基于小裂纹的2024-T3铝合金中心孔试样疲劳寿命预测

对2024-T3铝合金板材中心孔试样进行了疲劳裂纹扩展行为及寿命预测的理论和试验研究.采用疲劳条带与显微镜观测相结合的办法获得试样在块谱作用下孔边自然萌生裂纹扩展的α-N数据,并通过对断口的SEM观察获取试样的初始缺陷形状.利用基于裂纹闭合的小裂纹扩展分析程序FASTRAN3.9对试样α-N数据进行反推,建立了描述孔边裂纹细节原始疲劳质量的当量初始缺陷尺寸(EIFS)分布.以该分布为基础,采用FASTRAN3.9对试样进行了恒幅载荷下试样的中值疲劳S-N曲线的预测,预测结果与试验验证结果吻合较好.     

某型发动机轴流叶轮疲劳寿命分析

为准确了解某型发动机的关键零部件——轴流叶轮的使用寿命,进而提高其可靠性,分析了该轴流叶轮的痧劳寿命,并通过疲劳寿命试验进行了验证．研究结果为轴流叶轮的定寿和延寿提供了重要依据。     

中性盐雾预腐蚀对AF1410高强钢疲劳寿命的影响

采用失重法和XRD法研究了AF1410钢在中性盐雾环境中的耐蚀性能,并对中性盐雾预腐蚀不同时间后的试样进行疲劳性能测试,研究了不同预腐蚀时间对材料疲劳寿命的影响。结果表明:AF1410钢发生了严重的全面腐蚀,腐蚀产物主要由FeO(OH)和Fe3O4组成,并得到其腐蚀失重曲线;疲劳断口形貌分析表明,随预腐蚀时间的延长,腐蚀损伤程度增加,在疲劳加载过程中易形成较多的疲劳裂纹扩展源而导致疲劳断裂失效;最终获得中性盐雾预腐蚀AF1410钢结构疲劳寿命特性以及预腐蚀对疲劳寿命的影响系数C(t)曲线。     

基于EMD熵特征融合的滚动轴承故障诊断方法

研究了滚动轴承故障诊断单一故障信号的局限性和故障特征的非线性,从信息融合的理论出发,利用非线性动力学参数熵作为特征,提出了基于经验模态分解(EMD)熵特征融合的方法来解决滚动轴承故障诊断问题.首先将原始信号进行EMD,利用EMD的自适应多分辨率的特点计算EMD得到的固有模态函数(IMF)信号的多种熵值,然后采用核主元分析(KPCA)对提取的状态特征进行信息融合,从而得到互补的特征,最后将提取的融合特征通过支持向量机(SVM)进行故障诊断.滚动轴承故障诊断实验表明:该方法结合了EMD、信息熵理论和KPCA强大的非线性处理能力的特点,可以进行滚动轴承故障诊断.      

层合板螺栓连接结构疲劳寿命预测

为了准确预测复合材料连接结构损伤的产生和扩展,基于单向板疲劳性能预测层合板螺栓连接结构疲劳寿命。用T300/BMP-316单向板试验数据对正则化疲劳寿命与剩余强度的参数进行拟合;在复合材料基体主控失效判据基础上增加纤维失效和分层失效判据,改进基于断裂韧性的失效准则判定损伤的产生和扩展;采用二级载荷疲劳寿命等效实现损伤的非线性累积,再对相应的损伤进行材料性能退化。预测结果与试验对比表明:对不同几何参数层合板连接结构的对数寿命预测与试验误差在5%以内,对不同应力水平下层合板连接结构的对数寿命预测与试验误差在10%以内,最终破坏模式及损伤区域的预测与试验结果吻合良好。     

A100钢外螺纹椭圆超声滚压强化试验研究

A100钢有较高的疲劳抗力和显著的减重效果.在航空工业中,飞机起落架主要承力件正逐步采用A100钢,且主要承力件多采用螺纹联接.为了提高螺纹疲劳寿命,提出了超声振动滚压强化工艺方法,设计了外螺纹超声滚压强化装置,进行了螺纹超声滚压强化前后性能对比试验.利用X射线分析仪、维式硬度计、粗糙度仪和疲劳试验机,分别测量了螺纹超声滚压强化前后的残余应力、维氏硬度、表面粗糙度以及疲劳寿命.结果表明,超声滚压强化后牙底残余应力提高了70％,显微硬度提高了14％,粗糙度降低了51％,600MPa应力条件下寿命提高了5倍.     

国外飞机机轮刹车系统的发展

阐述了航空机轮刹车系统最新的研究方向包括吸收能量更多并且更耐磨损的高密度碳材料,寻求更轻更强的结构部件材料,提升设计方法以优化刹车性能,机轮刹车系统的结构动力学研究,更大范围的电刹车装置和电刹车控制系统研究等。     

Remaining useful life estimation for deteriorating systems with time-varying operational conditions and condition-specific failure zones

Dynamic time-varying operational conditions pose great challenge to the estimation of system remaining useful life (RUL) for the deteriorating systems. This paper presents a method based on probabilistic and stochastic approaches to estimate system RUL for periodically moni-tored degradation processes with dynamic time-varying operational conditions and condition-specific failure zones. The method assumes that the degradation rate is influenced by specific oper-ational condition and moreover, the transition between different operational conditions plays the most important role in affecting the degradation process. These operational conditions are assumed to evolve as a discrete-time Markov chain (DTMC). The failure thresholds are also determined by specific operational conditions and described as different failure zones. The 2008 PHM Conference Challenge Data is utilized to illustrate our method, which contains mass sensory signals related to the degradation process of a commercial turbofan engine. The RUL estimation method using the sensor measurements of a single sensor was first developed, and then multiple vital sensors were selected through a particular optimization procedure in order to increase the prediction accuracy. The effectiveness and advantages of the proposed method are presented in a comparison with exist-ing methods for the same dataset.     

200N·m·s控制力矩陀螺用圆柱型导电环寿命试验

导电环用于200N·m·s控制力矩陀螺高速转子电信号的传输,其使用寿命直接决定了200N·m·s控制力矩陀螺整机寿命,因此需要对200N·m·s控制力矩陀螺用导电环进行加速寿命试验.对试验目的、试验对象、加速因子、试验环境、试验系统组成、失效判据进行了详细描述,对导电环寿命试验期间的电噪声、摩擦力矩、绝缘性能等测试结果进行的分析表明,在进行了4×106转的寿命试验后,导电环的各项性能指标仍能够满足200N·m·s控制力矩陀螺的使用需求.