Ultrasound assisted solidification process of ternary Cu–Sn–Sb alloy

It is well-known that the application of ultrasound during liquid to solid transitions for alloys can refine the solidification microstructure and thus improves the mechanical properties. How-ever, most published work focuses on single phase dendritic growth, whereas little has been con-ducted on the multiphase alloys with complicated phase transformations during solidification. In this work, the solidification process of ternary Cu40Sn45Sb15 alloy was realized within intensive ultra-sonic field with a resonant frequency of 20 kHz and ultrasound power from 0 W to 1000 W. The ultrasound refines the size of the primary e(Cu3Sn) intermetallic compound by two orders of mag-nitudes. If the ultrasound power increases to 1000 W, g(Cu6Sn5) phase nucleates and grows directly from parent liquid phase without the occurrence of peri-eutectic reaction on the top of the alloy sam-ple where the ultrasound intensity is sufficiently high. These microstructural variations lead to the enhancement of compressive strength and elasticity modulus of ternary Cu40Sn45Sb15 alloy.     

一种测量铝合金裸金属钝化速率的新方法

在研究金属材料尤其是敏感金属材料的腐蚀疲劳裂纹增长机理时，由于腐蚀疲劳裂纹尖端裸金属滑移面其裸露与钝化的快速瞬时性，要求有一种能够及时准确地测出金属材料裸金属面的瞬面钝化速率的实用方法。为此，本文设计了一种测试试件，提出一种不仅测量准确，而且带助一般材料试验设备可完成的裸金属钝化速率测试方法，这对进一步研究金属材料的腐蚀疲劳问题，具有一定的现实意义。     

页轮干式磨削Ti6Al4V合金

进行了Ti6A14V合金锆刚玉页轮和碳化硅页轮的磨削性能试验研究,分析了磨削用量对磨削力、磨削温度和磨削表面完整性的影响。磨削力通过KISTLER9265B测力仪测定,磨削表面温度由NIUSB-621X信号采集系统测得,磨削表面形貌和金相组织由HiroxKH-7700型体视显微仪和Quanta200型扫描电镜（SEM）观察,表面粗糙度由Mahr Perthometer M1粗糙度仪测得,表层显微硬度通过HVS—1000硬度计测定。研究结果表明：页轮磨削钛合金工件表面没有发生烧伤现象,磨削热影响区厚度小于50μm,锆刚玉页轮比碳化硅页轮更适合干式磨削钛合金。     

TiAl基金属间化合物的超塑性研究现状

综述了国内外在TiAl基金属间化合物超塑性研究方面所取得的成就,内容包括超塑性力学性能及其影响因素。最后,对TiAl基金属间化合物超塑性成形的应用前景进行了展望。     

新型电子封装Si-Al合金的基础研究

对传统金属电子封装材料的研究开发现状进行了简单评述。利用喷射沉积成形技术制备了Si—Al（含硅量50～70wt％）合金。这种合金具有细小均匀的显微组织，同时具有低热膨胀系数、高热传导率和低密度等特点。     

Selective laser melting of Al–8.5Fe–1.3V–1.7Si alloy: Investigation on the resultant microstructure and hardness

This article presents the microstructure and hardness variation of an Al–8.5Fe–1.3V–1.7Si(wt%, FVS0812) alloy after selective laser melting(SLM) modification. Three zones were distinguished across the melting pool of the SLM-processed FVS0812 alloy: the laser melted zone(LMZ), the melting pool border, and the heat affected zone(HAZ) in the previously deposited area around the melting pool. Inside the LMZ, either an extremely fine cellular-dendritic structure or a mixture zone of the a-Al matrix and nanoscale Al_(12)(Fe,V)_3Si particles appeared. With a decreased laser beam scanning speed, the cellular-dendritic structure zone within the LMZ shrank significantly while the mixture zone expanded. The a-Al and Al_(12)(Fe,V)_3Si mixture zone was also observed in the HAZ, but another phase, submicron h-Al_(13)Fe_4 particles with rectangular or hexagonal shapes,formed along the melting pool border. Microhardness tests indicated that the hardness of the SLM-processed FVS0812 samples far exceeded that of the as-cast FVS0812 alloy.     

Al-4.5％Cu合金的过冷及凝固组织特征

对Ａｌ－４．５％Ｃｕ合金在纯石黑坩埚中用卤盐熔剂净化后的过冷度及其在金属锭模中的凝固组织特征进行了研究。实验结果发现：粘度较大的半固态熔剂对合金的净化作用较强,可使合金在金属锭模中得到６２℃的形核过冷度;金属熔体净化得到的热力学过冷度对合金形核及最终宏观组织的影响明显不同于激冷得到的动力学过冷度对其所产生的影响,在一定过冷度下,晶粒尺寸随热力学过冷度的增大而增大     

SMA 智能复合构件控制裂纹的数值与试验研究

将ＴｉＮｉ形状记忆合金（ＳＭＡ）薄带复合于基体材料内部,利用形状记忆合金的特性,可以控制构件裂纹的扩展。本文介绍了智能复合构件控制裂纹的机理,并利用拟温度载荷法,直接应用现有有限元程序对控制裂纹的ＳＭＡ智能复合构件进行了计算与分析,同时还进行了激光云纹干涉法试验测试。计算和试验结果表明智能复合构件中的记忆合金薄带对构件裂纹有显著的控制效果,同时计算和试验结果的一致性也表明本文的分析方法是可行的。     

等离子体处理对非晶态合金镀层表面改性研究

通过微波等离子体处理方法对Ni-W、Ni-W-B非晶态合金镀层表面进行改性的研究,测量了表面改性对非晶态镀层耐蚀性、表面成分及结构的影响.结果表明,经过微波等离子体处理过的Ni-W、Ni-W-B非晶态合金镀层,提高了在H₂SO₄、HNO₃溶液中的耐蚀性以及在700℃环境下的抗氧化性能;微波等离子体处理过的非晶态合金镀层表面含W量和含O量相对提高了;镀层结构仍然是非晶态.     

铝合金薄板零件橡皮囊成形屈曲分析与实验

为了抑制铝合金薄板类零件在橡皮囊成形后出现屈曲的缺陷,采用薄板屈曲微分方程对零件成形后的屈曲进行理论分析,并通过橡皮囊成形实验研究自然时效时间和成形压力对屈曲缺陷的影响。理论分析结果表明：零件法兰屈曲波数与其内外径比有关,通过改变法兰宽度进行实验验证,实验结果与理论分析结果相符;而成形实验结果表明,屈曲缺陷高度随板料自然时效时间的增加而增加,随成形压力的增加而减少。因此,理论分析结果有效,并且可通过减少淬火后成形时间和增加成形压力来抑制屈曲缺陷。