Electrolytic Passivation of Nitinol Shape Memory Alloy in Different Electrolytes

The corrosion behavior of the nitinol alloy was studied in various corrosion media of different Cl–ion concentrations. The results demonstrate that the Cl–ion concentration has significant influences on the corrosion behavior of the nitinol alloy. In order to enhance the corrosion resistance, protective films were generated on the surface of the nitinol alloy by means of the electrochemical passivation method, for which five different electrolytic solutions were investigated. The surface analysis indicates full growth of all samples pas-sivated in the different electrolytic solutions with layers, however, showing different morphological features. Without any defects like micro-cracks and pores, the surface of the samples passivated in the molybdate solution turns out smoother and denser than those pas-sivated in other solutions. It is shown that the electro-chemical passivation will reduce Ni content but increase Ti content in the surface, reaching the Mole ratio of Ti:Ni=9.01:1 on the outermost surface. Potentiodynamic polarization test demonstrates that the samples electrochemically passivated in the molybdate solution present a significant increase in breakdown potential due to titanium enrichment on the outermost surface.     

硅橡胶基防热涂层高温压缩行为

为研究硅橡胶基防热涂层高温下的力学性能,针对两种硅橡胶基防热涂层开展高温压缩试验,对其截面的宏观及微观形貌进行分析,并结合高温下的热失重分析,探讨了其高温压缩强度变化规律及机理。研究结果表明:甲基苯基硅橡胶涂层高温热解温度区间主要为500～650℃,最终质量残余率为67.61%,其高温压缩强度在25～800℃呈增加趋势,由于玻璃小球的软化及树脂基体的热解,导致在400及700℃两个温度点的压缩强度降低,但在800℃由于玻璃小球与涂层中填料、烧蚀产物等发生共融,使涂层力学性能显著增加。甲基乙烯基硅橡胶涂层的高温热解温度区间主要为450～800℃,最终质量残余率为89.95%,由于甲基乙烯基硅橡胶涂层在高温热解后产生的陶瓷相,弥补了树脂裂解所带来的强度下降,因此在25～800℃其高温压缩强度较为稳定,并未产生明显衰减。影响硅橡胶基防热涂层高温力学性能的因素主要包括树脂基体的热解以及填料在高温下发生的物理-化学变化。     

氧化层非均匀增长对热障涂层应力分布的影响

利用扫描电镜对不同氧化程度的热障涂层(TBCs)进行观察,分析发现热生长氧化层(TGO)各部位并非均匀增长。假设热生长氧化层的形状为正弦曲线,用统计方法处理扫描电镜图片可以得到热生长氧化层的基本几何参数。由此建立单波形二维轴对称有限元模型,计算并分析了非均匀增长模型的应力状况。结果表明:相同温度下,非均匀增长模型的轴向、剪切和Mises应力分量的变化趋势与均匀增长模型的对应趋势一致;但是非均匀增长模型的各个应力分量最大值均小于均匀增长模型的应力分量最大值。      

划痕法表征TD处理制备的VC涂层界面结合强度

 为了测定碳化钒(VC)涂层与基体之间的结合强度,分析涂层与基体的结合机制,采用热扩散(TD)处理在冷作模具钢Cr12MoV表面制备了VC涂层,通过扫描电镜(SEM)观察了其表面与界面形貌,利用能谱议(EDS)分析了结合界面的V、C元素的分布,用划痕法测定了涂层与基体的界面结合强度,并对涂层失效机理进行了分析.结果表明,经TD处理制备的VC涂层与基体结合界面为成分梯度界面,二者结合面为成分含量呈梯度变化的过渡层,V元素含量从表面到基体逐渐下降,而C元素含量逐渐上升;其结合界面处化学元素相互结合,形成冶金结合,测得涂层与基体的结合强度平均值为45.7 N;涂层失效形式为界面层的压裂,其结合强度主要与VC涂层残余压应力有关.     

热障涂层喷涂质量微焦点CT检测

采用微焦点X射线源对热障涂层样品进行了高分辨率X射线成像研究,采用多尺度对比度增强算法提高了热障涂层与基体之间的对比度.X射线图像显示热障涂层各处厚度差异较大,热障涂层内部可能存在大量孔隙.通过微焦点计算机层析成像(CT)对样品进行了高分辨率CT扫描与重建,得到了样品的CT重建图像.从热障涂层CT图像观察到热障涂层内部存在大量孔隙,且不同层孔隙尺寸、数量不同.结合3个坐标方向的切片图像分析了热障涂层深度方向的热障涂层厚度,得到了热障涂层厚度的二维分布,测量得到热障涂层平均厚度约为40μm.对沿热障涂层深度方向850~1131层切片图像,利用可视化软件VGstudio MAX得到了热障涂层内部孔隙三维分布.研究结果表明:微焦点CT可用于热障涂层制备工艺质量检测.      

