保载条件下FGH95材料的疲劳特性及寿命建模

针对FGH95粉末冶金材料进行了650℃时不同保载形式(拉伸保载、压缩保载和拉压保载)的疲劳试验, 分析了其变形特征和疲劳寿命分布特征以及保载对疲劳寿命的影响.并据此, 为改进保载条件下疲劳寿命的建模, 提出了迟滞环位置-形状修正因子的概念, 进而得到了一种修正的非弹性应变能~寿命方程.经对该材料疲劳试验寿命的建模和计算分析表明:该方法相比其他几种工程上经常采用的寿命预测方程, 较好地解决粉末冶金材料高温保载疲劳时的寿命建模问题, 且该方程对试验寿命预测的精度更高, 形式简单, 具有明显的物理意义.      

高温合金渗Al-Si层的微观组织分析

利用SEM,XRD和EPMA详细分析K4104镍基高温合金料浆渗Al-Si的微观结构.结果表明,表层主要为富Al的β-NiAl CrxSiy化合物,过渡层主要为富Ni的β-NiAl相,内扩散层主要为β-NiAl相 富Cr相 γ'-Ni3Al相 Ni固溶体.     

模具约束条件对H96黄铜双脊矩形管E弯截面变形的影响

 双脊矩形管的绕弯成形受内外侧模具的共同约束,不同模具约束下管坯的受力不同,使得其截面变形情况也不相同,而截面变形严重地影响弯管件的成形质量和使用性能。因此,基于ABAQUS有限元平台建立了双脊矩形管E弯成形三维有限元模型,并通过实验验证了模型的可靠性。采用所建模型,研究了内外侧模具约束条件对双脊矩形管E弯截面变形的影响规律,发现当只有内腹板脊槽受约束时,内腹板脊槽的内缩变形可得到较好的控制,而其他部位的变形则有增大的趋势;当只有外腹板脊槽受约束时,内腹板脊槽宽度变形基本不发生变化,而其他部位的变形则有减小的趋势;当内外腹板脊槽均受约束时,可较好地控制双脊矩形管E弯过程中的截面变形。芯头个数对整管截面高度、宽度、外腹板脊槽宽度与两脊槽底部的间距的变形影响较大,但对内腹板脊槽宽度的变形影响不显著。     

成分调整对DZ125合金凝固行为的影响

研究了标准成分的DZ125合金与以此为基础提高W、Al，降低Mo、Ti合金中的初生相的凝固顺序，确定了这两种合金在固-液范围内不同温度下的固-液相比例。结果表明，高W、Al低Mo、Ti合金显著缩小了合金凝固范围（Δ），使液相线温度提高了20℃，固相温度提高了70℃，并缩小失去技晶间毛细补缩能力时的温度与固相线之间的温度范围（ΔT2），从而减少了合金热裂倾向，提高了可铸性。Ti含量影响（γ＋γ'）共晶相尺寸、数量及形态，W、Wo对（γ＋γ'）共晶的数量、尺寸及形态均无影响。     

细晶铸造对K418合金拉伸性能的影响

测试了不同温度下细晶铸造和普通铸造Ｋ４１８合金的拉伸性能。结果表明，细晶铸造明显改善了合金的极限位伸强度和屈服强度，室温和６００℃的合金拉伸强度和晶粒平均直径符合Ｈａｌｌ－Ｐｅｔｃｈ关系。     

FGH96粉末涡轮盘结构模拟件疲劳小裂纹扩展试验

为了分析涡轮盘轮缘榫槽等几何不连续部位对疲劳裂纹萌生及小裂纹扩展行为的影响,基于FGH96粉末盘实际构型设计结构特征模拟件,并对其在高温条件下开展自然萌生疲劳小裂纹扩展试验,通过疲劳中断试验和表面复型技术对榫槽和螺栓孔结构模拟件在500℃下的裂纹萌生和小裂纹扩展行为进行了观测和分析。结果表明：2种结构模拟件缺口表面存在多裂纹萌生现象,随着应力水平的降低,裂纹萌生位置由表面晶界转变为近表面特定方向的晶面以及非金属夹杂物处;2种结构模拟件裂纹萌生寿命占比约为36%～73%,且随着应力水平的降低而提高,裂纹扩展至工程可检裂纹尺寸时的寿命占比约为82%～96%,应力水平对其影响相对较小;特征模拟件缺口附近高水平的塑性变形能够导致小裂纹扩展速率分段特征现象消失,并延缓裂纹扩展过程中的合并行为,延长裂纹扩展寿命。     

