Hf和Zr在高温材料中作用机理研究

在高温合金中,元素Hf和Zr可以促进γ γ′共晶、MC(2)碳化物、M2SC碳硫化物和Ni5M相的形成,改变草书状MC和M3B2成为块状并且通过净化晶界或枝晶间自由态的S来提高这些薄弱部位的结合强度,从而延迟裂纹的形成和扩展.Hf和Zr可提高铸造高温合金室温拉伸和中温持久的强度和塑性.Hf,Zr抑制次生碳化物M23C6和M6C的生成,从而提高了合金在高温长时热暴露时的显微组织稳定性.Hf,Zr降低合金的初熔温度,Ni5Hf和Ni5Zr相的初熔被认为是Hf,Zr影响初熔的主要原因.通过1150℃/8h的预处理,Ni5Hf以Ni5Hf γ(C)→MC(2) γ反应或者固溶两种方式被消除.元素Hf可以缩小枝晶间失去毛细管补缩能力和固相线之间的温度范围,还能降低枝晶间液池沟通所需的液体量.在凝固后期枝晶间的富Hf熔体具有很好的流动性、浸润性和趋肤效应,这些都是降低合金热裂倾向、提高合金可铸性和焊接性能的有利因素.具有高的化学活性的富Hf液膜容易在铸件表面形成Hf2O薄层.Hf和Zr是钎焊用中间层合金的降熔点元素.根据凝固过程中富Hf,Zr熔体的成分最终发展出Ni-18.6Co-4.5Cr-4.7W-25.6Hf和Ni-10Co-8Cr-4W-13Zr两种中间层合金,使单晶高温合金的无Si、B连接成为现实.还发展出了定向凝固片状Ni3Al/Ni7Hf2共晶合金,成分为Ni-5.8Al-32Hf和Ni-4Al-26Hf-8Cr-4W.Ni-5.8Al-32Hf合金的最佳凝固条件为温度梯度G=250℃·cm-1和凝固生长速率R=5μm·s-1;Ni-4Al-26Hf-8Cr-4W,凝固条件为G=350℃·cm-1和R=1μm·s-1.     

Ti600合金板材的轧制工艺与电子束焊接性能研究

测试研究了Ti600 高温钛合金板材在不同加工及热处理状态下的室温拉伸及高温蠕变性能,分析对比了热机械处理工艺(thermomechanical process-TMP)与常规加工热处理对合金板材组织形态特征与性能的影响规律与内在机制;另外还对Ti600合金板材的焊接性能进行了研究.结果表明:采用热机械处理工艺(TMP)可获得充分生长的片层状团束组织(colony structure),这种类型的组织显著提高了合金的高温蠕变性能.而且合金经电子束焊接后仍然具有良好的综合性能.     

降低颗粒粘结高燃速推进剂初始压强峰的途径

为降低颗粒粘结高燃速推进剂发动机试验时的初始压强峰,分别采用降低点火药量,改变燃喉比、燃通比,内外表面涂钝感剂和控制内、外燃通比之比小于1等方法进行了发动机试验,获得了每种条件下的压峰比数据。分析结果表明,采用控制内、外燃通比之比小于1的装填条件,可使其高燃速推进剂的压峰比小于1 3。     

变物性与热辐射对发汗冷却过程的影响规律研究

采用两层k-ε湍流模型对高温条件下有发汗冷却时的矩形槽道内湍流流动和换热进行了数值模拟。计算结果表明:随着冷却气体流量的增加,在发汗冷却壁面附近主流气体的温度梯度大大减小,壁面温度、局部对流换热系数都迅速下降;变物性条件下同时考虑热辐射时数值计算得到的平均St相对值St/S_t0随修正注入率F/St0的变化比已知的常物性条件下的值小;随着高温气体温度的上升,变物性和热辐射对与高温流体接触的表面温度有较大影响,热辐射对壁面温度的影响比变物性更大,而对流换热系数所受的影响不大;当主流为高温气体(如:2500K)、而壁面温度较低时(如:800K)热辐射的影响不大,发汗冷却效果仍然很明显。      

氰酸酯/线性酚醛/环氧树脂三元体系的研究

 在氰酸酯树脂/ 环氧树脂体系中引入了线性酚醛树脂,得到氰酸酯树脂/ 环氧树脂/ 线性酚醛树脂三元共聚体系。采用差示扫描量热法(DSC) 研究了三元共聚体系的反应动力学,根据Kissinger 方程和Ozawa 方程得到体系的表观活化能( Ea) :62. 94kJ / mol,确定了体系的反应速率常数K。比较了纯氰酸酯树脂、氰酸酯/ 环氧树脂体系和三元树脂体系玻璃布层压板的力学性能、介电性能以及吸湿率。结果表明,线性酚醛树脂用量为15wt %的三元体系复合材料的弯曲强度和层间剪切强度分别比氰酸酯/ 环氧树脂体系复合材料提高了6 %和15 %,介电损耗和吸水率分别降低了33 %和8 %。     

