轻质隔热纳米孔结构耐烧蚀酚醛材料

在一定温度下,通过改性剂组分与热固性钡酚醛树脂之间热共聚反应,制备了改性酚醛树脂。采
用模压工艺制备出具有目标尺寸和形状的改性酚醛树脂固化物,对该样品分别进行了400 和700℃的炭化处
理,得到了相应的酚醛炭化样品,并测试其密度、失重率、收缩率等特征参数。研究改性剂用量对碳化物特征参
数和性能的影响,如密度、失重率形貌、比表面积、隔热性能、压缩强度等。SEM 研究表明,700℃炭化后样品形
成了“珊瑚状”碳结构,形成了30 ~150 nm 纳米孔。比表面积测试(BET)结果表明其比表面积可达464 m2 / g。
隔热性能与力学性能的测试结果表明,相对于未改性酚醛树脂碳化物,改性酚醛碳化物的热导率降低了
45． 57%,并且保持了较好的压缩强度。     

POSS 催化剂改性氰酸酯复合材料的性能

通过POSS 催化剂改性氰酸酯树脂,并采用热熔法排布制备了碳纤维/ 中温固化氰酸酯预浸料, 验证了改性氰酸酯的工艺性。同时考察了氰酸酯树脂及其复合材料的性能。结果表明, POSS 催化剂的加入, 降低了氰酸酯的固化温度,同时其使用温度、室温及-18℃的储存性能和复合材料力学性能与改性前相当。     

真空绝热板阻隔膜PA/ VMPET/ Al/ PE 热封工艺

真空绝热板阻隔膜PA/ VMPET/ Al/ PE 是一种多层复合阻隔膜,是真空绝热板的重要候选膜材。 通过实验研究了热封温度、时间、压力对其强度的影响,同时采用Matlab 软件对热封工艺参数进行优化,得出 最佳的热封工艺。利用DSC 对PA/ VMPET/ Al/ PE 进行热分析。实验结果表明:热封温度是影响热封强度的 最显著因素,当热封温度为160 ~170℃,热封时间为1. 0 ~2. 0 s,热封压力为0. 2 ~0. 4 MPa 时,热封边的热封 强度良好。Matlab 软件优化最佳热封工艺参数值为:热封温度167℃,热封时间1. 80 s,热封压力0. 34 MPa,该 模拟优化热封工艺参数与实验值一致。     

Performance of a small and low-cost chamber to simulate lunar surface environment

The performance of a small and low-cost metal chamber built to simulate the pressure and temperature conditions of lunar surface was assessed and the results are presented. This chamber is intended for studying the physical properties of lunar surface and subsurface (using soil simulants) and also to validate the technology readiness of certain newly developed payloads planned for future lunar surface missions (Lander/Rover). It is possible to reach down to ∼10⁻⁷ Pa under specific conditions and maintain the temperature of the sample under investigation to lunar day and night temperatures. The designed system has been subjected to various tests to evaluate its performance and suitability for carrying out experiments in a simulated lunar environment.     

Solar cycle and latitude dependence of high-beta suprathermal plasma conditions in interplanetary space between 1.3 and 5.4 AU

The analysis of energetic particles and magnetic field measurements from the Ulysses spacecraft has shown that in a series of events, the energy density contained in the suprathermal tail particle distribution is comparable to or larger than that of the magnetic field, creating conditions of high-beta plasma. In this work we analyze periods of high-beta suprathermal plasma occurrences (β_ep > 1) in interplanetary space, using the ratio (β_ep) of the energetic particle (20 keV to ∼5 MeV) and magnetic field energy densities from measurements covering the entire Ulysses mission lifetime (1990–2009) in order to reveal new or to reconfirm some recently defined interesting characteristics. The main key-results of the work are summarized as follows: (i) we verify that high-beta events are detected within well identified regions corresponding mainly to the vicinity of shock surfaces and magnetic structures, and associated with energetic particle intensity enhancements due to (a) reacceleration at shock-fronts and (b) unusually large magnetic field depressions. (ii) We define three considerable features for the high-beta events, concentrated on the next points: (a) there is an appreciable solar-activity influence on the high-beta events, during the maximum and middle solar-cycle phase, (b) the annual peak magnitude and the number of occurrences of high events are well correlated with the sunspot number, (c) the high-beta suprathermal plasma events present a spatial distribution in heliographic latitudes (HL) up to ∼±80°, and a specific important concentration on the low (−25° ? HL < −6°, 6° < HL ? 25°) and median (−45° ? HL < −25°, 25° < HL ? 45°) latitudes. We also reconfirm by a statistical analysis the results of Marhavilas and Sarris (2011), that the high-beta suprathermal plasma (β_ep > 1) events are characterized by a very large parameter β_ep (up to 1732.5), a great total duration (406 days) and a large percentage of the Ulysses-mission lifetime (which is equal to 6.34% of the total duration with usable measurements, and 11.3% of the duration in presence of suprathermal particles events).     

新型电工钢片磁性能无损检测传感器及应用

介绍了一种新型电工钢片磁性能无损检测传感器及其测量原理 ,同时讨论了该传感器的设计原则并给出了典型数据及仿真测试结果     

关于对喷水室热工计算公式的分析及修正

通过分析喷水室内水和空气之间的热质交换过程，指出目前采用的热工计算公式的不足，并在此基础上推导出喷水室热平衡方程新公式，对理论教学起到一定的指导作用。     

2. 5D 衍生结构SiO2 f / SiO2 复合材料的经向力学性能

以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。     

酚醛树脂炭的合成及力学性能研究

为了表征多孔炭泡沫材料基体的结构与力学性能,采用碱催化法制备热固性酚醛树脂,经固化、高温炭化处理合成多孔炭泡沫材料的基体——酚醛树脂炭。研究酚醛树脂炭的微观结构、压缩强度及压缩断裂韧性。结果表明:酚醛树脂炭结构以树脂炭基体、微孔和微裂纹为主,其碳元素以sp3杂化的非晶炭形式存在;压缩强度为8.58 MPa,压缩断裂特征为脆性断裂模式;酚醛树脂炭的压缩断裂韧性较差,断裂过程中吸收的总能量为0.135 MJ/m3。