Grinding force and surface quality in creep feed profile grinding of turbine blade root of nickel-based superalloy with microcrystalline alumina abrasive wheels

Creep feed profile grinding of the fir-tree blade root forms of single crystal nickel-based superalloy was conducted using microcrystalline alumina abrasive wheels in the present study. The grinding force and the surface quality in terms of surface topography, subsurface microstructure, microhardness and residual stress obtained under different grinding conditions were evaluated comparatively. Experimental results indicated that the grinding force was influenced significantly by the competing predominance between the grinding parameters and the cross-sectional root workpiece profile. In addition, the root workpiece surface, including the root peak and valley regions, was produced with the large difference in surface quality due to the nonuniform grinding loads along the root workpiece profile in normal section. Detailed results showed that the surface roughness, subsurface plastic deformation and work hardening level of the root valley region were higher by up to 25%, 20% and 7% in average than those obtained in the root peak region, respectively, in the current investigation. Finally, the superior parameters were recommended in the creep feed profile grinding of the fir-tree blade root forms. This study is helpful to provide industry guidance to optimize the machining process for the high-valued parts with complicated profiles.     

基于T96模型的极尖区位形变化特性研究

基于T96模型,定义了极尖区的位形以及相关的描述参量(例如赤道向边界磁纬的最小值,纬向宽度,子午向和晨昏向的张角,倾斜度,扁平度,中心磁地方时等),讨论了太阳风动压(P_d)、行星际磁场(IMF)及磁暴强度对极尖区位形的影响.太阳风动压和磁暴强度越大,则极尖区的赤道向边界磁纬越小,纬向宽度越大,子午向和晨昏向的张角越大,倾斜度越大,扁平度越小;南向IMF B_z越强,则极尖区的赤道向边界磁纬越小,纬向宽度越小,子午向的张角越小,晨昏向的张角越大,倾斜度越大,扁平度越大;北向IMF B_z与南向IMF B_z的情况刚好相反;极尖区的中心磁地方时受IMF B_y控制,IMF B_y为正时,极尖区向昏侧移动,而IMF B_y为负时,极尖区则向晨侧移动,并且极尖区的中心磁地方时与IMF B_y之间有着良好的线性关系.将所得结果与前人的观测结果进行了简单比较,发现利用T96模型确定的极尖区位形与观测基本一致.     

Ru过渡层对NiCoCrAlY涂层与DD6单晶高温合金界面扩散行为的影响

针对第二代单晶高温合金DD6开展了一种具有阻扩散功能的金属防护涂层的探索性研究.采用电镀和电子束物理气相沉积(EB-PVD)方法在DD6单晶高温合金上制备了NiCoCrAlY/Ru双层结构涂层,同时采用EB-PVD在单晶合金上沉积了单层NiCoCrAlY涂层.研究结果表明,在1 050℃大气环境中扩散处理300 h后,...     

IC10高温合金的微观组织

研究了IC10高温合金的微观组织。研究表明:铸态组织包括γ′和γ,′以及γ γ′共晶相和MC碳化物,其中γ′体积百分数为64%,碳化物相主要是TaC和H fC,碳化物呈骨架状和点状、块状分布,共晶相多为葵花状。热处理后有残留的γ γ′共晶相,碳化物分解并有γ′包覆,γ′相发生球化,晶界上MC分解,并有H fC析出。IC10合金经950℃,3000h长期时效后组织保持稳定,未析出有害的TCP相;长期时效的组织变化表现为γ′的长大和条状化;枝晶间二次析出细小的富H f的MC相;晶界上析出少量的M6C和M23C6。