内氧化制备A1_2O_3/Cu复合材料载流条件下表面磨损形貌和摩擦学性能研究(英文)

Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.     

铝铜点焊的研究

提出了铝铜过渡接头的点焊新方法,用交流焊机点焊铝铜,解决了Al2O3氧化膜层的破碎问题。从而可利用热活化、压力、电磁搅拌力,使铝铜固溶,扩散和铝液面移动,完成铝铜点焊,获得比铝强度高的焊接接头,为铝代铜的运用提供了一种特殊的途径。     

LY12cz铝合金晶间腐蚀模拟试验研究

用金属间化合物 θ(CuAl₂)、S(Al₂CuMg)、MnAl₆与纯Al(L1)组成多电极体系,以模拟LY12cz合金的晶界区.通过电化学测试、SEM和能谱分析等方法研究了该合金晶间腐蚀机理.证实其晶间腐蚀是由沿晶界偏析的强化相与贫Cu区所组成的多电极体系引起的.在含Cl^－离子的中性溶液中,S相是导致晶间腐蚀的主要阳极相.S相首先发生阳极溶解,随后,贫铜区、MnAl₆相逐步随S相一起溶解.以这种方式沿晶界形成了阳极溶解通道,导致晶间腐蚀.     

稀土元素及杂质在铝锂合金中的作用研究现状与发展

 综述了稀土元素和杂质对铝锂合金微观组织及力学性能的作用,概括了杂质致脆及稀土微合金化的规律与机制,根据已有研究结果,对目前铝锂合金的发展与应用中需要引起重视的问题,提出了某些观点与建议。     

SiCw/Al复合材料热挤压模具设计及其对挤压棒材组织和性能的影响

用具有宏观夹铝带的ＳｉＣｗ／Ａｌ复合材料的热挤压余,对热挤压压余中的金属流线进行了观察并建立了金属流线方程,为抗日夺模具的设计提供了指导原则。本文用曲线形状较金属流线形状陆的流线凹模进行挤压,结果表明,使用该种凹模能够有效地消除金属“死区”并在一定程度上减少了晶须折断,从而提高了挤压棒的强度。     

溶胶-凝胶法制备复合材料用氧化铝基体及涂层研究

采用溶胶—凝胶法,分别研究了用三种起始物异丙醇铝［Ａｌ（ＯＣ３Ｈ７ｉ）３］、氯化铝（ＡｌＣｌ３·６Ｈ２Ｏ）、硝酸铝［Ａｌ（ＮＯ３）３·９Ｈ２Ｏ）］,制备碳纤维三维编织物增强复合材料用氧化铝基体及涂层的工艺,考察了三种体系反应物配比、水解温度、反应时间等因素对制得的三种溶胶体系性能的影响,获得了较佳的溶胶配制参数;还考察了三种溶胶体系在通常情况下和在编织物中的凝胶化情况,获得了较佳的凝胶化条件;同时还研究了不同条件下三种凝胶的裂解产物及其晶体类型。结果表明,不管经过何种途径,凝胶在经１２６０℃裂解后均可获得α－Ａｌ２Ｏ３。     

Microstructure and Properties of Low-pressure Cold Sprayed Al-based Composite Coatings on Magnesium Alloy Surface

Pure Al and Al-30% Al2O3 composite coatings are prepared on the surface of AZ31B magnesium alloy by low-pressure cold spraying. The morphology and structure of the coatings are analyzed by scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD), and the effects of the addition of Al2O3 on the microstructure of the Al-based coatings are discussed. The mechanical properties and corrosion resistance of the coatings are fully evaluated by the micro-hardness tester, electronic tensile machine, and electrochemical workstation. The results show that the coating structure is more uniform and denser, and the porosity is significantly reduced after the addition of Al2O3. The interfaces between the coatings and the magnesium alloy substrate are distinct, and the coatings and the substrate are mechanically combined. Compared with the pure Al coating, the microhardness of the Al-Al2O3 composite coating is increased to 61.1 HV0.2, and the bonding strength reaches above 53.1 MPa. The self-corrosion potential of the two coatings is higher than that of the magnesium alloy, and the self-corrosion current density is significantly lower than that of the magnesium alloy substrate. The Al-based coatings prepared by low-pressure cold spraying have high hardness, good bonding strength, and good corrosion resistance, which can be used for the repair and protection of magnesium alloy structural parts.     

直流磁控溅射ZnO:Al薄膜的光电和红外发射特性

以锌、铝合金(ω(Al)=3%)为靶材,利用直流反应磁控溅射法制备了系列掺铝氧化锌ZnO:Al(ZAO)薄膜样品,通过X射线衍射(XRD)、扫描电子显微镜(SEM)、分光光度计、霍耳效应及红外发射率测量仪等测试仪器或方法表征了样品的结构、形貌、光学、电学及红外发射特性.测得样品最低电阻率达到1.8×10^-6(Ω·m),最大禁带宽度为3.47?eV,可见光区平均透过率达到90%,8~14?μm波段平均红外发射率在0.26~0.9之间.上述特性均随衬底温度和溅射功率的变化有着规律的变化.当方块电阻小于45?Ω时,薄膜在8~14?μm波段平均红外发射率与方块电阻遵循二阶函数变化规律.     

激光快速熔凝Al2O3/YAG共晶陶瓷的制备与组织

采用激光快速熔凝技术制备Al₂O₃/YAG共晶自生复合陶瓷, 研究Al₂O₃/YAG共晶陶瓷在高能激光束作用下,不同扫描速率(0.01~2.0mm/s)、超高温度梯度下的凝固组织特征及其生长机制,探索激光熔凝过程控制参数与凝固组织的关系.研究结果表明:激光熔凝Al₂O₃/YAG共晶陶瓷由无规则连续分布的Al₂O₃相和YAG相两相组成,没有晶界和其他相,Al₂O₃相的体积分数为(45.0±2.0)%,两相耦合生长,交错分布,是典型的快速凝固层片状非规则共晶组织;共晶层间距细密, 并随激光扫描速度的增大而减小,扫描速度为0.02mm/s 时,共晶间距约为1~2μm,扫描速度为2.0mm/s时,共晶间距仅为0.5μm左右;综合热分析表明,Al₂O₃/YAG共晶熔点为2096K,与相图吻合.     

喷射成形电子封装Si-Al合金凝固过程模拟研究

为了优化喷射成形Si—Al合金成形工艺，获得优良的显微组织，本文模拟了喷射成形Si-30wt％ Al合金的凝固过程。研究了雾化压力和沉积距离对熔滴冷却过程中的温度和固相分数的影响。模拟计算结果得到实验验证。