采用有限元计算方法，对平面应变、平面应力两种应力状态下含中间层的陶瓷接头界面上应力分布规律进行数值分析。得到了接头界面上正应力和剪应力沿板定的分布曲线。结果表明，中间层材料厚度小时，两种应力状态下的正应力和剪应力在接头界面上滑板定的分布基本均匀。中间层材料厚度增大，平面应变状态下试件中部的正应力增大并出现峰值；平面应力状态下在试件自由瑞边缘正应力增大并出现峰值。两种应力状态下界面上的剪应力由板中央到板边缘逐渐增大，界面上边缘处最大剪应力的值也随中间层厚度的增加而增大。因此，在保证接头接合良好的前提下，应采用小厚度的中间层。     

连接压力在Ti/Ni/Ti复合层TLP扩散连接Si3N4陶瓷中的作用机制

研究了Ｔｉ／Ｎｉ／Ｔｉ复合层ＴＬＰ扩散连接Ｓｉ３Ｎ４陶瓷时压力对接头形成的作用机制。结果表明,ＴＬＰ来不及与陶瓷发生充分反应并形成高强度结合界面就已完全凝固,为形成高强度的结合界面,必须进一步发生固态扩散反应。只有当连接过程中施加足够的压力,才能保证ＴＬＰ在其存在期间充分铺展陶瓷,并在ＴＬＰ完全凝固后形成大量扩散通道,为固态扩散反应提供必要条件。     

Perpendicular transport of charged particles: Results for the unified nonlinear transport theory derived from the Newton–Lorentz equation

The perpendicular diffusion coefficient is calculated by combining a recently developed Unified Nonlinear Transport (UNLT) theory with the Newton–Lorentz equation. The total perpendicular mean free path can be described as a combination of a guiding center contribution and a microscopic contribution. It is shown that the total mean free path depends strongly on the energy range of the turbulence power spectrum and on particle energy. Further, a slab/2D composite model is used to investigate the influence of each contribution to the total mean free path for a quasi-3D turbulence model. For pure 2D turbulence the UNLT reduces to the NLGC-theory. For pure slab turbulence the guiding center contribution is subdiffusive in accordance with simulations and the theorem on reduced dimensionality. Conversely, the microscopic contribution is non-zero, which has to be interpreted as normal diffusion.     

Ni/Ti中间层部分瞬间液相法连接C/C复合材料和GH3044

采用Ni/Ti中间层,部分瞬间液相法(Partial Transient Liquid-Phase,简称PTLP)连接C/C复合材料和GH3044,通过SEM+EDS对接头的微观结构和元素分布进行了表征,并分析了接头形成机理。研究表明,这种方法可实现C/C复合材料与中间层、中间层与GH3044界面处的良好结合;所得接头截面为GH3044/扩散层/残余Ni层/Ni-Ti金属间化合物层/炭化物反应层/C/C复合材料;随保温时间的延长,接头中金属间化合物Ni3Ti不断生长,同时两侧的Ni、NiTi被逐渐消耗。另外,因为C/C复合材料和GH3044的热膨胀系数(Coefficient of Thermal Expansion,CTE)差别很大,所以冷却过程中产生了较大的热应力,导致C/C复合材料/中间层界面附近出现了大尺寸裂纹,使接头性能下降,其剪切强度仅有9.78 MPa。     

真空紫外辐照引起的聚合物材料质量损失模型及实验验证

基于扩散理论及辐射化学反应理论,建立真空紫外(VUV)辐照引起的聚合物材料质量损失数学模型。采用分离变量法与特征函数展开法,获得材料中挥发物质量随辐照剂量变化的函数关系式。通过实验得到聚酰亚胺(PI)薄膜和聚酯(PET)薄膜的质量损失数据,拟合求解模型中的参数,验证模型的适用性。实验结果表明,该质量损失模型适用于PI薄膜及PET薄膜,借助该模型可预估VUV辐照引起的材料的质量损失。     

