSiA结构钢和LY12CZ铝合金两种金属的纯腐蚀和腐蚀疲劳试验研究。得到的试验曲线表明,它们的腐蚀动力学规律都近似遵循线性关系,每条曲线的腐蚀速度也基本保持不变。从而认为,飞机日历寿命试验介质成分最好选用飞机所在机场使用环境的各腐蚀介质成分,加速腐蚀试验的最好方法,就是在此机场的各介质成分上加权,加权越高,加速越快。这个结论得到了试验验证。     

不同温、湿度条件下硅橡胶密封圈贮存寿命研究

通过对硅橡胶P6144密封圈的加速老化试验,建立了该密封圈材料在贮存温度下的压缩永久变形和时间的关系,预测了25℃、35℃、45℃、55℃、65℃和75℃温度条件下硅橡胶P6144密封材料的贮存寿命,研究了温度对硅橡胶密封圈贮存寿命的影响规律。     

基于小裂纹的2024-T3铝合金中心孔试样疲劳寿命预测

对2024-T3铝合金板材中心孔试样进行了疲劳裂纹扩展行为及寿命预测的理论和试验研究.采用疲劳条带与显微镜观测相结合的办法获得试样在块谱作用下孔边自然萌生裂纹扩展的α-N数据,并通过对断口的SEM观察获取试样的初始缺陷形状.利用基于裂纹闭合的小裂纹扩展分析程序FASTRAN3.9对试样α-N数据进行反推,建立了描述孔边裂纹细节原始疲劳质量的当量初始缺陷尺寸(EIFS)分布.以该分布为基础,采用FASTRAN3.9对试样进行了恒幅载荷下试样的中值疲劳S-N曲线的预测,预测结果与试验验证结果吻合较好.     

某型发动机轴流叶轮疲劳寿命分析

为准确了解某型发动机的关键零部件——轴流叶轮的使用寿命,进而提高其可靠性,分析了该轴流叶轮的痧劳寿命,并通过疲劳寿命试验进行了验证．研究结果为轴流叶轮的定寿和延寿提供了重要依据。     

中性盐雾预腐蚀对AF1410高强钢疲劳寿命的影响

采用失重法和XRD法研究了AF1410钢在中性盐雾环境中的耐蚀性能,并对中性盐雾预腐蚀不同时间后的试样进行疲劳性能测试,研究了不同预腐蚀时间对材料疲劳寿命的影响。结果表明:AF1410钢发生了严重的全面腐蚀,腐蚀产物主要由FeO(OH)和Fe3O4组成,并得到其腐蚀失重曲线;疲劳断口形貌分析表明,随预腐蚀时间的延长,腐蚀损伤程度增加,在疲劳加载过程中易形成较多的疲劳裂纹扩展源而导致疲劳断裂失效;最终获得中性盐雾预腐蚀AF1410钢结构疲劳寿命特性以及预腐蚀对疲劳寿命的影响系数C(t)曲线。     

层合板螺栓连接结构疲劳寿命预测

为了准确预测复合材料连接结构损伤的产生和扩展,基于单向板疲劳性能预测层合板螺栓连接结构疲劳寿命。用T300/BMP-316单向板试验数据对正则化疲劳寿命与剩余强度的参数进行拟合;在复合材料基体主控失效判据基础上增加纤维失效和分层失效判据,改进基于断裂韧性的失效准则判定损伤的产生和扩展;采用二级载荷疲劳寿命等效实现损伤的非线性累积,再对相应的损伤进行材料性能退化。预测结果与试验对比表明:对不同几何参数层合板连接结构的对数寿命预测与试验误差在5%以内,对不同应力水平下层合板连接结构的对数寿命预测与试验误差在10%以内,最终破坏模式及损伤区域的预测与试验结果吻合良好。     

热声载荷下薄壁结构振动响应试验验证与疲劳分析

由于热声环境下金属薄壁结构表现出复杂的大挠度强非线性振动响应特性,影响结构的疲劳性能与寿命,结合有限元法与降阶模态法对四边固支高温合金矩形薄壁结构的热声响应进行计算。结果研究发现:屈曲后结构出现跳变运动且应力循环呈三角状分布,热声载荷的相对强弱决定了跳变形式。采用改进雨流计数法、Morrow平均应力模型、Miner线性损伤累积理论计算热声疲劳寿命,屈曲前到临界屈曲时应力循环损伤量级显著增大,由10-5增大到10-4,寿命随温度增加呈先减小后增加趋势。开展薄壁结构热声试验,并将仿真计算结果与试验结果进行对比,结果表明结构的模态频率偏差不超过1Hz,动态应变响应结果的量值相当,验证了薄壁结构热声响应计算方法与模型的有效性。      

一种TiAl合金高温低循环疲劳性能及失效机理

通过对TiAl合金进行总应变范围控制的高温(750℃)低循环疲劳实验,研究双态(Duplex,DP)和全片层(Fully Lamellar,FL)组织形态对TiAl合金低循环疲劳性能和寿命的影响,并采用总应变幅-寿命方程对两类组态TiAl合金低循环疲劳寿命进行预测。结果表明:在相同温度和应变条件下,DP组态TiAl合金稳态迟滞回线对应的平均应力明显低于FL组态TiAl合金稳态迟滞回线对应的平均应力;采用总应变幅-疲劳寿命方程能够准确预测两种组态TiAl合金在750℃下的疲劳寿命,预测寿命基本位于试验寿命的±2倍分散带以内;另外,DP组态TiAl合金的疲劳源区位于试样的近心部,而FL组态TiAl合金的疲劳源区位于试样的次表面,两类组态TiAl合金的高温疲劳失效机理存在明显差异。     

综合时序信息的试验优化设计及稀疏求解

考虑不同试验点的试验成本及试验时序信息,在性能指标与影响因素间的响应模型未知情况下,利用装备系统的先验信息构造模型驱动的基函数,构造相应的回归模型来刻画系统的内在关系,分析不同试验点成本及试验时序对试验方案的影响。定义了一种考虑空间权重及批序贯时序的非均匀最优设计模型,将稀疏理论引入到回归试验设计中,把不同批次试验下的回归试验设计模型参数估计问题转换为结构化稀疏重构问题,讨论了非均匀最优设计的构造定理,提出结构化稀疏参数求解算法。算例表明:利用本方法生成的试验点考虑了试验点空间权重和试验时序信息,更符合实际试验规程;采用本方法获得的响应函数得到的期望预测误差更小。