激光3D打印铁基块体非晶复合材料

Fe基非晶合金因强度高、硬度高、软磁性能优异等优势,得到人们极大关注。然而,目前实验室和工业领域利用铜模铸造法所能制备的Fe基非晶合金尺寸仍然较小,这严重制约了Fe基非晶合金作为结构材料在工业领域的实际应用。激光3D打印技术的出现为解决上述问题提供了难得的契机。然而,目前国内外的研究中,利用激光3D打印技术制备Fe基非晶合金存在较为严重的裂纹,所以无法利用该技术成型大尺寸的样品。在Fe基非晶合金中引入塑性较好的第二相来吸收热应力,防止在激光3D打印过程中发生开裂,能成功打印出大尺寸的Fe基非晶合金复合材料。通过上述方法成型的大尺寸Fe基非晶合金复合材料,宏观上没有裂纹发生且成型性良好,但微观上仍在局域发现微小裂纹。由于Cu将Fe基非晶合金包裹在中间,所以这些局域的微裂纹没有扩展,也没有贯穿整个材料,打印的Fe基非晶合金复合材料成型性没有受到较大影响。     

Crack monitoring method based on Cu coating sensor and electrical potential technique for metal structure

Advanced crack monitoring technique is the cornerstone of aircraft structural health monitoring.To achieve real-time crack monitoring of aircraft metal structures in the course of service,a new crack monitoring method is proposed based on Cu coating sensor and electrical potential difference principle.Firstly,insulation treatment process was used to prepare a dielectric layer on structural substrate,such as an anodizing layer on 2A12-T4 aluminum alloy substrate,and then a Cu coating crack monitoring sensor was deposited on the structure fatigue critical parts by pulsed bias arc ion plating technology.Secondly,the damage consistency of the Cu coating sensor and2A12-T4 aluminum alloy substrate was investigated by static tensile experiment and fatigue test.The results show that strain values of the coating sensor and the 2A12-T4 aluminum alloy substrate measured by strain gauges are highly coincident in static tensile experiment and the sensor has excellent fatigue damage consistency with the substrate.Thirdly,the fatigue performance discrepancy between samples with the coating sensor and original samples was investigated.The result shows that there is no obvious negative influence on the fatigue performance of the 2A12-T4 aluminum alloy after preparing the Cu coating sensor on its surface.Finally,crack monitoring experiment was carried out with the Cu coating sensor.The experimental results indicate that the sensor is sensitive to crack,and crack origination and propagation can be monitored effectively through analyzing the change of electrical potential values of the coating sensor.     

Comparative study between crack closure model and Willenborg model for fatigue prediction under overload effects

A comparative study is performed between a crack closure model and the Willenborg model, which can calculate the fatigue crack growth rate under the overload effects. The modified virtual crack annealing (VCA) model is briefly reviewed, which is based on the equivalent plastic zone concept. In this method, the retardation phenomenon is explained by the crack closure level variation, which is derived from the interactions between forward and reverse plastic zones ahead of the crack tip. As a comparison, the Forman equation in conjunction with the Willenborg model is also reviewed. The retardation phenomenon is described by directly modifying the stress intensity factor. It is known that the large plastic zone created by the overload can decelerate the fatigue crack growth rate until the crack grows beyond this region. A relationship between the plastic zone and the modified stress intensity factor is developed, which is a mathematical fitting equation instead of physical-based formulation. The experimental data in aluminum alloys are used to val-idate these two models. Overall, good agreement is observed between the model predictions and the testing data. It is noted that the approach based on modified VCA model can give more accurate prediction curves than the Willenborg model.     