Optimal assimilation for ionospheric weather – Theoretical aspect

Observation, specification and prediction of ionospheric weather are the key scientific pursuits of space physicists, which largely based on an optimal assimilation system. The optimal assimilation system, or commonly called data assimilation system, consists of dynamic process, observation system and optimal estimation procedure. We attempt to give a complete framework in this paper under which the data assimilation procedure carries through. We discuss some crucial issues of data assimilation as follows: modeling a dynamic system for ionospheric weather; state estimation for static or steady system in sense of optimization and likelihood; state and its uncertainty estimation for dynamic process. Meanwhile we also discuss briefly the observability of an observation system; system parameter identification. Some data assimilation procedures existed at present are reviewed in the framework of this paper. As an example, a second order dynamic system is discussed in more detail to illustrate the specific optimal assimilation procedure, ranging from modeling the system, state and its uncertainty calculation, to the quantitatively integration of dynamic law, measurement to significantly reduce the estimation error. The analysis shows that the optimal assimilation model, with mathematical core of optimal estimation, differs from the theoretical, empirical and semi-empirical models in assimilating measured data, being constrained by physical law and being optimized respectively. The data assimilation technique, due to its optimization and integration feature, could obtain better accurate results than those obtained by dynamic process, measurement or their statistical analysis alone. The model based on optimal assimilation meets well with the criterion of the model or algorithm assessment by ‘space weather metrics’. More attention for optimal assimilation procedure creation should be paid to transition matrix finding, which is usually not easy for practical space weather system. High performance computing hardware and software studies should be promoted further so as to meet the requirement of large storage and extensive computation in the optimal estimation. The discussion in this paper is appropriate for the static or steady state or transition process of dynamic system. Many phenomena in space environment are unstable and chaos. So space environment study should include and integrate these two branches of learning. This revised version was published online in August 2006 with corrections to the Cover Date.     

不同腐蚀介质对高锰钢摩擦学性能影响机制的研究

考察了高锰钢在H2SO4、HCl、NaOH、NaCl和FeCl3等不同腐蚀介质条件下的摩擦学性能,并对各种腐蚀介质对摩擦学性能的影响机制进行了讨论.结果表明:腐蚀磨损过程伴随着气泡产生,高锰钢在磨损过程中发生了产生气体的反应,由于腐蚀介质自身的黏性以及反应膜的润滑作用,高锰钢在FeCl3中的摩擦系数最低.在FeCl3中,受Fe3 强氧化性的作用以及Cl-对反应膜的破坏,高锰钢的腐蚀磨损率最高;由于腐蚀介质相对较弱的氧化作用以及自身良好的润滑性,高锰钢在H2SO4和NaOH中的磨损率最低.     

EB-PVD工艺制备Ti/Ti-Al超薄多层复合材料的微观结构与性能研究

利用大功率电子束物理气相沉积(EB-PVD)技术制备了Ti和Ti-48at%Al交替蒸发沉积形成的金属/金属间化合物型多层材料薄箔.研究了靶基距、微观结构参数及试样在制备材料的选取位置对其性能的影响,考察了Ti/Ti-Al微叠层材料在不同温度下的拉伸性能,结果表明材料的室温脆性得到了明显改善,高温下由于金属间化合物层的反常强化作用,使材料在500～800 ℃之间的性能较为理想.     

热障涂层用Dy2Zr2O7陶瓷粉末制备及其热物理性能研究

采用共沉淀-煅烧法制备了热障涂层用Dy2Zr2O7陶瓷粉末.通过电感耦合等离子体原子发射光谱(ICPAES)、X射线衍射,SEM,DSC及霍尔流速计等分析方法,对粉末的化学组成、相组成、微观结构、高温相稳定性和流动性能进行了研究.通过高温膨胀仪、DSC和激光热导仪分别测定其热膨胀系数、比热系数和导热系数.结果表明,所制备粉末的组成与锆酸镝氟石结构的组成相近;高温下Dy2Zr2O7无明显相变;在高于1400℃的温度下煅烧后,Dy2Zr2O7的流动性得到显著改善;Dy2Zr2O7具有比8YSZ更高的热膨胀系数和更低的导热系数.     

固体火箭发动机多层粘接结构超声图像诊断

针对固体火箭发动机的钢壳、绝热层、衬层、推进剂多层粘接结构的粘接质量检测问题,利用聚焦探头采用斜声束液浸反射回波法,选用往返透射率高的板波模式,特别是采用了双模式检测技术以提高检测信号能量,获得有效检测信号,并开发出了检测系统。通过一次C扫描获得了双层包覆三个界面粘接质量诊断图像,其脱粘检测分辨率≤Φ5 mm。采用聚集探头双模式检测技术实现了固体火箭发动机多层粘接结构超声图像诊断。