We review aspects of anomalous cosmic rays (ACRs) that bear on the solar modulation of energetic particles in the heliosphere. We show that the latitudinal and radial gradients of these particles exhibit a 22-year periodicity in concert with the reversal of the Sun's magnetic field. The power-law index of the low energy portion of the energy spectrum of ACRs at the shock in 1996 appears to be -1.3, suggesting that the strength of the solar wind termination shock at the helioequatorial plane is relatively weak, with s 2.8. The rigidity dependence of the perpendicular interplanetary mean free path in the outer heliosphere for particles with rigidities between 0.2 and 0.7 GV varies approximately as R2, where R is particle rigidity. There is evidence that ACR oxygen is primarily multiply charged above 20 MeV/nuc and primarily singly-charged below 16 MeV/nuc. The location of the termination shock was at 65 AU in 1987 and 85 AU in 1994.     

激光选区熔化成形Ti6Al4V合金的热处理组织演变机理

激光选区熔化(SLM)Ti6Al4V成形构件需要通过热处理改善其塑性。为探究该过程中的组织特征和演变机理,研究了Ti6Al4V试样固溶时效热处理(910℃/8 h水冷,750℃/4 h炉冷)前后的微观形貌和力学性能。结果表明:沉积态的马氏体α′相尺寸具有层次结构;热处理相变时初生马氏体α′发生分解,小尺寸马氏体α′转变为β相,随后发生β→(α+β)转变,最后得到α相片层和精细(α+β)相结构均匀分布的组织;热处理后材料抗拉强度达1 055 MPa,延伸率提升至16.2%,均优于典型Ti6Al4V合金拉伸性能。采取的热处理技术对Ti6Al4V组织调控成效显著,满足后续工艺要求,可在激光选区熔化成形双相钛合金中推广应用。     

双向应力状态下IC10高温合金的屈服行为研究

 为了研究Ni₃Al基金属间化合物IC10高温合金的屈服行为,对其进行了不同加载路径下的双向拉伸试验.试验采用十字形双向拉伸试验件在Zwick/Roell Z010双向拉伸试验机上进行,得到的最大等效应变为0.02.试验加载方向与材料塑性各向异性主轴重合,采用位移控制方法让两个夹头的加载速率比保持不变,得到不同线性加载路径下的应力-应变曲线.根据单位体积塑性功相等原理获得了IC10合金在双向拉伸应力状态下的屈服轨迹,并与目前常用的几种正交各向异性屈服准则及von Mises屈服准则预测结果进行了对比.结果表明,IC10合金的试验屈服轨迹呈外凸性,以双向等拉线为界的上下部分屈服轨迹不对称,显示出明显的塑性各向异性.各向同性von Mises 屈服准则只包含一个材料常数,无法描述IC10合金的塑性各向异性行为;Hill 二次式屈服准则在双向等拉应力状态附近低估了材料的屈服强度;Logan &; Hosford屈服准则在从双向等拉到横向单拉的应力状态下都低估了材料的屈服强度,与试验结果相差较大.Banabic-Balan屈服准则和Barlat (1989) 屈服准则的预测值与试验结果吻合很好,能很好地描述IC10合金在双向应力状态下的屈服行为.     

16Co14Ni10Cr2Mo钢力学性能与应力腐蚀行为

研究了１６Ｃｏ１４Ｎｉ１０Ｃｒ２Ｍｏ钢不同温度回火５ｈ强度、冲击韧性、断裂韧性和应力腐蚀性能（在３．５％ＮａＣｌ水溶液中）。在５１０℃回火可以获得较高的强度，最高的断裂韧性及抗应力腐蚀性能，此时Ｋ＿（ＩＳＣＣ）可达，Ｋ＿（ＩＣ）为，屈服强度为１５８０ＭＰａ。应力腐蚀性能（ＳＣＣ）的改善主要与在较高温度回火，使Ｍｏ＿２Ｃ共格造成的应力下降，位错亚结构的恢复及碳化物的粗化，并导致氢的偏聚下降有关。     

