细晶处理对磷微合金化GH761合金力学性能的影响

实验使用添加0.023%磷进行微合金化的GH761合金,采用6种不同处理制度进行细晶化处理.结果表明,一次热处理温度在780～950℃范围内变化时,对合金的晶粒组织影响不大,但与标准热处理组织相比,晶粒组织显著细化.采用830℃×4 h,AC,720℃×24 h,AC的热处理制度时,合金的综合力学性能较好.与标准处理相比,室温和650℃的抗拉强度和屈服强度均明显提高,塑性也有所改善,而且650℃/690 MPa持久寿命比普通GH761合金650℃/637 MPa的持久寿命长.     

脉冲加压扩散连接工艺参数对钛合金与不锈钢接头强度的影响

采用脉冲加压扩散连接工艺对TA17钛合金与0Cr18Ni9Ti不锈钢进行了连接试验.利用液压万能试验机测试了接头拉伸强度,分析了脉冲加压扩散连接工艺参数对接头强度的影响.结果表明:当连接温度为1098K、脉冲最小压力Pmin=8MPa、脉冲最大压力Pmax=50MPa、脉冲次数为20次、脉冲频率为0.5Hz时,加热速度vh=30K/s,冷却温度vc=5K/s,得到最高的接头拉伸强度为293MPa,连接所用的有效时间仅为220s,实现了钛合金与不锈钢的高效良好连接.利用X射线衍射(XRD)及扫描电镜(SEM)分析了接头组成相及断口形貌,接头界面主要存在β-钛、Fe2Ti,FeTi,拉伸试验中β-钛的固溶体承担了主要的拉伸力.     

含Ni夹层SiCp/2014Al铝基复合材料扩散焊

利用中间添加Ni层,在610℃保温60min工艺成功实现了SiCp/2014Al铝基复合材料的真空扩散焊接.焊接之后利用金相显微镜(OP)、扫描电镜(SEM)、电子探针(EPMA)等对焊接接头进行分析.分析表明,Ni和Al之间相互扩散形成由金属间化合物构成的中间过渡层,主要由Ni3Al//NiAl//NiAl3组成.在理论上,计算出Ni和Al元素扩散浓度与焊接温度和保温时间之间的关系,以及元素的扩散距离与焊接参数之间的关系呈抛物线形变化.     

热塑弹性体铝合金化学铣切保护涂料的研制

采用热塑性弹性体为基体材料制备不同配方的铝合金化学铣切保护涂料.实验包括涂料中酚醛树脂的合成,涂料的制备.所做涂料的性能考核包括外观、粘度、固体含量、抗张性、断裂伸长率、浸蚀比、致密性、剥离强度等.最后与美国同类产品性能对比.研究表明,自制的铝合金化学铣切保护涂料的涂膜透明均匀、剥离强度大小适中、耐强碱,满足化学铣切工艺要求,也基本上与美国同类产品性能相当.     

不同壁厚的TiNiFe形状记忆合金管接头紧固力的模拟计算

研究不同壁厚的TiNiFe形状记忆合金管接头紧固力随时间变化的定量关系对航空用TiNiFe形状记忆合金管接头有重要的实际工程应用价值。在有关TiNiFe形状记忆合金的力学建模和公式推导的基础上,利用计算机进行软件编程,完成了对TiNiFe形状记忆合金管接头升温过程产生紧固力的计算模拟,得到了TiNiFe形状记忆合金管接头在约束升温状态下紧固力随时间变化的模拟曲线,重点研究了管接头壁的厚度对管接头产生紧固力的影响,并通过具体的实验进行验证。发现管接头的升温逆转变过程很短,壁厚小于2.5mm范围内的管接头的紧固力随着壁厚的增加而增加,几乎成线性关系。     

镁合金AZ91表面弧辉等离子沉积TiN/CrN薄膜的摩擦行为研究

镁合金具有高的比强度、低的弹性模量、减震等优点,在航空航天领域具有很大的应用前景.但是低劣的耐磨性导致镁合金限制于制造静载零件.为改进其耐磨性,采用弧辉等离子沉积的新工艺在镁合金AZ91表面涂覆TiN/CrN多层薄膜.薄膜由12层TiN和CrN交替沉积而成,总厚度为2 μm.用扫描电镜(SEM)、X射线衍射(XRD)和辉光放电光谱(GDS)分析涂层的成分和微观结构.采用球盘磨损试验测试摩擦系数,并计算出比磨损率.结果表明,与未处理试样相比摩擦系数增大,但磨损率急剧下降.薄膜的表面硬度超过HK0.011433.     

The Two-step Reverse Martensitic Transformations of TiNi Shape Memory Alloy Based on Solution-treatment and Aging

A TiNi-alloy is solution-treated in a vacuum furnace of 6.7×10-3 Pa at 1 223 K for 3.6 ks, and then aged at 773 K for 1.8 ks. The differential scanning calorimetry (DSC) measurements show that after the heat-treatment, takes place a two-step reverse Martensitic transformation, from which results the two-stage recovery strain in a prestrained Martensitic TiNi-alloy wire during heating. The Vickers microhardness indentation test in cross-sectional areas of the TiNi-alloy wire indicates the compositional heterogeneity between its sur-face layers and its inside. The fact that the sizes of the indentation in surface layers smaller than those in the inside bears witness to the existence of slightly harder surface layers. It is believed that these phenomena are related to the compositional fluctuation caused by the evaporation and oxidization of Ti-element during the solution-treatment and heterogeneity formed during the subsequent aging treat-ment.     

V,Al对Nb-Si系超高温结构材料抗氧化性能的影响

采用真空非自耗电弧炉制备了Nb-22Ti-12Si三元以及三种不同V,Al含量的Nb.Ti-Si-V-Al五元Nb-Si合金,研究了四种合金铸态显微组织和1250℃的抗氧化性能.结果表明:V,Al的加入促进了反应Nb3Si→Nb Nb Nb5Si3,使合金相组成由Nb Nb3Si转变成为Nb Nb5Si3,从而增加了合金中Nb相体积分数;合金的抗氧化性能随V,Al含量的增加而提高;V,Al的加入使合金氧化皮结构发生了转变,生成了较为致密的氧化皮,降低了合金的氧化速率,减少了合金氧化皮的剥落和金属氧化损失量.Nb-21.9 Ti-11.9Si-4.4V-4.1Al经过1250℃/50h氧化后金属损失厚度仅为0.1mm.     

镍基合金钼元素可见光谱数字化分析技术研究

使用可见光谱数字化自动分析系统对镍基合金中Mo元素可见光谱进行了分析测定,研究了镍基合金中Mo元素的Mo550.65nm和M588.83nm分析谱线组的特征,探索了镍基合金中Mo元素的数字化分析技术.结果可用于镍基合金中Mo元素的定性、定量分析和牌号鉴别.     

铝合金厚板时效成形回弹补偿算法

 时效成形是一种适用于飞机整体壁板零件制造的成形工艺,具有回弹量大的特点,因此需要在准确预测回弹量的基础上对模具型面进行修正,以消除回弹对成形精度的影响。本文提出了一种基于有限元计算驱动的适用于铝合金时效成形的模具型面迭代修正算法,并应用该算法进行了单曲率的圆柱面零件、双曲率的球面零件及马鞍形零件的修模计算分析。通过4次迭代计算,使圆柱面和球面零件成形误差减小到0.4 mm以内;通过5次迭代,使马鞍形零件除4个角部外,其余部位型面误差小于0.5 mm。证明了该回弹补偿算法具有计算精度高、收敛速度快的优点。