Improving tensile-shear properties of friction stir lap welded dissimilar Al/Mg joints by eliminating hook defect and controlling interfacial reaction

To improve tensile-shear properties of fiction stir lap welded(FSLW) dissimilar Al/Mg joints, pin-tip profiles were innovatively designed and welding speed was optimized, and effects of them on formation, interface microstructure and mechanical properties of different FSLW joints were investigated. With increasing the welding speed, the tensile-shear load of FSLW joints produced by three pins presents an increasing firstly and then decreasing trend. Compared with Rpin, the hook and hole defect i...     

Microstructural formation and mechanical performance of friction stir double-riveting welded Al-Cu joints

A novel friction stir double-riveting welding (FSDRW) technology was proposed in order to realize the high-quality joining of upper aluminum (Al) and lower copper (Cu) plates, and this technology employed a Cu column as a rivet and a specially designed welding tool with a large concave-angle shoulder. The formations, interfacial characteristics, mechanical properties and fracture features of Al/Cu FSDRW joints under different rotational velocities and dwell times were investigated. The results showed that the well-formed FSDRW joint was successfully obtained. The cylindrical Cu column was transformed into a double riveting heads structure with a Cu anchor at the top and an Al anchor at the bottom, thereby providing an excellent mechanical interlocking. The defect-free Cu/Cu interface was formed at the lap interface due to the sufficient metallurgical bonding between the Cu column and the Cu plate, thereby effectively inhibiting the propagation of crack from the intermetallic compound layer at the lap interface between the Al and Cu plates. The tensile shear load of joint was increased first and then decreased when the rotational velocity and dwell time of welding tool increased, and the maximum value was 5.52 kN. The FSDRW joint presented a mixed mode of ductile and brittle fractures.     

Si粉特性对反应烧结Si3N4多孔陶瓷的强韧性及介电性能的调控作用

Si₃N₄多孔陶瓷具有优异的力学性能、介电性能、热学性能和化学稳定性等，特别适用于高温、大载荷、强侵蚀环境下的宽频透波材料。反应烧结Si₃N₄多孔陶瓷在性能、工艺和成本方面优势显著，原料Si粉特性显著控制着其物相、显微结构、力学和介电性能。本文以不同粒径和纯度的Si粉为原料制备注凝成形、反应烧结Si₃N₄多孔陶瓷。结果表明，双粒径配料使素坯产生紧密堆积效应，其遗传并进一步演化出两级显微组织强韧化机制，双粒径配料5 & 45 μm时的弯曲强度和断裂功获得最大值109.94 MPa和990.74 J/m²。该值分别比单粒径配料5和45 μm时的值提高了111.42%、25.97%和46.55%、20.46%；介电常数和介电损耗分别约为4.20和0.007。注凝成形、反应烧结Si₃N₄多孔陶瓷可以兼顾力学性能和介电性能，适用于透波罩等异形、大尺寸构件。     

国产M55J级碳纤维与两种典型树脂界面性能研究

为了夯实国产M55J级碳纤维在航天构件中的应用基础，重点研究了国产M55J级碳纤维与航天环氧和氰酸酯树脂的界面性能，并与进口M55J碳纤维进行对比。采用扫描电子显微镜、原子力显微镜对碳纤维的微观形貌进行表征，通过接触角测量、红外光谱分析和微脱粘测试对碳纤维与航天树脂的粘附功、浸润性、化学反应特性和界面剪切强度进行测定。结果显示，国产M55J级碳纤维表面存在大量沟槽，上浆剂形成少量突起；国产M55J级碳纤维与两种树脂的浸润性优于M55J碳纤维与树脂浸润性，国产M55J级碳纤维与两种航天树脂的粘附功分别为55.76和48.61 mN/m，均高于进口碳纤维的粘附功；国产M55J级碳纤维上浆剂与两种航天树脂经高温固化后反应程度达到100%；国产M55J级碳纤维与两种航天树脂的界面剪切强度分别为74.62和62.99 MPa，均高于M55J碳纤维。     

