Electrolytic Passivation of Nitinol Shape Memory Alloy in Different Electrolytes

The corrosion behavior of the nitinol alloy was studied in various corrosion media of different Cl–ion concentrations. The results demonstrate that the Cl–ion concentration has significant influences on the corrosion behavior of the nitinol alloy. In order to enhance the corrosion resistance, protective films were generated on the surface of the nitinol alloy by means of the electrochemical passivation method, for which five different electrolytic solutions were investigated. The surface analysis indicates full growth of all samples pas-sivated in the different electrolytic solutions with layers, however, showing different morphological features. Without any defects like micro-cracks and pores, the surface of the samples passivated in the molybdate solution turns out smoother and denser than those pas-sivated in other solutions. It is shown that the electro-chemical passivation will reduce Ni content but increase Ti content in the surface, reaching the Mole ratio of Ti:Ni=9.01:1 on the outermost surface. Potentiodynamic polarization test demonstrates that the samples electrochemically passivated in the molybdate solution present a significant increase in breakdown potential due to titanium enrichment on the outermost surface.     

一种基于P2P MMOG的分布式消息分发算法

提出了一种适合于P2P MMOG的分布式消息分发算法。游戏世界通过N-Tree划分为若干个子区域,并从每个子区域中选举出一个协调者节点。对于区域内玩家交互过程中产生的事件,由该玩家通过多播机制发送给其兴趣域中的其他玩家和区域协调者,协调者仅负责保存区域内的对象的状态信息并周期性的进行更新。实验表明该算法能够满足游戏状态的一致性需求,并且能够在较大的程度上降低协调者负载和通信开销,节省了大量的计算资源和宝贵的带宽。     

2-氯-4,6-二硝基-1,3-苯二酚萃取热力学研究

采用萃取平衡实验法,研究了用有机溶剂萃取水相中2-氯-4,6-二硝基-1,3-苯二酚的萃取热力学性质。考察了选用乙酸乙酯作萃取剂,苯、甲苯、环己烷和正庚烷作稀释剂时对萃取水相中2-氯-4,6-二硝基-1,3-苯二酚的影响。结果表明,萃合物的结构与稀释剂的种类有关,并且2-氯-4,6-二硝基-1,3-苯二酚在有机相中的分配系数随稀释剂介电常数的增大而增大。通过研究温度对萃取过程的影响,证实了乙酸乙酯从水相中萃取2-氯-4,6-二硝基-1,3-苯二酚的过程是一个放热过程,表观热效应ΔH=-10.088 kJ/mol。     

基于鲁棒自适应反步法的航天器姿态跟踪控制

针对存在未知惯量矩阵和外干扰的刚体航天器姿态跟踪,提出了一种鲁棒自适应控制方法。综合自适应反步法和非线性L2增益干扰抑制方法,用自适应反步法构造系统的Lyapunov函数,获得了具L2增益的鲁棒自适应控制器,以保证姿态跟踪误差系统为一致最终有界稳定,确保估计的航天器惯量参数的有界性,并使从外干扰输入到评价输出的L2增益不大于给定值。仿真结果验证了方法的有效性和可行性。     

温差发电模块面积比功率实验优化研究

同位素温差发电器是目前深空探测航天器广泛采用的电源装置。为优选温差发电模块构型、提高模块的输出功率和面积比功率,制备了具有不同热电元件截面积的碲化铋基温差发电模块。通过建立的实验测试系统,测量了多种温差条件下发电模块的输出功率随负载的变化。实验结果表明:当模块包含的热电元件(p–n结)对数一定时,热电元件的截面积越大、模块占空比越高,则模块输出功率越高、匹配负载越小;在热源温度450 K、热沉温度300 K的条件下,测得热电元件截面积为1.6 mm×1.6 mm、占空比为0.406的发电模块的最大面积比功率约为0.282 W·cm~(-2)。最后,对理想与实际情况下,占空比为1时的模块面积比功率进行了分析。     

机械合金化＋热压制备Laves相NbCr2合金及其组织性能研究

采用机械合金化 热压工艺路线来制备化学配比成分的单相Laves相NbCr2合金.研究了Cr,Nb元素粉经20h球磨后在1200℃,1250℃和1300℃不同时间热压所获得的Laves相NbCr2合金的组织和性能.结果表明:1250℃×0.5h热压获得的Laves相NbCr2合金组织均匀,晶粒尺寸达到微/纳米级,致密度达到97.1%,室温断裂韧性高于5.07MPa·m1/2.与熔铸工艺制备的单相Laves相NbCr2合金的断裂韧性1.50MPa·m1/2相比,所制备的单相Laves相NbCr2合金的室温断裂韧性大大提高,充分实现了细晶韧化的效果.     

2DCf／SiC-Si复合材料的制备和性能研究

针对短时高温抗氧化的具体环境,采用先驱体转化工艺制备2D Cf/SiC-Si复合材料.首先考察首周期裂解温度对2D Cf/SiC-Si材料力学性能的影响,结果表明,首周期采用1200℃裂解,所制备的2D Cf/SiC-Si复合材料界面结合较好,弯曲强度和断裂韧性分别达到305.4MPa和15.7 MPa·m1/2.在此基础上研究了Si粉含量对材料性能的影响.结果表明,随着Si含量的增加,2D Cf/SiC-Si材料的力学性能稍有降低,而抗氧化性能明显提高,主要原因在于材料中游离碳含量的降低和Si氧化后生成的具有封填裂纹和隔氧作用的SiO2膜.     

2D70铝合金热稳定性研究

2D70是可热处理强化的耐热铝合金,一般用在高温场合.以2D70铝合金自由锻件为对象,研究了热稳定化处理对合金室温、高温拉伸性能的影响,测定了合金的高温持久、蠕变性能,并观察了合金在这些高温试验条件下的组织变化.结果表明,2D70铝合金的耐热性较好,可在150℃长时使用,175℃以下时,合金的性能和组织变化都不明显;高温下合金的断口呈现沿晶断裂特征.     

高分散高稳定ZrO2水悬浮液的分散性研究

本文选用纳米粉ZrO2,分别采用单一静电稳定机制、加入PEG的空间位阻稳定机制和加入PMAA-NH4的电空间稳定机制制备成2vol%的ZrO2水悬浮液,通过Zeta电位、沉降实验等手段,最终得到了碱性条件下的高分散、高稳定的ZrO2水悬浮液。实验证明:当pH=8.3时,PMAA-NH4的分散效果最好。     

高速CO2焊接过程稳定性分析

利用汉诺威焊接质量分析仪,检测CO2焊短路过渡过程的电参数信号,研究高速焊接情况下燃弧时间与短路过渡周期的变化规律,分析了高速CO2焊接过程中短路过渡各个电参数对焊接过程稳定性的影响。对短路与燃弧阶段的电流、电压波形进行分析,认为波形控制可以有效改善焊接过程的稳定性。