拉伸速率对NEPE推进剂力学性能的影响

运用单向拉伸手段,研究了不同拉伸速率(0.5～500 mm/min)、测试温度(25～70℃)对NEPE推进剂最大抗拉强度σm和最大伸长率εm的影响。试验结果发现,NEPE推进剂σm和εm均与拉伸速率v呈幂律函数关系,建立了相关性较好的幂函数方程σm=k(T)va和εm=f(T)vb。利用该方程,对极慢拉伸速率下NEPE推进剂σm和εm进行了预示,计算结果可为固体火箭发动机设计及推进剂贮存性能研究提供技术支持。     

Analytical solutions for Earth discontinuous coverage of satellite constellation with repeating ground tracks

This paper presents an analytical model for calculating the Earth discontinuous coverage of satellite constellation with repeating ground tracks by integrating and extending the application of coverage region and route theory. Specifically, the visibility condition for a ground point is represented as a coverage region in the two-dimension map of visibility properties, and the trajectories of satellites with circular orbits and repeating ground tracks are converted to several inclined lines in t...     

CVD技术制备Ta/W层状复合材料

运用化学气相沉积(Chemical Vapor Deposition,CVD)技术制备了W体积分数分别10%,13%和18%的Ta/W两层层状复合材料,采用金相显微镜(OM)、扫描电镜(SEM)和室温拉伸实验对复合材料的性能进行分析。结果表明:运用CVD技术可以制备W体积分数不同,且密度优于理论密度99.4%的层状复合材料;复合材料中Ta,W层的晶粒均为柱状晶粒,离界面越近,晶粒越细;沉积态复合材料的力学性能优于纯CVD Ta和CVD W;1600℃×2 h的热处理后,复合材料的界面扩散层宽度显著增大,力学性能高于沉积态的力学性能,最高抗拉强度可达660 MPa。     

Precipitation behavior and properties of extruded 7136 aluminum alloy under different aging treatments

In this work, the mechanical properties and electrical conductivity of the extruded 7136 aluminum alloy treated by single-stage aging treatment (T6), retrogression and re-aging treatment (RRA), and multiple retrogression and re-aging treatment have been investigated by means of hardness measurements, electrical conductivity tests and tensile tests. The results have shown that the properties of the 7136 alloy such as hardness, tensile strength and electrical conductivity were sensitive to retrogression time (within 90 min). With prolonging the retrogression time, the tensile strength was enhanced first and then decreased, yet the electrical conductivity was continuously increased. The 60 min-treated alloy performed the highest tensile strength (716 MPa), whereas the 90 min-treated alloy possessed the highest electrical conductivity (33.95%IACS). Compared with the T6-treated alloy, the tensile strength and electrical conductivity were improved by 3.3% and 18.9%, respectively. The electrical conductivity showed an obvious increase with repetitious times of the RRA treatment. After 3RRA60 treatment, a good combination of tensile strength (705 MPa) and electrical conductivity (33.20%IACS) can be obtained. Compared with the T6 condition, the tensile strength and electrical conductivity were improved by 1.7% and 16.3%, respectively. The mechanism of microstructure evolution under different aging treatments has been discussed in detail.     

石墨填料对浸渗热解-熔融浸渗方法制备的C/SiC复合材料结构和性能的影响

采用石墨树脂浆料浸渍三维针刺碳毡增强体,热解后得到C/C多孔体,并采用反应熔体浸渗法制备C/SiC复合材料.研究了石墨填料对C/C多孔体的结构以及C/SiC复合材料力学性能的影响.结果 表明,石墨树脂浆料浸渍时树脂填充束间小孔形成结构致密的亚结构单元,而石墨可以有效填充胎网层等大孔隙,一次浸渍热解后碳产率有效提高.所得...     

Fatigue crack propagation of new aluminum lithium alloy bonded with titanium alloy strap

A new type of aluminum lithium alloy (Al-Li alloy) Al-Li-S-4 was investigated by test in this paper. Alloy plate of 400 mm · 140 mm · 6 mm with single edge notch was made into samples bonded with Ti-6Al-4V alloy (Ti alloy) strap by FM 94 film adhesive after the surface was treated. Fatigue crack growth of samples was investigated under cyclic loading with stress ratio (R) of 0.1 and load amplitude constant. The results show that Al-Li alloy plate bonded with Ti alloy strap could retard fatigue crack propagation. Retardation effect is related with width and thickness of strap. Flaws have an observable effect on crack propagation direction.     

PP／SCF复合材料的制备和力学性能的研究

本文制备了聚丙烯（PP）／,短炭纤维（SCF）复合材料并研究了其力学性能。结果表明,复合材料的拉伸强度随SCF含量的增加有先增加后趋于稳定的趋势,当SCF含量达到6％时,拉伸强度达到极值。随着SCF的加入,冲击强度呈先增加后略有降低的趋势,复合材料在SCF含量为6％时冲击强度达到极值。由此可知,适量的加入SCF对PP起到了较好的增强增韧效果。     

POSS 催化剂改性氰酸酯复合材料的性能

通过POSS 催化剂改性氰酸酯树脂,并采用热熔法排布制备了碳纤维/ 中温固化氰酸酯预浸料, 验证了改性氰酸酯的工艺性。同时考察了氰酸酯树脂及其复合材料的性能。结果表明, POSS 催化剂的加入, 降低了氰酸酯的固化温度,同时其使用温度、室温及-18℃的储存性能和复合材料力学性能与改性前相当。     

Performance of a small and low-cost chamber to simulate lunar surface environment

The performance of a small and low-cost metal chamber built to simulate the pressure and temperature conditions of lunar surface was assessed and the results are presented. This chamber is intended for studying the physical properties of lunar surface and subsurface (using soil simulants) and also to validate the technology readiness of certain newly developed payloads planned for future lunar surface missions (Lander/Rover). It is possible to reach down to ∼10⁻⁷ Pa under specific conditions and maintain the temperature of the sample under investigation to lunar day and night temperatures. The designed system has been subjected to various tests to evaluate its performance and suitability for carrying out experiments in a simulated lunar environment.     

新型电工钢片磁性能无损检测传感器及应用

介绍了一种新型电工钢片磁性能无损检测传感器及其测量原理 ,同时讨论了该传感器的设计原则并给出了典型数据及仿真测试结果