采用热压缩试验研究了置氢量0.42%(质量分数)TC4钛合金粉末烧结材料在温度850～1000℃和应变速率0.001～0.10 s-1范围内的流变行为和组织演变,分析了该合金烧结材料在试验参数范围内变形的应力-应变曲线特征.动力学分析获得置氢TC4钛合金粉末烧结材料高温压缩变形的应力指数和变形激活能分别为3.97和50...     

钛基稀土激光熔覆层组织细化机制及性能

采用通快TruDisk 4002光纤激光器在TC4合金表面分别制备了0wt% Y₂O₃和3wt% Y₂O₃的TC4+Ni45+Co-WC钛基耐磨复合涂层。利用XRD、SEM、EDS、EPMA、显微硬度计和摩擦磨损试验机等分析了涂层组织、显微硬度和摩擦学性能。结果表明，两种涂层表面均无裂纹孔隙等缺陷，且生成相一致，主要包括TiC、TiB₂、Ti₂Ni、WC和α-Ti；0wt% Y₂O₃涂层组织存在明显偏析，析出相尺寸粗大且方向性明显；3wt% Y₂O₃涂层组织呈均匀弥散状态分布，细化特征明显；经Bramfitt二维点阵错配度计算，（100）_Y2O3和（100）_Ti2Ni、（111）_Y2O3和（110）_TiC、（110）_Y2O3和（1010）_TiB2间的错配度分别为5.75%、6.72%和10.10%，Y₂O₃作为异质形核核心对Ti₂Ni、TiC和TiB₂的细化能力依次为Ti₂Ni > TiC > TiB₂；0wt% Y₂O₃和3wt% Y₂O₃涂层显微硬度分别为600~630 HV_0.5和470~480 HV_0.5，较基材分别提高了约62%和26%；3wt% Y₂O₃涂层耐磨减摩性最优，其磨损体积和摩擦系数较0wt% Y₂O₃涂层分别下降了约47.8%和5.0%，磨损机制主要为磨粒磨损。     

不同温度下DSM11镍基高温合金热腐蚀试验

为了研究DSM11镍基高温合金的抗热腐蚀性能，对该合金在650、750、850℃条件下涂覆5%NaCl+95%Na 2 SO 4 混合盐膜 进行腐蚀试验。利用金相显微镜（OM）、扫描电子显微镜（SEM）、能谱仪（EDS）和X射线衍射仪（XRD）等手段，对合金被腐蚀200 h 后的表面形貌、物相组成、元素和腐蚀层的分布情况以及腐蚀机理进行分析。结果表明：随着试验温度的升高，合金表面腐蚀程度 逐渐加重、腐蚀产物组成逐渐复杂、失重加大、腐蚀产物层厚度增大；合金的腐蚀产物层均可分为3层，最外层和中间层主要为氧 化物，内层由颗粒状氧化物和硫化物组成，O和S的侵入现象表明合金发生了较明显的内氧化与内硫化现象；在3种温度下，合金 表面生成连续稳定的Al 2 O 3 保护层，抑制了热腐蚀反应的进行，对基体存在有效的保护作用，表明合金具有一定的抗热腐蚀性能。     

Solar Variation and Stratospheric Response

We have shown in several recent publications that it is necessary to group the meteorological data according to the phase of the Quasi-Biennial Oscillation (QBO) throughout the year, in order to find a clear signal of the 11-year sunspot cycle (SSC). This work is summarized here. It is the purpose of this paper (1) to update earlier results of the solar cycle – QBO relationship for the northern winter, (2) to stress the interaction between the hemispheres and (3) to summarize the influence of the QBO on the solar variability signal, as well as the influence of the solar variability signal on the QBO throughout the year. For this, the constructed annual mean of the solar cycle – QBO relationship is introduced.     

Link11干扰试验效果评估技术研究

数据链已在近年来的历次战争中大显身手，取得很好的实战效果，因之数据链对抗成为通信对抗的重要研究方向。本文首先对干扰效果评估现状和Link11干扰方法进行了简单介绍，最后根据Link11的特点，提出了多层次、多方面的Link11干扰试验效果评估指标体系及干扰效果综合评估数据处理算法，为Link11数据链干扰设备的靶场试验提供技术参考。     

The potential for radiometric retrievals of halocarbon concentrations from the MIPAS-E instrument

Halocarbons, such as CFC-11, CFC-12 and HCFC-22, are important trace gases in the atmosphere through their role as greenhouse gases and their influence on stratospheric ozone chemistry. This paper focuses on an initial study using integration of spectral radiance measurements from a spaceborne limb sounding Fourier Transform Spectrometer (FTS) to retrieve these compounds in the upper troposphere and lower stratosphere (UTLS). The instrument employed in this study is the Michelson Interferometer for Passive Atmospheric Sounding onboard ENVISAT (MIPAS-E) which obtains spectral data in the altitude range of 6–68 km at an unapodized spectral resolution of 0.025 cm⁻¹. We have used optimal estimation techniques to retrieve vertical information for these compounds using a radiometric approach.

It is shown that significant retrieval information is obtained at up to five measured levels in the UTLS for CFC-11, up to six for CFC-12 and up to two levels for HCFC-22. An initial error analysis indicates significant sensitivity of our retrievals to variability in operationally retrieved pressure and temperature data. For each halocarbon, gain, offset and spectroscopic uncertainties generally each contribute less than 10% to the total error. Finally, tracer correlations are used to compare the datasets to equivalent relationships derived here from version 2 ATMOS data with very good agreements for CFC-12 but with more variability in the CFC-11 comparisons.     

Al—Mg—Li（01420）合金的时效与断裂

本文研究了Al-Mg-Li(01420)超轻型合金的时效微观过程,指出δ’相尺寸与时效时间1/3次方成正比,PFz宽度与时效时间1/2次方成正比;进而分析了时效对合金变形机制及破断特征的影响,指出欠时效时,位错切过δ’相质点;过时效时,位错绕过δ’相质点。峰值时效时,处于位错切过与绕过机制过渡阶段。随时效温度升高和时效时间增长,亚晶界断裂比例增大,合金塑性降低。     

基于SDP的LINK11数据链对抗系统

LINK11数据链是美国海军和空军采用的一种战术数据通信方式,对LINK11信号进行干扰和破解是电子对抗中的一项重要课题。根据其信道构成特点和信号调制方式,提出了一整套识别、解调以及干扰算法,并分别在基于DSP的软件无线电装备上实现,构成了LINK11数据链对抗系统。     

冲击载荷作用下的界面扩展裂纹

本文给出了在不同材料界面上扩展裂纹动力学问题解的一般表示。文中利用结合面的边界条件,将问题中所有各量用单一未知函数表示。利用复变函数理论,我们将在不同材料界面上受冲击载荷作用的扩展裂纹问题化为解析函数理论中的Keledysh-Sedov混合问题。文中给出这一问题的闭合解,并且给出了不同材料常数及裂纹扩展速度对应力场分布及应力强度因子的影响。     

固体推进剂断裂韧性试验方法研究

利用声发射试验系统和CT试样，对HTPB推进剂I型裂纹断裂韧性进行实验研究。通过研究复合固体推进剂的声发射事件特性和裂纹扩展特性的关系，得到一种由振铃计数确定临界载荷的方法，该方法能准确求得断裂韧性。