Relight of jet engines at high altitude is difficult due to the relatively low pressure and temperature of inlet air. The penetration of initial flame kernel affects the ignition probability in the turbine engine combustor greatly. In order to achieve successful ignition at high altitude, a deeper penetration of initial flame kernel should be generated. In this study, a Gliding Arc Plasma Jet Igniter(GAPJI) is designed to induce initial flame kernel with deeper penetration to achieve successful ...     

2219 铝合金VPTIG 焊接接头拉伸性能分析

2219 铝合金气孔敏感性较强,变极性TIG 焊接工艺可以有效减少和抑制气孔产生,是适合于
2219 铝合金的焊接工艺。本文介绍了2219T62 铝合金VPTIG 焊接接头的拉伸性能,进行了拉伸断口形貌分析
和微观组织分析。结果表明:2219T62 铝合金VPTIG 焊接接头强度系数可以达到65% 以上,焊接接头为混合
断裂方式,VPTIG 焊缝盖面层气孔相比打底层较多。     

摆动焊接对异种热处理状态2219铝合金焊接接头性能的影响

针对2219异种热处理状态C1OS+CYS铝合金进行钨极氩弧焊接试验,对比研究了常规焊接与摆动焊接接头的力学性能、微观组织、硬度分布等.分析结果表明,相较常规接头,采用摆动焊接工艺的接头其力学性能有所提高,同时接头中下部PMZ、OAZ的硬度有所下降,宽度范围有所增加.应变分布结果表明,断裂前常规接头最大应变沿对角线分布...     

基于机器视觉的搅拌摩擦焊缝装配质量评测方法

搅拌摩擦焊常采用无坡口焊缝,焊缝装配质量对搅拌摩擦焊装配质量影响较大,通过焊缝的特征,可以对搅拌摩擦焊缝的装配质量进行评判。线结构光是提取焊缝特征的常用手段,基于结构光传感器扫描获得的焊缝轮廓信息多通过离散的点进行表示,如何高效地从轮廓点中提取焊缝轮廓信息,是焊缝特征识别的新挑战。本文提出一种基于机器视觉的焊缝装配质量评测方法,将离散的轮廓点转换为位图,通过抗锯齿算法提高轮廓直线特征的识别可靠性,并计算对应焊缝的装配质量信息,进而实现对整条焊缝的装配质量的量化评价。与传统的离散点拟合方法相比,本方法具有较为明显的效率优势。     

2219铝合金厚板TIG焊接头组织与力学性能研究

采用氦弧打底+氩弧填充、盖面的焊接工艺对2219-T87铝合金15 mm厚板进行TIG焊接试验，研究其焊缝成形和组织力学性能。结果表明，此工艺焊缝成形美观，无可见焊接缺陷，气孔抑制效果好，接头平均抗拉强度为278.22 MPa，平均断后延伸率为3.89%，接头平均强度系数达到58.94%。接头硬度整体表现为焊缝中心最低，从焊缝中心到母材呈现先增大后局部降低再增大的趋势；且焊缝中心填充层硬度高于打底层和盖面层。熔合区的微观组织为柱状树枝晶和胞状树枝晶，且垂直于熔合线生长，在靠近熔合区两侧出现了等轴细晶带。焊接接头断面有较多撕裂棱和韧窝，局部发现第二相粒子和微孔，其断裂机制为典型的韧性断裂。     

2524与7150铝合金激光焊T型接头的组织与性能

介绍了2524与7150铝合金激光焊T型接头优化的工艺参数,并研究了T型接头在优化工艺下的显微组织与力学性能,进行金相分析、显微硬度测试与接头拉伸试验。结果表明:优化工艺下焊缝没有裂纹、气孔,金相组织晶粒细小、致密,焊缝区域的硬度最低;T型接头x方向的拉伸强度达到384 MPa,z方向的拉伸强度为236 MPa。     

2219 铝合金单、双道焊接头性能分析

通过对比2219 铝合金单道氩弧焊和氦弧打底+氩弧盖面双道焊接头的常温及液氮温度拉伸性
能、显微硬度分布、单向拉伸过程的数字散斑测量(DIC)结果,发现在常、低温条件下双道焊接头的拉伸强度和
延伸率均比单道焊接头高10% ~20%,单道焊接头焊缝及热影响区内材料的显微硬度值相比母材的降低程度
比双道焊接头更为显著,其主要原因是单道焊接头的一次性热输入大于双道焊,材料受热影响更严重,焊漏高
度及形状的可控性更差。     

2195铝锂合金弧焊技术研究现状

铝锂合金具有密度低、比模量高、比强度高、抗疲劳及腐蚀性能良好等特点,被认为是航空航天领域最有应用前途的结构材料之一.本文回顾了铝锂合金的发展历程,介绍了新一代2195铝锂合金的成分、组织结构及可焊接性,分析其焊接过程出现的主要问题,概述了国内外机构通过优化2195铝锂合金配用焊丝及弧焊工艺,改善接头组织结构及力学性能的...     

Effect of adding Nb foil on joint properties of laser fusion welding for TC4 titanium and 7075 aluminum alloy

It is difficult to gain effective Ti-Al fusion welding joints due to their differences in thermal properties and the appearance of brittle Ti-Al Intermetallic Compounds (IMCs). The experiments of laser fusion welding for TC4 titanium and 7075 aluminum alloy were carried out, temperature field and ductility/brittleness, as well as chemical potential of elements, were calculated, and the effect of adding Nb foil on mechanical properties of the weld was also investigated. The results suggested that Nb atoms tend to diffuse toward Al side, which is conducive to the participation of Nb in the metallurgical reaction and contributes to forming the Ti-Nb-Al IMC layer at the interface. As the thickness of Nb foil increases, the tensile-shear force of joint climbs first but then declines, and reaches the highest value of 1663 N with 0.10 mm-thickness Nb foil, representing 58.38% enhancement compared with the non-added one. Adding Nb foil slows down the heat transfer as a blocker, and thus both the melting amount of Al and the mixing area of Ti and Al decrease. In addition, Nb alloying reduces the brittleness of the Ti-Al compound. Hence, the joint properties of titanium/aluminum are improved with the addition of Nb foil.     

Through-thickness heterogeneity in creep properties of friction stir welding 7B50-T7451 aluminum alloy thick plate joint: Experiments and modeling

Through-thickness heterogeneity in creep properties of 7B50-T7451 aluminum alloy Friction Stir Welding(FSW) joints was investigated. Creep tests for three slices of the FSW joint were conducted at the temperature of 150–200 °C and applied stress of 60–225 MPa. The theta projection method was used to predict creep curves and minimum creep rate. The results show that the minimum creep rate increases and creep rupture life decreases with the increase of creep temperature and applied stress. Creep p...