本文以Al-50wt%Si高硅铝合金为研究对象，采用单因素试验方法进行无涂层硬质合金刀具干式铣削试验，分析切削参数对刀具磨损和表面粗糙度的影响。结果表明：表面粗糙度受每齿进给量的影响最显著，随每齿进给量的增加而增加，当每齿进给量从0.07 mm/z增加到0.16 mm/z时，表面粗糙度增加2倍；刀具磨损受切削速度的影响最显著，随切削速度的增加而增加，当切削速度从140 m/min增加到260 m/min时，切削总长度降低3倍，而刀具后刀面磨损量仅是260 m/min速度下的0.8倍；表面粗糙度随刀具磨损的增加呈现先增加后降低的变化趋势，切削长度从350 mm增加到1 750 mm，刀具磨损量平均增加4.5倍，而表面粗糙度却下降2倍；硬质合金刀具主要的磨损形式为磨粒磨损、崩刃。     

Effects of surface topography and specimen thickness on high-speed raindrop impact damage of CFRP laminates

Raindrop impact erosion has been observed since early days of aviation, and can be catastrophic for exposed materials during supersonic flight. A single impact waterjet apparatus is established for mimicking drop impacts at the velocities between 350 m/s and 620 m/s. Carbon Fiber Reinforced Polymer(CFRP) laminates with three different surface morphologies and specimen thicknesses are tested here. A central region with no visible damage has been noticed, surrounded by a “failure ring” with common...