The microstructure of rain has been studied with observations using a vertical looking Micro Rain Radar (MRR) at Ahmedabad (23.06°N, 72.62°E), a tropical location in the Indian region. The rain height, derived from the bright band signature of melting layer of radar reflectivity profile, is found to be variable between the heights 4600 m and 5200 m. The change in the nature of rain, classified on the basis of radar reflectivity, is also observed through the MRR. It has been found that there are three types of rain, namely, convective, mixed and stratiform rain, prevailing with different vertical rain microstructures, such as, Drop Size Distribution (DSD), mean drop size, rain rate, liquid water content and average fall speed of the drops at different heights. It is observed that the vertical DSD profile is more inhomogeneous for mixed and stratiform type rain than for convective type rain. It is also found that the large number of drops of size <0.5 mm is present in convective rain whereas in stratiform rain, drops concentration is appreciable up to 1 mm. A comparison of measurements taken by ground based Disdrometer and that from the 200 m level obtained from MRR shows good agreement for rain rate and DSD at smaller rain rate values. The results may be useful for understanding rain structures over this region.     

钛合金TB6铣削加工硬化实验

研究了使用涂层硬质合金刀具对钛合金TB6进行端铣加工时,铣削参数以及刀具后刀面磨损量对加工硬化（表面硬化率、硬化层深度以及硬化层硬度分布）的影响,以弄清TB6铣削硬化现象及机理.结果表明,在实验参数范围内,刀具无磨损的情况下,硬化率基本保持在107%~112%范围内,硬化层深度范围为18~36 μm;铣削速度增加时,加工硬化程度会有较为明显的降低现象,而进给量与切深对加工硬化的影响并不明显;刀具磨损对加工硬化的影响较为显著,后刀面磨损量低于0.2 mm时,硬化层深度随着磨损增加从30 μm增加至55 μm,而后刀面磨损量为0.35 mm时,硬化层深度达到了130 μm.刀具磨损后在加工表面下较浅位置出现软化区域,而且随着磨损量的增加,软化越来越明显.      

GH909合金长期时效后组织和性能的研究

研究了GH909合金在650℃长期时效后的组织和性能的变化.结果表明,合金在650℃长期时效后,针状ε和ε″相大量析出并粗化,γ'相数量增加,尺寸基本不变;合金的拉伸强度下降,塑性提高,650℃×510MPa缺口持久寿命提高.合金在650℃长期时效2000h后组织和性能比较稳定,具有较好的综合性能.     

Phase Transformation and Microstructure of Ti50Ni48-xFe2Ndx Shape Memory Alloys

The influences of rare earth element Nd on the phase transformation and the microstructure of Ti₅₀Ni_48−xFe₂Nd_x shape memory alloys are investigated by means of electrical resistivity, optical microscopy, electron probe microanalyzer, and X-ray diffraction. The results show that TiNiFe alloys with different Nd contents exhibit two-step martensitic transformation. The start temperature of martensitic transformation increases sharply from 212 K to 267 K when 0.1 at.% Nd is added in, and then decreases gradually if Nd content further increases. The microstructure of TiNiFeNd quaternary alloys consists of TiNi matrix, Ti₂Ni second phase, and Nd₃Ni intermetallic compound. The spherical Nd₃Ni precipitate-particles evenly disperse in the matrix.     

Cu-1.0% Cr亚共晶合金定向凝固组织演化

在定向凝固下计算和比较了Cu-1.0%Cr亚共晶合金组织中各相的界面生长温度,结果表明当定向凝同速率大于5αm/s时,α-Cu相的界面生长温度高于共晶组织,α-Cu相会作为初生相首先析出凝固,从而难以制备出全耦合生长的共晶组织的复合材料,计算获得的结果与实验结果相一致.另外随定向凝固速率的增加,初牛胞状α-Cu相一次枝晶间距和尖端半径以及共晶组织的体积分数都相应地减少,其中α-Cu相一次枝晶间距实验结果与KF一次枝晶间距模型计算结果较为接近.     

Interfacial characteristics in CNTs-AgCuTi systems

AgCuTi-based composite fillers reinforced with Carbon Nanotubes（CNTs） were prepared by mechanical ball milling and ultrasonic agitation. The morphological features, chemical components, and melting characteristics of the composite fillers with different content of CNTs addition were investigated using Field Emission Scanning Electron Microscopy（FESEM）, XRay Diffraction（XRD） and a Differential Scanning Calorimeter（DSC）. After being heated at 900 ℃, the microstructure of the composite fillers was ...     

硼纤维/环氧复合材料界面剪切强度的测试与研究

设计了一种单纤维拔出试样制备方法,分析了单根硼纤维拔出特性;同时采用该方法分别测试了四种硼纤维/环氧复合材料界面剪切强度。固化剂采用异佛尔酮二胺(IPDA)的硼纤维/环氧复合材料界面剪切强度比采用二乙烯三胺(DETA)的提高了44.7%;采用液体丁腈橡胶(LNBR)改性环氧树脂的硼纤维/环氧复合材料界面剪切强度提高了97.7%~135%。     

浇注温度对1种新型铸造镍基高温合金组织和拉伸性能的影响

为分析浇注温度与合金的组织结构和力学性能之间的变化关系,通过改变浇注温度获得不同枝晶组织试样,采用金相显微镜和扫描电镜来观察和分析合金的组织结构,结合拉伸性能测试研究了合金的组织结构对拉伸性能的影响。结果表明：降低浇注温度使γ＇相和碳化物得到细化;降低浇注温度提高了合金的拉伸强度,并改善了塑性。     

基于微观图像及内聚力模型的复合材料裂纹扩展模拟

为研究材料微观结构及晶界强度对材料力学性能的影响,在晶界处引入内聚力单元模型,模拟晶间破坏过程。以ZrB_2-SiC复合材料为研究对象,将其扫描的微观结构图片进行矢量化处理,并导入ABAQUS有限元软件中建立模型,同时在其晶界处,设置内聚力单元模拟晶界破坏过程。通过改变Zr B2与Si C相界面强度,得到了晶界及材料不均匀对材料应力分布及裂纹扩展的影响。结果表明,由于晶界的存在,材料内部出现应力分布不均匀现象并产生应力集中。随着晶界强度的改变,裂纹起始位置及扩展方向发生改变,且裂纹沿低强度的界面进行扩展。随着ZrB_2-SiC界面强度增大,材料的强度提高,拉伸模量不变。     

浸渗时间对C/C-SiC复合材料显微结构和力学性能的影响

采用反应熔体浸渗法,经不同的浸渗时间渗Si制备了3种不同的C/C-SiC复合材料,测试了材料的增重率、体积密度、断裂韧性及三点弯曲强度,分析了材料的物相组成,并观察了材料的显微结构.结果表明,在得到的C/C-SiC复合材料中,主要存在纳米级和微米级2种尺度的SiC颗粒,随着浸渗时间延长,材料的体积密度和SiC含量随之增加,但抗弯强度随之降低.浸渗时间从0.5 h延长到5 h,材料的密度从2.16 g·cm-3增加到2.21 g·cm-3,SiC的质量百分含量从21.54%增加到31.72%,三点弯曲强度从133 MPa下降到86 MPa,3种复合材料均表现出一种类似于金属材料的非脆性断裂行为,断裂应变约为1.3%,断裂韧性为9～10 MPa·m1/2.