碳纤维复合材料轴向压缩性能测试方法对比北大核心CSCD

轴向压缩性能一直是复合材料力学性能评价表征研究的难点。本文以国产T800级、M40J级碳纤维复合材料为研究对象,从试验研究、机理分析、计算模拟等角度,系统对比并分析了四种常用复合材料压缩性能测试方法的优劣与适用性,提出了优化的测试条件。试验与模拟结果表明,剪切加载方法(GB/T 3856—2005)易产生应力集中造成试样提前破坏,使压缩强度测试结果相比美标剪切加载方法(ASTM D3410—2016)降低约9%;端部加载(SACMA SRM 1R—94)测试结果较美标剪切加载和联合加载方法(ASTM D6641—2014)高3%~6%。测试条件优化研究中发现,加强片材质对破坏模式影响较大,强界面高强度复合材料适宜采用金属加强片,弱界面低强度复合材料适宜采用玻璃钢加强片。分析试样断口形貌,剪切加载和端部加载方法都可以观察到单向复合材料以纤维“跪折”为主的破坏模式。从测试结果和破坏模式来看,端部加载方法是较优的压缩强度测试方法。     

表面织构加工方法的研究

总结了激光加工、电解加工、电火花加工、化学刻蚀、光刻蚀以及超声振动辅助加工技术等方法；分析了表面织构形状对材料表面性能的影响；论述了表面织构几何参数对润滑性、摩擦学特性和疏水性等材料表面性能的影响。得出了合适的表面织构形状、面积率、深径比等表面织构设计参数可有效改善机械零部件表面性能的结论；发现了为获得理想表面性能，不仅需要考虑织构形状和几何参数，还需考虑工况条件、工件材料性质以及加工技术带来的影响。最后对关于表面织构加工技术所存在的问题进行了总结，并对如何提高表面织构技术对材料性能的影响进行展望。     

PBT固体推进剂低温力学性能研究

为考察PBT固体推进剂低温力学性能，采用单轴拉伸实验方法研究了固化参数、交联参数、固化时间三种因素对PBT固体推进剂-40℃下力学性能的影响。玻璃化温度测试结果表明，全部样品玻璃化温度处于-51.3～-53.6℃，推进剂在-40℃下处于高弹态；单轴拉伸测试结果表明：PBT固体推进剂在低温状态下硬度、抗拉强度与固化参数、交联参数、固化时间呈正相关，伸长率与固化参数、交联参数、固化时间呈负相关。低温力学性能受固化参数、交联参数影响显著性低于常温力学性能；低温下固化参数在1.00～1.05内与伸长率呈现一定线性关系。     

摆动焊接对异种热处理状态2219铝合金焊接接头性能的影响

针对2219异种热处理状态C1OS+CYS铝合金进行钨极氩弧焊接试验,对比研究了常规焊接与摆动焊接接头的力学性能、微观组织、硬度分布等.分析结果表明,相较常规接头,采用摆动焊接工艺的接头其力学性能有所提高,同时接头中下部PMZ、OAZ的硬度有所下降,宽度范围有所增加.应变分布结果表明,断裂前常规接头最大应变沿对角线分布...     

耐300 ℃聚酰亚胺树脂及其复合材料性能

为了解决耐300 ℃聚酰亚胺复合材料在热压成型工艺过程中尚未解决的基础性科学问题，推动其在飞行器主承力结构件的成熟应用，本文通过DSC、FTIR、流变、TGA和力学性能测试方法，系统分析了耐300 ℃聚酰亚胺树脂化学反应特性及其复合材料力学性能。结果表明，聚酰亚胺树脂于230 ℃完全酰亚胺化，1 ℃/min升温速率下最低黏度为86 Pa·s，采用优化成型工艺制备的复合材料具有良好的内部质量和力学性能。     

2219铝合金厚板TIG焊接头组织与力学性能研究

采用氦弧打底+氩弧填充、盖面的焊接工艺对2219-T87铝合金15 mm厚板进行TIG焊接试验，研究其焊缝成形和组织力学性能。结果表明，此工艺焊缝成形美观，无可见焊接缺陷，气孔抑制效果好，接头平均抗拉强度为278.22 MPa，平均断后延伸率为3.89%，接头平均强度系数达到58.94%。接头硬度整体表现为焊缝中心最低，从焊缝中心到母材呈现先增大后局部降低再增大的趋势；且焊缝中心填充层硬度高于打底层和盖面层。熔合区的微观组织为柱状树枝晶和胞状树枝晶，且垂直于熔合线生长，在靠近熔合区两侧出现了等轴细晶带。焊接接头断面有较多撕裂棱和韧窝，局部发现第二相粒子和微孔，其断裂机制为典型的韧性断裂。