The diurnal variations in total electron content (TEC) in the equatorial ionisation anomaly (EIA) region are not always represented by two crests on both sides of the magnetic equator. Sometimes, only an obvious single crest is evident at equatorial and low latitudes. In this paper, we focus on analysis of the morphological features of the single crest phenomenon in TEC around 120°E longitude during geomagnetic quiet days (Kp < 4₋). The variations in TEC are also compared with morphological parameters (foF2 and hmF2) derived from the International Reference Ionosphere extended to Plasmasphere (IRI–Plas) model. Our results show that the single crest phenomenon occurs mainly on days with extremely low solar activity, while the corresponding F2 layer critical frequency showed obvious asymmetry, or even only a single peak.     

高固含量改性双基推进剂的烤燃试验研究

采用非限定烤燃试验,测定了高固含量改性双基推进剂药柱的热爆炸临界温度,讨论了固含量与临界温度的关系及临界温度的尺度效应;通过高压热分解研究,获得了高固体含量推进剂热分解反应非等温动力学参数,探讨了固含量对临界温度的影响机理。结果表明,固含量由0％增加至50％,热爆炸临界温度由134．5℃上升到156．1℃,3 MPa压力下第一热分解峰温由201．8℃上升到206．2℃（β＝10℃／min）,表明热稳定性增加;长径比为1的GLX?4药柱临界温度与直径的对数呈线性关系。此外,随着固含量升高,热分解活化能由161．0 kJ／mol升高到181．9 kJ／mol,揭示了烤燃试验热获得的爆炸临界温度升高这一现象的高压热分解动力学理论依据。     

Phase Equilibria in Nb-Si-Mo Ternary Alloys at 1 273 K and 2 073 K

Phase equilibrium in Nb-Si-Mo ternary alloys （〈37.5 at.% Si） at 1 273 K and 2 073 K is investigated by using X-ray diffraction （XRD） analysis, scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS）. The partial isothermal section at 1 273 K, which contains four single-phase regions, five two-phase regions and two three-phase regions, is basically the same as that at 1 973 K. However, when the temperature increases to 2 073 K, the three-phase region of Nbss＋ct-（Nb（Mo））sSi3＋13-（Nb,Mo）sSi3 obviously moves towards the Nb-rich comer. This suggests that Nb-Si-Mo ternary alloys remain stable at least up to 1 973 K.     

复合材料热气防冰系统试验研究

为了进行复合材料热气防冰性能的研究,结合冲击射流和微通道强化换热,针对复合材料导向叶片提出了一种热气防冰系统。对给出的复合材料热气防冰系统进行了简易的冰风洞试验,在同一气流速度、防冰热气流量、平均水滴有效直径条件下,对不同防冰热气温度、外流冷气温度和液态水含量状态下的蒙皮外表面温度进行了测量。结果表明：给出的复合材料热气防冰系统性能正常,能够满足防冰要求;比较了液态水含量、防冰热气温度和冷气温度对蒙皮外表面温度的影响,说明在本实验范围内液态水含量是影响蒙皮外表面温度的最大因素。     

Cu含量对2219铝合金锻件及其焊接接头组织与性能的影响

采用力学拉伸实验、焊接实验、电化学阻抗谱(EIS)、循环阳极极化曲线(Tafel)以及金相和扫描电镜(SEM)等分析测试方法,研究Cu含量对2219铝合金锻件组织与性能的影响。结果表明:降低Cu含量,有利于减少2219铝合金基体内的残余结晶相,并有效抑制在合金焊接过程中粗大Al_2Cu相的析出,使基材和焊件的伸长率显著提高,强度略有下降;Cu在铝基体中形成Al_2Cu相诱导合金发生局部腐蚀,使材料的耐腐蚀性能变差,降低Cu含量能够减小合金的腐蚀倾向,改善合金的耐腐蚀性能。     

C含量对第二代单晶高温合金组织的影响

在高温度梯度真空定向凝固炉中,制备不同C含量的单晶高温合金,研究不同C含量对第二代单晶高温合金显微组织的影响。结果表明:C含量对合金枝晶间距的影响较小;随着C含量增加,共晶含量和尺寸减小,碳化物含量增加,其形貌由块状向骨架状、汉字状转变;随着C含量增加,Ta元素枝晶偏析减轻,Re,W,Mo,Nb元素枝晶偏析加重;C含量对铸态和热处理γ'相尺寸和形貌影响较小;热处理后碳化物的形貌无明显变化。     

树脂含量对F-8H3/602 芳纶复合材料性能的影响

探索研究了F-8H3/602芳纶织物增强树脂基复合材料层合板不同树脂含量对其冲击韧性、层间剪切强度及弯曲性能的影响,并采用显微镜及扫描电镜对破坏试样形貌进行观察。结果表明芳纶复合材料的树脂含量对其冲击韧性、层间剪切强度及弯曲性能影响较为明显,树脂含量为46.02wt%的芳纶复合材料层合板的0°冲击韧性为22 J/cm2、0°层间剪切强度为49.1 MPa、0°弯曲强度为506 MPa;在一定的树脂含量下,芳纶复合材料的0°冲击韧性、层间剪切强度及弯曲性能较90°的性能更优异;破坏试样的形貌表明纤维与树脂界面结合较为薄弱。     

Fe含量对2219铝合金锻件焊接组织与性能的影响

为研究杂质Fe元素对2219铝合金及其焊接接头的组织、性能以及电化学腐蚀性能等的影响,采用力学拉伸、焊接试验以及金相和扫描电镜等分析测试方法,对0.15%(w)至0.01%(w)等不同Fe元素含量的2219铝合金锻件进行实验研究和分析。研究表明:2219铝合金中经热变形加工存在网络状Al_2Cu变成颗粒状和纤维状的Al_7Cu_2(Fe,Mn)相,随着Fe含量由0.15%(w)降低至0.01%(w),合金固溶时效后的Al_7Cu_2(Fe,Mn)相显著减少,锻件强度和塑性显著提高;合金焊接接头断口由脆性断裂逐渐转变为韧窝尺寸细小的韧性断裂,尤其对于延伸率,提高至近1.4倍,强度和塑性显著提高;合金的自腐蚀电流逐渐减小,单位面积上的线性极化电阻增大,合金焊接接头的耐腐蚀性能显著提高。     

氢对TC4合金切削加工性能的影响

通过对不同氢含量的TC4合金试件进行车削试验,测量切削力和加工后的表面粗糙度及观察切屑形态,研究氢对TC4合金切削加工性的影响.结果表明:在一定范围内,随氢含量增加,TC4合金的切削加工性提高,并且有一个最佳值,氢含量为0.2%.超过该值后,随氢含量增加,钛合金切削加工性变差.