Ti-51.8at%Ni形状记忆合金中Ti_3Ni_4相的析出过程

 用透射电镜系统地研究了Ti-51.8at％Ni形状记忆合金在300～600℃时效时Ti_3Ni_4相的析出过程。结果表明:Ti_3Ni_4相以均匀成核方式从过饱和基体中弥散析出。时效初期,Ti_3Ni_4相为细小颗粒状;随时效时间延长或时效温度升高,Ti_3Ni_4相逐渐长大为透镜片状,最终粗化为粗片状。Ti_3Ni_4相通常与基体保持良好的共格关系,其共格应变场衬度随Ti_3Ni_4相尺寸增大而变化,至Ti_3Ni_4相聚集粗化后,与基体的共格关系逐渐丧失,并在其周围基体中产生位错,位错的柏氏矢量为1/2(111)_(B2)或1/2(111)_(B2)。     

TC4钛合金与多层TiN/Ti涂层的砂尘冲蚀损伤试验

建了砂尘冲蚀试验系统,采用粒子成像测速方法获得了气体压力和砂尘速度之间的关系,并在砂尘质量浓度为28.91g/m3,速度为80m/s,冲蚀角度为30°的条件下,对TC4钛合金和多层TiN/Ti涂层进行了冲蚀试验.结果表明:TC4钛合金抗冲蚀损伤能力较差,平均质量损失率达0.7mg/min.多层TiN/Ti涂层可承受砂尘冲蚀200min以上,且TiN/Ti调制比为1:3涂层的抗冲蚀能力优于调制比为1:1的涂层.砂尘粒子垂直冲击速度分量引起的微区剥落是涂层冲蚀损伤的主要原因,增加多层涂层韧性是提高其抗冲蚀性能的关键.      

IC10单晶高温合金室温和750℃高周疲劳行为

在涡轮叶片服役过程中,疲劳是其失效的重要原因之一,而已有研究主要针对不同应变速率下IC10合金1 100℃低周疲劳性能展开,本文研究定向凝固IC10单晶高温合金静态空气介质环境下室温和750℃高周疲劳性能。在应力比R=-1、f≈83.3Hz条件下,进行高周疲劳试验,并利用扫描电镜对疲劳断口进行观察;基于试验观测结果,讨论室温和750℃下IC10单晶高温合金高周疲劳性能差异的内在机制。结果表明:IC10单晶室温疲劳强度为288 MPa,750℃疲劳强度为416 MPa;裂纹萌生于试样表面或近表面缺陷处,断口主要由裂纹萌生区、稳态扩展区和组成。     

Ti2AlNb合金双层辉光等离子表面渗钼的扩散行为研究

Ti2AlNb合金(O相)具有高的比强度、断裂韧性以及优良的抗蠕变性能,因而在航空制造中成为一种颇具吸引力的高温结构材料.但是,较差的耐磨性是其主要的缺陷并限制其实际应用.为解决这一问题,对Ti2AlNb合金进行双层辉光等离子表面渗Mo.探讨主要工艺参数对Mo的扩散行为的影响.采用扫描电镜(SEM)、X射线衍射(XRD)和辉光放电光谱仪(GDS)分析表面合金化层的成分分布和微观结构.测定从表面到中心的显微硬度变化曲线.结果表明温度与时间均对扩散过程具有显著的影响.最后通过回归分析计算出在优化的工艺温度980℃下的扩散系数.     

Preparation and Microstructure of Cu/Ti_3SiC_2 Nanocomposite

Mixed micron-sized Cu/Ti3SiC2 (vol5%) powder was mechanically milled using agate balls and zirconia balls separately. Then followed an examination of it with the FEI-SEM. The experimental results show that, distributed homogenously in Cu matrix, the Ti3SiC2 particles have a size of about 30-50 nm after milled with agate balls for 8 h, while it remains approximately unchanged after milled with zirconia balls. The microstructure of the mixture at different ball-milling stages was also studied. Bulks of Cu/Ti3SiC2 nano-composite were fabricated by hot pressing nano-sized Cu/Ti3SiC2 powder at the temperature of 1 073 K under 100 MPa. Then came an investigation of the effects of the particle size and agglomerate state of Ti3SiC2 as well as the microstructure of Cu/Ti3SiC2 nano-composite. It was found that the nano-sized Ti3SiC2 particles distribute evenly in copper.     

Microstructure and Mechanical Properties of Cross-rolled Ti50Ni47Fe3 Shape Memory Alloy

The microstructures, the phase transformation characteristics, and the mechanical properties of the Ti50Ni47Fe3 alloy in as-forged and as-cross-rolled states were investigated. It is found that, after cross-rolling, the phase transformation temperature （Ms） of the alloy decreases drastically and the grains get refined. Moreover, its yield strength and fracture strength after cross-rolling hit 540 MPa and 687 MPa respectively, up by about 200 MPa over those in as-forged state.