压电陶瓷柱体中裂纹前缘场分析

为了揭示含裂纹的压电陶瓷介质在机械载荷作用下裂纹前缘的力学和电学的奇异行为,以一承受扭矩的压电陶瓷柱体为例,求得了其中所含的圆币形裂纹前缘的应力场和电场移场。     

航空发动机齿轮副动态啮合过程与齿根裂纹扩展轨迹影响因素研究

为了研究航空发动机中附件齿轮箱中的一对齿轮副在动态啮合过程中的响应特性和齿根裂纹的扩展对齿轮系统的影响,利用有限元仿真分析法,基于显示动力学和线弹性断裂力学研究了该齿轮副动态啮合过程和齿根裂纹扩展轨迹影响因素。含有齿根裂纹的齿轮在啮合过程会产生额外的振动和噪声,会引起转速、啮合力、啮合频率、接触应力产生较大波动;齿根裂纹的扩展轨迹不同会导致齿轮系统两种典型的失效模式:轮缘断裂失效或齿断裂失效,发生轮缘断裂的可能性受到轮缘厚度与齿高比值和裂纹初始位置的影响,会随着该比值的减少和初始裂纹位置沿着齿根方向下移而增大,初始裂纹方向对裂纹扩展轨迹影响很小可以忽略。研究成果在工程中可以为齿轮结构的故障监测和结构设计提供参考。     

某机身壁板结构环向裂纹扩展分析与试验对比

对于机身加筋壁板结构,获取较为准确的应力强度因子是进行裂纹扩展分析的基础,其核心工作是计算结构的几何因子。本文结合T.Swift提出的机身加筋壁板结构几何因子计算方法,编制了相关分析工具,计算获得某机身壁板结构环向裂纹几何因子,将计算结果与采用有限元法计算获得的几何因子进行对比。最后,将几何因子输入Nasgro软件进行裂纹扩展寿命分析,与试验结果进行对比,吻合较好。该方法计算效率高,可节省大量计算时间,具有较强的工程应用价值。     

2195铝锂合金氩弧焊接头组织分析及力学性能研究

针对T8态2195铝锂合金在氩弧焊焊时接头裂纹敏感性高、接头力学性能差等问题,开展2195铝锂合金焊丝研制工作,对接头的显微组织、抗裂性能及综合力学性能进行了研究。结果表明,2195铝锂合金熔焊接头主要由α-Al、Al₂Cu、Al₃（Ti,Zr）相组成,具备优异的抗裂性及力学性能,其裂纹敏感性K₁＜1%,K₂=0%,接头常温抗拉强度约为390 MPa,延伸率为6.3%。BJ-4505焊丝的研制为2195铝锂合金工程应用提供技术支撑。     

基于电涡流位移传感器的钛合金叶片振动疲劳试验研究

为了研究钛合金叶片振动疲劳特性,基于电磁振动测试平台和非接触式电涡流位移传感器,开展了试验工装和试验程序设计.通过本文的传感器标定和振动应力标定方法研究,发展了基于电涡流位移传感器的非接触测量式钛合金叶片振动疲劳试验手段,进而完成了疲劳考核试验和裂纹扩展试验,研究了裂纹长度和固有频率随疲劳循环数累积的变化规律.试验结果...     

固体推进剂燃烧断裂边界二维流场特性

在高温、高压的对流燃烧条件下,固体推进剂的断裂扩展是一个十分复杂的非线性非平衡不可逆的热力学耦合过程,裂纹对流燃烧流场与裂纹的变形、扩展之间存在着强耦合作用。以二维粘流Ｎ－Ｓ方程着重模拟了固体推进剂燃烧断裂边界二维流场特性,并和一维结果进行比较,全面展示了燃烧断裂动力学边界的时变特性,为燃烧断裂扩展模式的后续研究提供参考。     

Introduction of fretting-contact-induced crack closure: Numerical simulation of crack initiation and growth path in disk/blade attachment

Fretting fatigue crack initiation and growth in titanium alloy dovetail assembly was investigated by the Finite Element Method(FEM). Firstly, contact stress was calculated precisely with an elastic–plastic material model. Secondly, the location and angle of crack initiation were determined by the parameter of the maximum shear stress range on the critical plane, and the angle of crack growth was predicted by the Maximum Tangential Stress(MTS) criterion, which showed agreement with experimental observation. Finally, the fretting-contact-induced crack closure behavior was simulated by the node release technique in software ABAQUS with both elastic and elastic–plastic material models. The simulation shows that the variation of the contact status between fretting surfaces will result in crack closure even for the elastic material model. The fretting crack closure ratio decreases as the crack grows out of the contact area and it has great impact on the effective range of Stress Intensity Factor(SIF) as well as the crack growth rate.