碳纤维/双马树脂复合材料整体成型过程分层扩展行为实验研究

针对复合材料构件热压罐成型过程中常见的分层缺陷,考察了整体成型工艺温度对分层扩展、QY8911双马树脂基体韧性及T300/QY8911层合板Ⅰ型层间断裂韧性的影响,并通过分层扩展断面形貌深入分析了复合材料整体成型工艺中分层扩展的路径和断面破坏模式,给出了复合材料整体成型工艺和结构设计的优化建议措施。结果表明,随着整体成型最高温度的升高,分层扩展程度增大,QY8911双马树脂基体的拉伸强度和拉伸模量逐渐降低,T300/QY8911层合板Ⅰ型层间断裂韧性逐渐增大;对分层扩展断面进行SEM扫描电镜分析发现分层扩展沿着层间开裂,断面内存在基体断裂和基体/纤维界面脱粘两种破坏模式,Ⅰ型层间断裂是复合材料整体成型工艺中分层扩展的典型微观特征。     

Effects of various dissipation range onset models on the 26-day variations of low-energy galactic cosmic-ray electrons

The effect of various models presented by Leamon et al. (2000) for the dissipation range cutoff wavenumber on the 26-day variations of galactic cosmic-ray electrons in a Fisk-Parker hybrid field is investigated, by means of a three-dimensional steady-state numerical modulation code. Analytical expressions for the mean free paths parallel and perpendicular to the heliospheric magnetic field are adapted from the works of 31 and 28, respectively. Note that only solar minimum conditions are considered, and that only qualitative agreement with data is sought. Effective diffusion for galactic electrons pertaining to 26-day variations is found to be dominated by the ratio of the perpendicular to parallel mean free paths at low energies, and the relationship between changes in cosmic-ray intensities and the modulation parameter postulated by Zhang (1997) is found to no longer hold when this ratio drops below a critical value. Use of ion inertial scale dependent models for the dissipation range cutoff leads to possible second linearities in the relative amplitudes as functions of latitude gradient.     

脉冲电流辅助粉末夹层TLP连接SiC_p/Al接头微观组织和力学性能

研究脉冲电流辅助瞬间液相(Transient Liquid Phase,TLP)扩散连接技术,采用粉末中间层,利用低压高强脉冲电流通过铝基复合材料搭接面与中间层,从而实现对SiC_p/2024Al复合材料板材的TLP扩散连接。分析不同工艺参数下连接试样的微观组织和力学性能,探索脉冲电流对铝基复合材料连接的影响机理。结果表明:采用真空压强为1×10~(-3)Pa,平均电流密度115 A/mm~2,连接预紧压力为0.5 MPa,连接时间60 min条件下,连接接头形成了良好的冶金连接界面,无缺陷产生;通过对连接接头微观组织观察发现,在脉冲电流作用下,接头原位生成弥散的高强度高硬度金属间化合物增强相,有效地提高了接头的力学性能。     

大厚度扩散焊NLU成像检测技术

针对钛合金大厚度扩散焊,基于非线性超声(Non-linear ultrasonic,NLU)原理,构建了一种NLU成像方法和检测系统,设计制备了不同的大厚度扩散焊试件,进行了NLU成像检测试验分析。检测结果表明,采用NLU成像检测方法,可实现钛合金大厚度扩散焊的超声可视化检测,最大检测厚度可达70mm。     

铝合金表面贯穿式复合涂层设计、制备及性能研究

为了改善航空航天用铝合金的耐磨性能,尤其是保证在使用环境温度升高情况下铝合金的正常使用。本文在机械球磨涂层与基体之间扩散层形成原理的基础之上,设计三维立体状扩散层来增大涂层与基体之间结合性能;采用融合机械球磨、激光织构微孔和电沉积3种技术在铝合金表面制备贯穿式复合涂层,对复合涂层的力学和摩擦学性能进行测试分析。结果表明,电沉积Ni涂层完全覆盖了机械球磨涂层的织构表面,经过热处理后机械球磨涂层和电沉积涂层显微硬度分别约为285和165 HV,并且铝合金基体、机械球磨涂层和电沉积涂层3者界面处形成了三维立体结构扩散层。铝合金在室温情况下摩擦学性能表现正常,但在300℃下出现失效现象。针对4种复合涂层,室温下N150复合涂层的摩擦因数最低(约为0.7);300℃下N100、N150、N200复合涂层摩擦因数约为0.5。两种温度环境下4种样品的磨损率分布在(0.9～1.6)×10^-3mm³/(N·m),N100和N150复合涂层性能表现略好。采用该方法制备的贯穿式复合涂层在室温和300℃环境下有效的保护了铝合金基体,拓宽了铝合金的适用范围。