飞机典型结构件防护涂层耐腐蚀试验对比研究

基于2种涂层的飞机典型结构模拟试验件加速腐蚀及老化试验,得到涂层光泽度和色差随加速腐蚀时间的变化规律。利用灰色关联分析方法,对影响涂层腐蚀损伤的9个评定指标进行量化比较,计算出2种涂层防护体系评价指标与参考标准之间的关联度大小,并对2种涂层防护体系进行了综合评定。结果表明,2种涂层光泽度和色差变化均随加速腐蚀时间增加而增大,TB06-9涂层较H06-076涂层变化更明显,H06-076涂层的防护效果优于TB06-9涂层。     

脉冲风洞热喷流实验方法初步研究

发动机燃气喷流对高超声速飞行器后体气动热环境有显著的影响,燃气喷流的物理模型对预测飞行器局部热环境有显著影响,为了利用脉冲风洞研究这类影响规律,研制了一套瞬态热喷流供气系统,建立了瞬态热喷流供气系统的工作方法。该系统的核心技术是利用氢氧燃烧驱动路德维希管（Ludwiegtube）,提供瞬态热喷流气源。本研究包括以下内容：不同氢氧比例对燃烧产物热力学状态及产生方式的影响;不同点火、破膜方式对气源产生及喷流流场稳定性的影响。本研究提出的热喷流供气系统可以提供满足缩比模型喷流实验所需喷流状态的热气源;可以在50ms内起动工作,满足与脉冲风洞同步工作的要求。     

DSM11镍基高温合金表面三种涂层高温性能

DSM11镍基高温合金表面制备Al-Si、Al和Co-Al三种涂层,研究三种涂层在900℃下的涂盐（质量分数为5% NaCl+95% Na₂SO₄）热腐蚀性能和800℃下的疲劳性能。实验结果表明:在900℃热腐蚀200h后,Al-Si涂层和Co-Al涂层表面腐蚀区均形成了以Al₂O₃为主的连续且致密的氧化层,抑制热腐蚀反应的进行,具有一定的抗热腐蚀性能;Al涂层表面腐蚀区形成了混合型氧化层,热腐蚀反应会持续进行,抗热腐蚀性能较差。在800℃的疲劳实验后,Al-Si涂层表面生成大量的微裂纹,涂层容易发生开裂,进而引起合金试样快速断裂;Co-Al涂层和Al涂层的合金试样表现较好的抗高温疲劳性能。在高温合金的防护涂层使用中,要充分考虑到涂层的服役环境,对相关性能进行综合评价,选出最适合的防护涂层。      

高温吸波涂层的多目标优化模型设计

大多数高温吸波材料都属于非磁损耗型,单层往往很难达到理想的吸波性能.为解决此问题并优化涂层厚度,通过差分进化算法建立了多层高温吸波涂层的多目标优化模型,重点以8.2～12.4 GHz内反射率RL＜-10 dB频率带宽和涂层总厚度d为优化目标.设定三种高温吸波材料,研究表明,单层涂层很难达到理想的吸波性能;在单目标优化中...     

TGO非均匀增长对热障涂层应力演化和破坏机理的影响

采用内聚力模型和热生长氧化层(TGO)非均匀增长子程序,数值模拟了在热循环载荷作用下热障涂层(TBC)内部应力演化规律和开裂行为。涂层失效过程首先是源自陶瓷层(TC)内近波峰位置的拉伸和切应力共同主导的陶瓷层Ⅰ、陶瓷层Ⅱ混合型裂纹;随着循环数增加,则转向由TC内近波峰位置的切应力主导的Ⅱ型裂纹和波峰波谷中间的涂层厚度方向拉伸应力主导的Ⅰ型裂纹。整体非均匀增长和波谷均匀增长模式下的最大拉伸应力经过一定循环数后几乎不再随循环数而增加;而在波峰均匀增长和整体均匀增长模式下,最大拉伸应力则会随着循环数增加持续增长。整体非均匀增长、波谷非均匀增长模式下,20个循环后最大切应力出现在近波峰位置,分别为-16241 MPa和-15428 MPa;而整体波峰均匀增长和整体均匀增长模式下,最大切应力为-11382 MPa和-11198 MPa。对于波谷均匀增长和整体非均匀增长模式,在9个循环后出现界面裂纹。而对于波峰均匀增长和整体非均匀增长模式,在第17个循环出现界面裂纹。