装配间隙对顶盖环缝搅拌摩擦焊焊接质量的影响

结合超声波相控阵、金相观察、力学试验分析技术,研究了由于铣切角度不同产生的装配间隙对顶盖环缝搅拌摩擦焊焊缝质量及力学性能的影响。结果显示当铣切角差异带来的装配间隙大于1.30 mm时,焊缝中存在孔洞型体积缺陷,装配间隙越大,缺陷越严重;装配间隙的存在会使得焊缝的致密程度降低,焊缝的延伸率下降,并且在装配间隙大于1.30 mm时,焊缝的抗拉强度会发生大幅度地下降。     

摩擦焊设备振动油缸的性能分析

液压式摩擦焊设备是将电液伺服控制技术运用到摩擦焊接领域的一种先进设备。通过分析系统振动油缸的频率,找出影响频率的关键因素,深入分析这些因素对振动油缸伺服控制系统的影响,并利用AMESim仿真软件对该系统进行建模分析,验证了分析结果,并总结出改进系统的几点措施,为摩擦焊设备的设计改进提供了理论依据。。     

推进剂贮箱金属焊接件疲劳裂纹对应力强度因子影响的数值分析

卫星推进剂贮箱的焊接质量直接影响卫星的寿命和可靠性。文章通过仿真分析研究焊接残余应力对贮箱上已存在裂纹的影响。首先针对球壳模型和平板模型分别计算焊接残余应力,然后在应力强度值最大的危险区域引入裂纹,对不同角度和尺寸系数的裂纹对应力强度因子影响的数值和变化趋势进行分析。研究表明：起主要作用的是应力强度因子KI;KII受角度影响相对较大;KI和KII的最小值都在裂纹中心处;KIII基本随归一化裂纹前沿数值增加而增加。     

Impact of bending dies with different friction forms on forming force and quality of tubes manufactured by free bending technology

In the 3D free bending forming system, the bending die can be designed either in a sliding type or rolling friction type. Bending die-based sliding friction type is often called normal bending dies; however, the bending dies-based rolling friction type includes bending die-based roller type and ball type in structure. In the current study, the impact of three bending dies on the forming force, and the bent tube quality was investigated. The obtained results showed that the tangential stresses and strains of the tubes formed by the bending die-based roller type were the smallest among the three bending dies. Besides, the spherical bearing force P_U was reduced drastically after using the roller type and ball type compared to the sliding friction type. Moreover, the uniformity of the wall thickness distribution of the tubes formed by the roller type and ball type was better than those obtained from the sliding friction type. In addition, the cross-section distortion rate was reduced by 2.8% using the roller type, and 1.8% using ball-type compared to the sliding friction type.     

AZ31B变形镁合金激光-MIG复合焊焊接组织和性能分析

采用激光-MIC复合焊对10mm厚的AZ31B变形镁合金进行焊接.利用光学显微镜、扫描电镜、X射线衍射仪等手段分析了焊接接头的外观和截面特征、显微组织、元素分布、焊缝物相和断口形貌等,并检测了接头区域硬度和接头强度.试验结果表明:采用激光-MIG复合焊能获得成形美观的焊缝,无明显的缺陷;焊缝热影响最大宽度位于激光区,约为100μm,焊缝组织为15～25μm的等轴晶粒;相比于母材,焊缝区的镁元素出现烧损,铝和锰元素的比例有一定增加;焊缝区主要为Mg,Al和少量的MgO相.焊接接头硬度值较均匀;焊缝抗拉强度达到222MPa,断口形貌为混合断裂断口.     

G105钻杆摩擦焊接头的断裂韧度和组织性能

G105钻杆的工具接头和管体采用摩擦方式进行焊接,对摩擦焊接头进行了适当热处理.对钻杆工具接头、管体、焊合区三点弯曲试样的断裂韧度进行了测试,分析了弯曲试样的微观组织和断裂形貌以及接头焊合区韧性损伤的原因.     

活性剂等离子弧焊焊接电弧与电弧力

 针对活性剂等离子弧焊焊接过程,对焊接电弧外形的变化,焊接电弧力与活性剂之间的关系进行了研究,并建立了活性剂等离子弧焊焊接电弧轴向压强模型。研究结果表明:活性剂等离子弧焊焊接电弧收缩,弧尾翼消失,尾焰加大,电弧穿透力增强,电弧电压升高;活性剂等离子弧焊焊接电弧的温度分布比较紧凑,温度场外形窄,温度分布范围较集中,电弧径向温度梯度较大;活性剂等离子弧焊焊接电弧力的分布半径减小,压力峰值增大。     

Morphology and Frictional Characteristics Under Electrical Currents of Al203/Cu Composites Prepared by Internal Oxidation

Two AhO3/Cu composites containing 0.24 wt.% A1203 and 0.60 wt.% A1203 separately are prepared by internal oxidation.Effectsof sliding speed and pressure on the fi-ictional characteristics of the composites and copper against brass are investigated and compared.The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope (SEM) and energy dispersive X-ray spectrum (EDS).The results show that the wear resistance of the AI203/Cu composites is superior to that of copperunder the same conditions.Under a given electrical current,the wear rate of AI203/Cu composites decreases as the AleO3-content increases.However,the wear rates of the Al203/Cu composites and copper increase as the sliding speed and pressure increase under drysliding condition.The main wear mechanisms for AleO3/Cu composites are of abrasion and adhesion;for copper,it is adhesion,although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.     

Stability analysis of an aeroelastic system with friction

In this paper, harmonic balance method, exact formulation and numerical simulation method are adopted to study the effects of different friction stiffness on the stability of 1.5 degrees of freedom aeroelastic system. On this basis, the expressions of input energy and dissipated energy are deduced, and the energy method is used to reveal the mechanisms of the stable boundary and unstable boundary existing in the system and the effects of different friction stiffness on the stability of the system. Studies have shown that the stability region and the critical aerodynamic damping ratio of the system rise with the increase of the friction stiffness, while the friction stiffness has little effect on the stability boundary. In the analysis of the stability of system, the results of harmonic balance method, exact formulation and Newmark of numerical simulation method are in good agreement. Compared with exact formulation and numerical simulation method, the concept and conclusion of harmonic balance method are simple in the system stability analysis.     

GH4169高温合金惯性摩擦焊接头动态再结晶过程

当温度、应变、应变速率达到一定条件时 ,GH4 16 9镍基高温合金在惯性摩擦焊接过程中易发生动态再结晶。本文研究结果表明 ,由于GH4 16 9合金惯性摩擦焊接时间很短 ,动态再结晶进行得相当充分 ,而动态回复不足 ,在动态再结晶的过程中还可以看到有些结晶过程还处于形核阶段 ,这是惯性摩擦焊接头产生细晶乃至超细晶的根本原因