研究了纤维增强塑料 ( FRP)拉挤型材的弯曲强度。试验结果表明 ,FRP拉挤型材在大跨距 (跨高比 l/h>1 0 )下的弯曲破坏模式通常是梁的纵向开裂 ;FRP拉挤型材由于剪切变形较大 ,强度计算时不能按普通各向同性梁理论进行计算 ,应考虑剪切变形的影响。为此 ,本文应用复合材料薄壁梁理论给出了 FRP拉挤型材在大跨距下弯曲强度计算的半经验公式     

Thermo-mechanical properties of RTM-made carbon fibre/polyimide composite attaching collar under transient heating

This study focuses on the thermo-mechanical properties of Carbon Fibre/Polyimide Composite (CFPC) attaching collars under transient heating. The CFPC attaching collars were fabricated by a high-temperature resin transfer moulding process, and their thermo-mechanical properties under the conditions of simultaneous transient heating and bending load were investigated. The results show that the attaching collar tends to fail at 118% of the limit load. The failure mode includes the fracture of the connecting screws, local extrusion damage of the hole edges, and slight ablation damage at the outer plies. And there is no observable residual deformation in the composite attaching collar. Furthermore, considering that the material properties vary with temperature, a progressive damage model based on the sequential thermo-mechanical coupling method was established to study the failure mechanism of the attaching collar. Finally, the damage factor of the CFPC was calculated to assess the safety status of the attaching collar. The results show that the primary damage modes of the composite attaching collar are intralaminar failure, which mainly occurs at the heat insulation layer and the hole edges, and these slightly affect the structural bearing capacity. A good correlation between the experiment and FEA is obtained. The test methods and analysis models proposed contribute to the safety assessment of composite structures under transient heating.     

国产中温固化热破胶膜性能

考察了一种适用于卫星太阳翼基板的国产中温固化胶膜的胶接性能和热破工艺性,并分别采用国产和进口胶膜,利用胶膜热破施胶方法制备了碳纤维网格面板/铝蜂窝芯夹层结构,对其弯曲性能进行评价。结果表明,国产胶膜的室温拉伸剪切强度（铝基材）为34.9 MPa,150 ℃时拉伸剪切强度降为10.2 MPa,-150 ℃时拉伸剪切强度降为30.4 MPa。碳纤维复合材料作为胶接基材时,室温拉伸剪切强度为17.5 MPa,破坏模式为基材分层破坏和胶黏剂内聚破坏的混合破坏模式。国产胶膜具有良好的热破工艺特性,在合适的工艺条件下,破孔率优于99.9%,90°板-芯剥离强度为15.4 N/cm;采用国产胶膜制备的蜂窝夹层结构的弯曲性能与采用进口Redux312UL的接近,弯曲刚度为1.94×10⁸ N·mm²,弯曲强度为35.7 MPa。     

航空复合材料纸蜂窝夹芯结构热成型开裂研究

飞机复合材料芳纶纸蜂窝夹芯部件在热压罐成型时处于热-力耦合工况。本文关注热成型过程中可能出现的蜂窝开裂现象,通过试验获得了蜂窝芯的拉、压、剪性能参数和芳纶纸的热性能参数,同时结合有限元分析手段和反演方法,对整体蜂窝夹芯部件的热-力顺序耦合和局部芯子抽真空导致的蜂窝胞元间压强差进行数值模拟。结果表明：成型过程中的热应力不会导致蜂窝胞元间胶层开裂,局部憋气的压差可能导致蜂窝开裂;胶层部分破坏与胶层完全破坏所需的胞元间压强差的差值与胶层初始法向断裂应力正相关;胶层完全破坏所需的胞元间压强差随着受载胞元数量的增多而减小。     

Interconnected Ni（OH）2 and polyether amine on carbon fiber surface for simultaneously improving interfacial adhesion of epoxy composites and electrochemical properties

Interconnected Ni（OH）₂ nanoflakes and polyether amine（PEA） were deposited on carbon fiber tows via a facial and effective process of chemical bath deposition and dip coating. Based on this, a win–win benefit of simultaneously improvements in interfacial shear strength（IFSS） of carbon fiber/epoxy composites and the electrochemical activity has been achieved. Compared with CF and CF-Ni（OH）₂ composites, the IFSS of CF-Ni（OH）₂-PEA/epoxy composite respectively increas...     

(TiB+TiC)/TC4复合材料电解钻孔试验研究

钛基复合材料是一种典型的难加工材料,采用传统机械加工方法存在加工效率低和加工质量差等问题。利用电解加工技术,采用直径为10mm的管状阴极,对(TiB+TiC)/TC4复合材料进行电解钻孔加工试验研究。进行了(TiB+TiC)/TC4复合材料的电化学特性研究,测量了(TiB+TiC)/TC4复合材料在10%NaNO₃溶液中的极化曲线和电流效率。探究了加工电压、电解液压力对加工精度的影响。结果表明,当加工电压为30V,电解液压力为0.6MPa时,电解钻孔可以在1mm/min的进给速度下稳定加工。当加工的盲孔深径比为3.06时,孔的圆度误差为41.1μm,锥度为0.4°,具有较高的加工精度。     

X 射线 CT 技术在 C/ C 复合材料研究中的应用

分析了X射线CT技术的基本原理和成像模式,综述了X射线CT技术在C/C复合材料的密度测量、孔隙率、孔隙形状和分布等量化表征中的应用。同时介绍了X射线CT图像在C/C复合材料力学性能预测和裂纹扩展规律研究中的应用。     

玻璃纤维增强酚醛基复合材料平均线胀系数测试影响因素

研究了保温时间、升温速率、预处理温度等对玻璃纤维增强酚醛基复合材料线胀系数测试的影响。结果表明,玻璃纤维增强酚醛基复合材料在加热条件下进一步固化,造成样品收缩与样品受热膨胀相抵消,升温曲线出现平台。因此,测试前应对样品进行预处理,处理温度高于试样最终的测试温度,低于样品固化温度,以免材料内部结构发生变化;设置合适的升温速率,升温速率低,增加了时间成本,升温速率太高,测温热电偶引入的误差增加,且不均匀的加热使试样产生热应力,影响试验结果。     

纳米炭分对炭／酚醛材料性能的影响

用纳米级炭粉对炭／酚醛复合材料性能进行了改进。对纳米级炭粉加入后酚醛树脂的热解性能,材料的烧蚀性能、常温下力学性能、热性能及炭化后材料的层间剪切强度的测定结果表明,材料性能得到不同程度的提高,特别是热膨胀特性及高温下层间剪切强度得到大幅度提高。     

碳化硅颗粒增强铝基复合材料及其口盖的研制

采用一种新型的复合材料替代传统的材料应用于航天产品推进舱上的口盖。经过复合材料制备、预镦粗变形、热轧和冷轧、热处理、表面阳极氧化等工艺过程，成功地制备了ＳｉＣｐ／ＬＤ１０复合材料口盖。探讨了制备过程中的工艺选择和工艺参数，并对复合材料板材的性能进行了测试。