This article deals with time-averaged coolant diffusion equation in arbitrary, body-fitted coordinates. Schmidt number and Lewis number are used to obtain the mass diffusion coefficient. Other than the existing N-S solver, a new solver for the diffusion equation and the influences of cooling air on the thermal parameters, such as gas constant, constant-pressure specific heat, is established. Capable of simulating the flow of multi component fluid, this solver is used to simulate the flow in air-cooled two-stage turbines. The comparison of test results from the modified solver to those from the traditional N-S solver has evidenced that a marked difference present is in thermal parameters and flow field structure.     

TC4钛合金扩散焊接头的力学性能

在温度为910℃,压力为3.4MPa条件下对TC4钛合金板材进行了扩散焊接,对获得的扩散焊接头取样进行金相观察,仅在接近接头表面材料深度为1mm范围内发现未焊合缺陷,其余部分焊合较好,表明在给定工艺下可获得质量良好的焊接头.随后对TC4扩散焊接头的力学性能进行了试验研究,分别开展了静拉伸试验、断裂韧性试验及焊缝附近区域的纳米压痕试验.试验结果表明,所制得的TC4扩散焊接头屈服强度为887MPa,抗拉强度为948MPa,断裂韧性为101.9MPa·m1/2,均与原材料的性能相差不大.纳米压痕试验的结果显示,接头焊缝区和母材区的显微弹性模量分别为180.2GPa和178.0GPa.      

Large eddy simulation of turbulent diffusion flame combustion using a conserved scalar methodology

The present paper describes an LES prediction of turbulent diffusion flame combustion in a simplified axi-symmetric combustor geometry.The calculations are carried out using a well-tested finite volume incompressible LES code which has been modified to handle variable density and reacting flows.The basic mixture fraction conserved scalar method is used with the chemical state relationships described by fast chemistry.The turbulence-chemistry interaction is modelled by a sub-grid PDF method and the PDF is assumed to follow a Beta-function shape.The LES predictions have been time-averaged over 3.5 flow-through times to generate the mean radial profiles of mixture fraction,product mass fraction,temperature,axial velocity and axial rms.The agreement of the LES predictions with the experimental data is good for all the above quantities at four different axial positions with largest differences at the first measurement plane.The LES method also provides information on the unsteady nature of turbulent diffusion combustion. For turbulent reacting flows with large density ratio,it was found necessary to use a relaxation method in order to remove unphysical high-frequency fluctuations and to maintain numerical stability.      

一种制备C/C复合材料的高效等温ICVI工艺

将传统的负压等温化学气相渗透(ICVI)工艺加以改进,在常压条件下以丙烯为气态前驱体,氮气为稀释气体,通过定向扩散和控制滞留时间,经 100h沉积后制备出密度为 1 72g/cm3 的 C/C复合材料。该方法克服了传统等温CVI工艺致密化速率较慢的问题,提高了致密化效率,有利于降低C/C复合材料的制备成本。     

中热值合成气扩散燃烧速度特性的实验研究

针对CH4和中热值合成气的旋流燃烧室进行了PIV测量,获得了不同燃料燃烧对火焰流场变化的影响.实验结果表明:在相同入口条件下,合成气燃烧时的火焰张角略大,回流区宽度和回流强度均高于CH4火焰,燃气流量较低时,合成气火焰的湍流强度更大,燃气流量增大后,CH4的燃烧脉动速度逐渐增大并超过合成气.     

扩散处理对K403铸造高温合金大间隙钎焊接头组织和力学性能的影响

研究采用自制钎料加入FGH95高温合金粉末的K403铸造高温合金大间隙钎焊后扩散处理参数对接头组织和持久性能的影响.结果表明,钎焊后进行温度1180℃,32h的扩散处理,钎缝化学成分及组织均匀,钎缝基体组织为γ固溶体,占体积50%～53%的γ′相均匀分布.骨架状硼化物化合物消除,少量小块和粒状碳化物和硼化物分布在晶界上.钎焊接头975℃的持久强度较高.     

Ni_3Al基合金TLP扩散焊接头性能

介绍Ni3Al基IC10合金孔P扩散焊后接头性能,以及长时间使用后接头性能的变化,分析认为孔P扩散焊接头在高温使用过程中,原子进一步扩散,接头性能变得和基体相同.     

脉冲加压扩散连接工艺参数对钛合金与不锈钢接头强度的影响

采用脉冲加压扩散连接工艺对TA17钛合金与0Cr18Ni9Ti不锈钢进行了连接试验.利用液压万能试验机测试了接头拉伸强度,分析了脉冲加压扩散连接工艺参数对接头强度的影响.结果表明:当连接温度为1098K、脉冲最小压力Pmin=8MPa、脉冲最大压力Pmax=50MPa、脉冲次数为20次、脉冲频率为0.5Hz时,加热速度vh=30K/s,冷却温度vc=5K/s,得到最高的接头拉伸强度为293MPa,连接所用的有效时间仅为220s,实现了钛合金与不锈钢的高效良好连接.利用X射线衍射(XRD)及扫描电镜(SEM)分析了接头组成相及断口形貌,接头界面主要存在β-钛、Fe2Ti,FeTi,拉伸试验中β-钛的固溶体承担了主要的拉伸力.     

Nb／α-Ti Al体系的互扩散行为

采用反应扩散偶的方法,研究了Nb元素在a-Ti3 Al中的扩散行为.反应扩散偶经过120 h扩散退火,在高温（1 573 K）下生成了均匀的阶（ Ti , Nb）扩散层;低温（1273,1 423 K）下生成不均匀的扩散区,相组成为Ti3Al（ Nb） ,β-（Ti , Nb）及Nb2Al.采用Dayananda方法计算了体系的扩散系数,即根据一个扩散偶的浓度分布曲线计算体系的扩散系数.采用平均扩散系数来表征体系的扩散系数,得出扩散模型和相关扩散机理.结果表明：Ti和A1的主扩散系数比Nb的主扩散系数大5个数量级;Ti的主扩散系数是Al的2倍.Nb通过占据Ti的空位进行扩散,Nb的掺入阻碍了Ti元素扩散,从而提高了a-Tip A1体系的高温抗氧化性能     

冲击位置对斜搭接接头冲击后拉伸性能的影响

低速冲击损伤对复合材料胶接结构的力学性能存在威胁。对在搭接区域3个不同位置承受低速冲击的斜搭接接头进行冲击后拉伸试验,并分别建立胶接接头冲击及冲击后拉伸有限元模型。试验结果表明:冲击位置在搭接区尖端背侧,造成的凹坑深度最大,冲击后拉伸强度最低;冲击位置在搭接区中部,凹坑深度最小,冲击后拉伸强度最大;冲击位置在搭接区尖端侧,凹坑深度及冲击后拉伸强度居中。有限元分析结果表明胶层损伤和复合材料纤维损伤的大范围扩展是导致结构失效的主要原因。