低合金钢管的焊接工艺及缺陷预防

采用氩弧焊打底,焊条电弧焊填充盖面焊接Cr5Mn低合金钢管,钢管壁厚为12mm,焊接位置为水平固定全位置焊接,在焊接之前,调整好焊接工艺参数,焊接完毕以后,对焊缝外观检验和X射线无损检测,发现焊缝的表面出现少量微裂纹,内部有少量气孔。为了保证焊缝的质量,对缺陷产生的原因进行分析并且采取正确的焊接工艺方法避免焊接缺陷。     

法兰环缝局部真空电子束焊机的研制

对所研制的法兰环缝局部真空电子束焊机作了简要介绍，对焊机的微机控制系统和电子 枪极坐标行走的控制、二次电子焊缝对中、焊接轨迹的示教再现、真空系统和焊接工艺的微机控制等关键技术作了较为详细的阐述。通过焊接工艺试验，用法兰环缝局部真空电子束焊机焊接出了成形良好、焊缝内部质量符合GJB1718－93Ⅰ级标准的铝合金法兰环缝典型工艺件。     

复合材料层板多钉机械连接强度计算方法

提出了一种适于设计计算使用的复合材料层板多钉机械连接强度分析方法。该方法将复合材料板多钉机械连接强度分析问题化为求解各向异性体弹性理论中的复势函数边值问题,以Faber级数和最小二乘边界配置技术为工具导出了孔边应力的级数解表达式。选用的孔边特征曲线上的点应力失效判据避开了孔边接触、材料非线性、大位移、刚度减缩等复杂且难以验证的强度模拟计算过程。计算结果与试验结果符合较好。还详细探讨了铺层比例、排距等设计参数对钉载分配、挤压强度的影响规律。     

铜与铜镶嵌非晶体焊料点焊的研究

研究了铜与铜镶嵌非晶体焊料ＱＪＹ－５Ａ、ＱＪＹ－５Ｂ点焊,以及调整点焊温度场来降低焊接区铜的熔点,提高焊接区电能利用率的措施;叙述了铜与铜镶嵌ＱＪＹ－５Ａ、ＱＪＹ－５Ｂ焊料点焊焊核形成过程及特点。     

“布朗”航天飞机结构的焊接

介绍了俄罗斯“布朗”航天飞机结构的焊接历史和现状,详细阐述了装配、机加、焊接、校正的工艺过程、试验数据及所采用的专用设备、工装概况。     

C300 穿孔型等离子弧焊接焊缝结晶裂纹的研究

采用光学显微镜、扫描电子显微镜以及Thermal-calc 计算等方法分析了马氏体时效钢(C300) 穿
孔型等离子弧焊接(Keyhole-Plasma Arc Welding, K-PAW)过程中结晶裂纹的成因及形貌。研究认为,C300 虽
然具有良好的焊接性,但也会产生结晶裂纹。本试验条件下,影响高纯净C300 产生结晶裂纹的主要因素是应
变—温度增长速率,提高预热温度和增加线能量有利于降低结晶裂纹倾向。焊接热源对母材的预热作用有利
于已形成结晶裂纹的逐步止裂。具有凸形表面的焊缝以及细小等轴晶的焊缝的结晶裂纹倾向较小。     

基于密度权重的可靠性灵敏度分析方法

为了提高可靠性灵敏度求解数字模拟法的效率,提出了一种变量空间确定性低偏差均匀抽样与样本点处联合概率密度函数构造权重相结合的方法,来估计可靠性灵敏度。该方法通过均匀样本点处联合概率密度函数的权重保证了可靠性灵敏度的估计值收敛于真值,而由低偏差抽样代替原问题中的联合概率密度抽样则可以保证更低的误差阶以及在小失效概率条件下抽得的样本有更高的可能性落入失效域,从而保证了所提方法具有更高的收敛速度。另外,所提方法可以采用与独立变量相同的步骤来估计相关变量情况下的可靠性灵敏度,计算简便,适用范围广。算例充分证明了所提方法的优越性。     

Friction moment analysis of space gyroscope bearing with ribbon cage under ultra-low oscillatory motion

This paper presents the model of calculating the total friction moment of space gyroscope ball bearings which usually work under ultra-low oscillatory motion and are very sensitive to the friction moment. The aim is to know the proportion of the friction moment caused by each frictional source in the bearing＇s total friction moment, which is helpful to optimize the bearing design to deduce the friction moment. In the model, the cage dynamic equations considering six degree-of-freedom and the balls dynamic equations considering two degree-of-freedom were solved.The good trends with different loads between the measured friction moments and computational results prove that the model under constant rate was validated. The computational results show that when the speed was set at 5 r/min, the bearing＇s maximum total friction moment when oscillation occurred was obviously larger than that occurred at a constant rate. At the onset of each oscillatory motion, the proportion of the friction moment caused by cage in the bearing＇s total friction moment was very high, and it increased with the increasing speed. The analyses of different cage thicknesses and different clearances between cage pocket and ball show that smaller thickness and clearance were preferred.     

带迎角钨杆斜侵彻铝板数值仿真研究

为研究迎角对钨杆斜侵过程的影响,开展了带迎角钨杆斜侵彻铝板数值仿真研究。仿真中采用SPH方法,Shock状态方程和Steinberg本构模型。钨杆共有两种尺寸,分别为Φ10mm×23mm和Φ10mm×46mm。铝板厚10mm,撞击速度为2km/s,撞击角度为60°。为简化分析,将迎角分解为俯仰角和偏航角,其中俯仰角范围为-90°～90°,偏航角范围为0°～90°。对钨杆侵彻过程的分析结果表明：斜侵彻存在临界迎角,在临界迎角范围内钨杆所受力矩可忽略不计;在临界迎角范围外,钨杆将发生弯曲甚至折断。对钨杆的剩余质量分析结果表明：当偏航角为0°且钨杆未折断时,剩余质量只在较小的范围内变化;当俯仰角为0°时,剩余质量随迎角增加线性减小。对钨杆的剩余速度分析结果表明：偏航角对剩余速度的影响与俯仰角对剩余速度的影响基本一致,剩余速度曲线关于0°迎角基本对称。根据仿真结果,采用曲线拟合的方法给出了钨杆斜侵彻铝板的剩余速度经验公式。     

柔性接头有效摆心漂移特性

设计了带缠裹式防热套的柔性接头,弹性件和防热套材料均采用硅橡胶.研究了柔性接头有效摆心和几何球心的关系,采用2阶四项式Mooney-Rivlin模型模拟弹性件的本构关系,利用ANSYS软件分别仿真计算柔性接头在压强为0,9MPa下不同摆角条件的有效摆心和几何球心漂移,得到了两者的漂移包络线,把仿真的有效摆心漂移结果与试验测量值进行比较,并利用间隙碰撞试验验证了几何球心漂移仿真结果的准确性,在此基础上研究了有效摆心漂移的原因.结果表明:摆心包络线的仿真结果与试验结果吻合较好,有效摆心和几何球心是两个不同的概念,柔性接头的有效摆心漂移在半径为2.5mm,高为1.4mm的圆柱包络面内,而几何球心的漂移在半径为0.013mm,高为0.6mm的圆柱包络面内,有效摆心漂移是由接头各层增强件和弹性件的变形不同引起的.