铸型搅动细晶铸造与力学性能

对比研究了高温合金铸型搅动细晶铸造和普通铸造叶轮的力学性能。研究结果表明,细晶铸造显著提高了K418B合金叶轮的室温和高温拉伸以及中温持久性能,并大幅度改善了合金的低周疲劳性能。细晶铸造K418B整体叶轮650℃的低周疲劳寿命为普通铸造的3倍。     

耐热粉末铝合金成形工艺研究

为研制超音速飞行器所需的耐热铝合金管材 ,采用喷射沉积管坯→挤压成厚壁管材→旋压成薄壁管的成形工艺路线 ,旋压出Al - 8.5Fe - 1.3V - 1.7Si耐热粉末铝合金Φ内 15 3mm× 1.2mm× 5 40mm的小直径管材和Φ内 380mm× 2 .5mm× 114 0mm的大直径管材。大直径管材做成的模拟舱段通过了静强与静热联合试验     

A Novel Processing Route for Ni-doped Alumina Composites

Alumina-based composites containing 0-15wt% Ni metallic phase were produced by hot press-sintering Ni-coated alumina pow-ders. The Ni-coated alumina powders were prepared by the aqueous heterogeneous precipitation of alumina micro-powders and nickel sulfate salt followed by reduction process. The microstructural features and dispersion of Ni phase in Ni-coated alumina powders and the subsequent alumina-Ni cermets were investigated using scanning electron microscope (SEM), X-ray diffractometer (XRD), and trans-mission electron microscope (TEM). The relative density of the hot press-sintered composites was measured with the Archimedes’ method while the fracture strength and the fracture toughness were defined with the three-point bending method and the mi-cro-indentation fracture method. In the formation of alumina-Ni cermets from sintered Ni-coated alumina powders, Ni phase to some extent limits the densification rate and stifles the coarsening and growing process of alumina grains. The Ni phase is found to be located at the interfaces and the triple-joint junctions of alumina grains which results into alteration of the fracture mode of alumina and its in-creased fracture strength and fracture toughness if compared with monolithic alumina.     

直线式感应同步器360度鉴相技术的研究

本文论述了直线式感应同步器３６０°鉴相技术原理，硬件设计及软件编程方法。     

Metric radio bursts and fine structures observed on 17 January, 2005

A complex radio event was observed on January 17, 2005 with the radio-spectrograph ARTEMIS-IV, operating at Thermopylae, Greece; it was associated with an X3.8 SXR flare and two fast Halo CMEs in close succession. We present dynamic spectra of this event; the high time resolution (1/100 s) of the data in the 450–270 MHz range, makes possible the detection and analysis of the fine structure which this major radio event exhibits. The fine structure was found to match, almost, the comprehensive Ondrejov Catalogue which it refers to the spectral range 0.8–2 GHz, yet seems to produce similar fine structure with the metric range.     

高温热源羽流流场及伴生粉尘控制特性

采用CFD数值模拟软件对高温热源上部接受罩的羽流温度场和速度场进行分析,比较不同工况下上部伞形接受罩对高温烟气的控制特性,同时提出合理设置排风罩位置和风量的措施。     

混粉、常规电火花加工通用储液箱的研制

利用水力旋流器对固体颗粒的分级、分离功能,设计了一种既能用于常规电火花加工又能用于混 粉电火花镜面加工的通用型储液箱。     

Effects of Mo on the Microstructure and Hydrogen Sorption Properties of Ti-Mo Getters

The effects of Mo on the microstructure evolution, porosity and hydrogen sorption properties of Ti-Mo getters are investigated in this work. The results show that the addition of Mo prolongs the densification process of Ti-Mo getters and results in a significant amount of sintered pores. With the Mo content increasing, the porosity of getters firstly increases reaching the maximum value as it at- tains about 7.5wt.%, and then drops. At the room temperature, the hydrogen sorption property of getters increases progressively with the Mo content increasing, but the tendency is not very clear before its content lies below 2.5wt.%. When the Mo content achieves about 7.5wt.%, the hydrogen sorption property proves to be the best. The discussion is made about the above mentioned phenomena inclusive of hydrogen sorption properties of getters under different activation conditions (from 500-750 ℃).     

置氢钛合金粉末模压成形-烧结改性机理

采用置氢TC4钛合金粉末模压成形+保护气氛下烧结工艺,研究了置氢TC4合金粉末模压成形-烧结后合金的组织性能的变化规律,提出了采用置氢钛合金粉末成形与钛合金热氢处理技术相结合的新工艺路线制备合金.结果表明:随着置氢量的增加和烧结温度的升高,置氢TC4合金粉末模压成形烧结体致密度均呈逐渐增高趋势;烧结体组织由明显的魏氏体...     

聚酰亚胺复合材料的防辐射性能设计

以聚酰亚胺、氧化锆及金属铅粉为主要原材料,制备了聚酰亚胺基复合材料,并进行了X-射线衍射、紫外射线分析.结果表明,聚酰亚胺/氧化锆+金属铅复合材料比纯聚酰亚胺具有更好的X-射线防护性能,耐热性能仍然很好.